Melamine-formaldehyde impregnating resin and preparing method thereof

A technology for melamine and impregnating resin is applied in the field of resin and its manufacturing, which can solve the problems of high price and high production cost of melamine-formaldehyde impregnating resin, and achieve the effects of saving resources and energy consumption, saving production cost and reducing cost.

Active Publication Date: 2011-03-30
圣象实业(江苏)有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the high price of caprolactam, the production cost of melamine-formaldehyde impregnated resin is also high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Melamine-formaldehyde impregnating resin and preparing method thereof
  • Melamine-formaldehyde impregnating resin and preparing method thereof
  • Melamine-formaldehyde impregnating resin and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Add 3500kg of purified water, 7500kg of formaldehyde, 600kg of diethylene glycol and 720kg of modifier into the reaction kettle in sequence, stir and add 7L of sodium hydroxide solution to adjust the pH value to 9.23, then add 6800kg of melamine and stir for 10 minutes , the temperature was raised to 90.1°C within 30 minutes, and the control system reacted for 30 minutes at a temperature of 90.1°C and a pH value of 9.23. When it drops below 30°C, adjust the pH value to 8.92, then take samples and discharge.

[0020] Various test results

[0021]

[0022]

[0023] Floor inspection indicators:

[0024]

[0025]

Embodiment 2

[0027] Add 3274kg of purified water, 6100kg of formaldehyde, 400kg of diethylene glycol and 600kg of modifier into the reactor in sequence, stir and add 8L of sodium hydroxide solution to adjust the pH value to 9.5, then add 5426kg of melamine and stir for 10 minutes , the temperature was raised to 85°C within 40 minutes, and the control system reacted for 30 minutes at a temperature of 85°C and a pH value of 9.5, and then a sample was taken to detect the water solubility of the reaction solution. When it drops below 30°C, adjust the pH value to 9.6, then take samples and discharge.

[0028] Various test results

[0029] Test items

Quality Index

Test results

Exterior

colorless transparent liquid

colorless transparent liquid

pH value

8.5-9.6

9.5

Viscosity (s / 20℃) coated with 4# cup

15-25

17

Solid content (wt%)

45-60

53.9

Water soluble ratio (25℃)

1.5-2.5

1.6

Free formaldeh...

Embodiment 3

[0034] Add 1990kg of purified water, 7290kg of formaldehyde, 324kg of diethylene glycol and 162kg of modifiers into the reaction kettle in sequence, stir and add 7L of sodium hydroxide solution to adjust the pH value to 9.26, then add 6434kg of melamine and stir for 10 minutes , the temperature was raised to 90.1°C within 30 minutes, and the control system was reacted at a temperature of 90.1°C and a pH value of 9.26 for 30 minutes, and then samples were taken to detect the water solubility of the reaction solution. When it drops below 30°C, adjust the pH value to 8.97, then take samples and discharge.

[0035] Various test results

[0036] Test items

Quality Index

Test results

Exterior

colorless transparent liquid

colorless transparent liquid

pH value

8.5-9.6

9.0

Viscosity (s / 20℃) coated with 4# cup

15-25

18

[0037] Solid content (wt%)

45-60

59

Water soluble ratio (25℃)

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a melamine-formaldehyde dipping resin which consists of 34-45 percent of formaldehyde, 30-40 percent of melamine, 1-4 percent of diethylene glycol, 12-28 percent of purified water, 1-4 percent of modifying agent and sodium hydroxide according to weight percentage; the invention further discloses a preparation method of the melamine-formaldehyde dipping resin. Caprolactam is omitted in the raw material formulation; by changing the formulation of raw material composition, each performance index of the polymer resin, which is finally generated, meets each index requirement of the dipping resin; when the dipping resin is used for manufacturing laminated flooring, the detected performance indexes of the flooring also meet the quality index requirements. As the caprolactam is omitted in the raw material formulation, production cost is greatly saved and process steps are simplified.

Description

technical field [0001] The invention relates to a resin and its manufacturing method, in particular to a melamine-formaldehyde resin and a manufacturing method of the resin. The resin can be simultaneously used for impregnating wear-resistant paper, decorative paper and balancing paper of laminate flooring. Background technique [0002] When laminate flooring is processed, melamine-formaldehyde resin is generally used to impregnate the wear-resistant paper, decorative paper and balance paper of laminate flooring, and then these three impregnated papers are pressed on the substrate with a low-pressure short-cycle press to form an impregnated layer. Press the floor. The melamine-formaldehyde impregnated resin is formed by the addition reaction of melamine and formaldehyde under alkaline conditions to generate methylol melamine, and then form a resin. However, the resin formed under such conditions is relatively brittle and needs to be used in the production of laminated wood ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G12/32C08L61/28C08K5/053C08K5/06C08K5/435
Inventor 王素鹏贡建
Owner 圣象实业(江苏)有限公司