Thin foamed polyethylene sheets and manufacture method thereof

A thin sheet, sheet technology, applied in the field of manufacturing these foam sheets, to achieve the effect of increasing the cushioning performance

Active Publication Date: 2008-12-17
DOW GLOBAL TECH LLC
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] Therefore, methods of increasing MD tear strength traditionally used for conventional films (typically such as using low melt index LLDPE resins or using neat LLDPE resins or blends of rich LLDPE

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thin foamed polyethylene sheets and manufacture method thereof
  • Thin foamed polyethylene sheets and manufacture method thereof
  • Thin foamed polyethylene sheets and manufacture method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0039] Sheets were formed from the LDPE and LLDPE resins shown in Table I. Resin A is an LDPE with a melt index (MI) (at 190°C / 2.16 kg) of 2.3 and a density of 0.920. Resin B is an LDPE with a MI of 0.47 g / 10 min and a density of 0.920. Resin C is LLDPE with a MI of 0.5 and a density of 0.920. Resin D is LLDPE with a MI of 1.0 and a density of 0.920. Resin E is LLDPE with a MI of 2.3 and a density of 0.917. Resin F is a ULDPE with a MI of 4 and a density of 0.904 g / cc. The chemical blowing agent or CBA used was SAFOAM FPE-50 containing 50% encapsulated sodium salt active ingredients of carbonic and polycarboxylic acids in a polyethylene carrier. A 3 mil thick film was made using a 2.5 inch extruder equipped with an 8 inch low pressure die and a medium shear barrier screw. A 40 mil lip with a 1 / 2 inch land length was used. The route runs at 220lbs.hr. MD tear strength was then measured according to ASTM D 1922 Elmendorf type B method. Puncture Propogation Tear (PPT) was...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to the use of particular blends of LLDPE and LDPE together with specific fabrication conditions to make foamed sheets of thin gauge with MD tear properties similar to an equivalent gauge non-foamed sheet of the same composition. In particular, blends which combine a high MI LLDPE rich fraction with a low MI branched LDPE minor fraction provide the adequate balance ofmechanical strength of the polymer base with its melt strength, extensibility and stress relaxation, allowing a thin foam film with MD tear strength which is comparable to non foamed counterparts of similar gauge and composition. The foamed films of the present invention are thin (generally from about I to 10 mils thick), and have an MD tear strength of at least about 160 grams for a 3 mil film as measured by ASTM D 1922. The foamed films of the present invention are preferably made at least in part from blends which comprise from 10 to 95 percent by weight of LLDPE having a relatively high (1.5 to 6) MI and from 5 to 90 percent of an LDPE resin having a relatively low MI (0.5 to 2.0).

Description

[0001] This application is a divisional application of Chinese Patent Application No. 200480019370.4 with an international filing date of June 30, 2004, an international application number of PCT / US2004 / 021173, and a title of "thin foamed polyethylene sheet". technical field [0002] The present invention relates to thin foamed polyethylene sheets, especially those having a thickness of 1 to 10 mils. These sheets have comparable MD tear strengths to non-foamed sheets of the same thickness and composition. The invention also relates to methods of making these foam sheets. Background technique [0003] The thin sheet or film of the present invention can be used in many applications, especially for blown film applications, including consumer trash bags, grocery bags, produce bags, pallet bags, etc. wrap), food wrap, liner, heavy duty bag, industrial bag, consumer bag, shrink film, label, FFS packaging Pouches for FFS packaging, tapes, stand-up pouches, lamination films, prote...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08J9/04C08L23/06C08J9/00
CPCC08J9/0061C08J2323/06C08J2423/00C08J5/18C08J2323/08Y10T428/1376C08J9/00
Inventor F·马丁内斯
Owner DOW GLOBAL TECH LLC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap