Production method for flexible graphite polar plate with plough groove on both faces

A manufacturing method, flexible graphite technology, applied in the direction of final product manufacturing, sustainable manufacturing/processing, battery electrodes, etc., can solve the problems of bipolar plate leakage, increase plate thickness, impermeability, etc.

Inactive Publication Date: 2008-07-16
SUNRISE POWER CO LTD
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantages of the prior art are: when forming a pole plate with grooves on both sides, since the low-density expanded graphite is a porous material, during the densification process, the open pores are closed to form high-pressure pores, and the pores are further compress

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method for flexible graphite polar plate with plough groove on both faces
  • Production method for flexible graphite polar plate with plough groove on both faces

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] Example 1

[0022] The 50-mesh expandable graphite with an expansion volume of 200ml / g is fully mixed with 10% by weight of acicular wollastonite powder. The particle size of the acicular wollastonite powder is 100 mesh. After being expanded in an expansion furnace at about 800°C, the expanded graphite powder passes Rolled to make a thickness of 4.5mm and a density of 0.2g / cm 3 , Expanded graphite board with a width of 450mm and a length of 500mm, cut this graphite board into a 450×120mm board, put such a graphite board in a closed impregnation tank, first vacuum the impregnation tank, the vacuum degree reaches -0.1MPa, and then Inhale the resin solution and immerse it in an ethanol solution mixed with phenolic resin and epoxy resin. The immersion time is about 10 minutes. The ratio of the resin solution is phenolic resin: epoxy resin: ethanol=10:5:85 (weight ratio). After being dipped, it will be volatilized frequently, and then dried at a temperature of about 90°C for abo...

Example Embodiment

[0023] Example 2

[0024] In the same steps as in Example 1, the original plate thickness is 4.5mm expanded graphite plate, the overall thickness is 1.1mm, the depth of one side of the flow field is 0.5mm, the width is 1.0mm, and the other side is 0.2mm deep and 0.8mm wide. mm cathode plates for fuel cells.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a manufacturing method for a flexible graphite pole plate both surfaces of which are provided with grooves, comprising the following steps: firstly, expandable graphite raw materials are rolled or extruded into a low density graphite plate with thickness of 1.5 to 8 millimeters and density of 0.15 to 0.5 gram per cubic centimeter; secondly, the low density graphite plate is infused into a low viscosity resin solution until grain in weight of resins is 15 to 50 percent of weight of the low density plate; the low density graphite plate is dried after being taken out and solvent in an infused plate is removed, and then a drying plate is obtained; thirdly, the drying plate is extruded into the pole plate both surfaces of which are provided with the grooves; fourthly, the pole plate both surfaces of which are provided with the grooves is solidified. The invention is characterized in that: the step in which the drying plate is extruded into the pole plate both surfaces of which are provided with the grooves is that the dried low density graphite plate after infusion in the low viscosity resin solution is extruded into the pole plate both surfaces of which are provided with the grooves under the condition of vacuum. The invention has the advantages that: thickness of the flexible graphite double pole plate is reduced; isotropy degree of particle orientation of the expandable graphite materials is improved; longitudinal resistivity of the expandable graphite plate materials is reduced.

Description

technical field [0001] The invention relates to the field of proton exchange membrane fuel cells, in particular to a method for manufacturing flexible graphite pole plates for fuel cells. Background technique [0002] The bipolar plate of the proton exchange membrane fuel cell is an important part of the proton exchange membrane fuel cell. It acts as a single cell in series, and also has channels and coolant channels for supplying fuel and oxidant to the single cell. It also has the function of separating fuel and oxidant. Therefore, it is required that the bipolar plate should have electrical conductivity, be impermeable to gas and coolant (water), and have corrosion resistance to fuel, oxidant, and electrolyte membrane. [0003] Using expanded graphite formed plates as bipolar plates is an option for bipolar plates. In the prior art, the use of expanded graphite forming plates to make bipolar plates is to roll expanded graphite into a low-density flat plate, then impregna...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M4/88H01M8/02H01M8/10H01M8/0234H01M8/1004
CPCY02E60/521Y02E60/50Y02P70/50
Inventor 徐洪峰傅云峰罗晓宽明平文
Owner SUNRISE POWER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap