Mildewproof dew resisting coating and preparation thereof
An anti-condensation and anti-mildew technology, applied in anti-fouling/underwater coatings, epoxy resin coatings, coatings, etc., can solve the problems of not being effective for a long time, coating water absorption swelling, and high price
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0038] Example 1: The paint was prepared according to the following ratio.
[0039]
[0040] Use this paint to make coatings and perform functional inspections:
[0041] 1. Hygroscopicity: make coating samples with a thickness of 2mm-3mm. After the prepared sample was naturally dried for 24 hours, it was dried in a drying oven at 80°C for 5 hours. Then it was placed in a humidity-conditioning box for a moisture absorption test, and the test conditions were 25°C and 85% relative humidity. After 48h, take it out and weigh it. Through the mass calculation before and after the test, the moisture absorption of the sample is 280g / m. 2 , Indicating that the test coating has a moisture absorption function; put the moisture-absorbing sample in a humidity-conditioning box with a temperature of 25°C and a relative humidity of 35%. After 48 hours, take it out and weigh it. The moisture release capacity of the sample is 220g / m 2 , Indicating that the test coating has the function of releasi...
Example Embodiment
[0044] Example 2: The paint was prepared according to the following ratio.
[0045]
[0046] The function test was performed with the same method as in Example 1. The result: The coating made of the coating was tested in a humidity control cabinet, and the moisture absorption reached 320g / m under the conditions of a temperature of 25°C and a relative humidity of 85%. 2 ; Under the condition of temperature 25℃ and relative humidity 35%, the moisture release amount is 260g / m 2 , Has a good moisture absorption and release function; the inhibition rate of the coating to six kinds of Candida albicans and Aspergillus niger is 0; the inhibition rate to Staphylococcus aureus and Escherichia coli are: 99.9% and 99.9%; the thermal conductivity of the coating measured by the coating thermal conductivity tester is 0.040W / m·K.
Example Embodiment
[0047] Example 3: The paint was prepared according to the following ratio.
[0048]
[0049] The function test was carried out with the same method as in Example 1. The result: the coating made with the paint was tested in a humidity control cabinet, and the moisture absorption reached 330g / m under the conditions of 25℃ and 85% relative humidity. 2 ; Under the condition of temperature 25℃ and relative humidity 35%, the moisture release amount is 259g / m 2 . The antibacterial performance of the coating to Candida albicans and Aspergillus niger six comprehensive molds are all up to level 0, and the antibacterial performance is 98.9% and 99.9% for Staphylococcus aureus and Escherichia coli respectively. The thermal conductivity of the coating measured by the coating thermal conductivity tester is 0.039W / m·K.
PUM
Property | Measurement | Unit |
---|---|---|
Thermal conductivity | aaaaa | aaaaa |
Moisture absorption | aaaaa | aaaaa |
Humidity release | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap