Water soluble adhesive and preparation method thereof

An adhesive and water-soluble technology, applied in the field of water-soluble adhesives and their preparation, can solve the problems of low final adhesive strength, low initial adhesive strength, and high cost, and achieve the effect of long-term performance maintenance and anti-aging effect

Active Publication Date: 2009-07-22
际华制鞋工业有限公司
View PDF0 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Solvent-based glue has the disadvantages of difficult processing, high energy consumption, high cost, long processing cycle, and high toxicity. At the same time, it also has quality defects such as low initial adhesive strength and low final ad

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0093] Example 1 Raw materials: 100kg of natural latex, 8kg of soft water, rubber compounding agent (vulcanizing agent: sulfur 0.3kg, vulcanization accelerator M0.4kg, vulcanization active agent: zinc oxide 0.4kg, diffusing agent 0.1kg, anhydride casein 0.1kg, Borax 0.01kg, stabilizer (H2kg), ammonia water 1kg, potassium hydroxide 0.3kg, sodium carboxymethyl cellulose 0.2kg, wetting agent JFC 0.4kg, anti-aging agent 4010NA 0.3kg, defoamer 0.1kg, antifungal agent 0.004 kg

[0094] Preparation:

[0095](1) Preparation of ball milling liquid: dissolve potassium hydroxide with 3.2kg of soft water, then add sulfur, vulcanization accelerator M, zinc oxide, anti-aging agent, defoamer, diffusing agent, casein anhydride and borax in sequence, then add 3.2 kg of soft water, stirred evenly, sealed ball milled in a ball mill tank for 24 hours to obtain a ball mill liquid, the total weight of ceramic balls in the ball mill tank is 8 kg, of which: the weight of ceramic balls with a diamete...

Embodiment 2

[0101] Example 2 Raw materials: 100kg of natural latex, 7kg of soft water, rubber compounding agent (vulcanizing agent (sulfur) 1.0kg, vulcanization accelerator M 0.3kg, vulcanization activator (active zinc oxide) 0.3kg, diffusing agent 0.3kg, anhydride casein 0.3kg, borax 0.01kg, stabilizer H1kg), ammonia 2kg, potassium hydroxide 0.2kg

[0102] Preparation:

[0103] (1) Preparation of ball milling fluid: Dissolve potassium hydroxide with 2.8kg of soft water, then add vulcanizing agent, vulcanization accelerator, vulcanization activator, diffusing agent, anhydride casein and borax in turn, then add 2.8kg of soft water, stir evenly , sealed and milled in a ball mill tank for 22 hours to obtain a ball mill liquid, the total weight of the ceramic balls in the ball mill tank is 8 kg, wherein: the weight of the ceramic balls with a diameter of 20 to 40 mm is 6 kg, and the weight of the ceramic balls with a diameter of 10 to 15 mm is 2 kg; use up the ball milling liquid within one ...

Embodiment 3

[0106] Example 3 Raw materials: 100kg of natural latex, 12kg of soft water, rubber compounding agent (0.2kg of vulcanizing agent, 1.0kg of vulcanization accelerator, 1.0kg of vulcanization active agent, 0.1kg of diffusing agent, 0.1kg of casein anhydride, 0.03kg of borax, stabilizer 3kg), ammonia water 0.5kg and potassium hydroxide 0.5kg, carboxymethyl cellulose sodium 0.5kg, wetting agent 3kg

[0107] (1) Preparation of ball milling liquid: dissolve potassium hydroxide with 40% soft water, then add vulcanizing agent, vulcanization accelerator, vulcanization activator, diffusing agent, anhydride casein and borax in turn, then add 40% soft water, stir evenly , sealed and milled in a ball mill tank for 28 hours to obtain a ball mill liquid, the total weight of the ceramic balls in the ball mill tank is 8 kg, wherein: the weight of the ceramic balls with a diameter of 20-40mm is 6 kg, and the weight of the ceramic balls with a diameter of 10-15mm is 2 kg; use up the ball milling ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a water-soluble adhesive and a preparation method thereof. The water-soluble adhesive is prepared mainly by natural latex, soft water, a vulcanizing agent, a vulcanization accelerator, a vulcanizing activator, a dispersant, anhydride casein, borax, a stabilizer, a wetting agent, ammonia and potassium hydroxide. In order to improve the performance of the water-soluble adhesive, carboxymethyl cellulose sodium, the wetting agent, an age inhibitor, an antifoaming agent and a mildew inhibitor also can be added; the obtained water-soluble adhesive is an environment-friendly material which is used for shoes, has the processing advantages of low energy consumption, non-toxicity, good processing property, simple operation and the like in the preparation process, strengthens self deterioration resistance, greatly prolongs the storage stabilization period of slurry, improves the intrinsic performance of the adhesive, and fundamentally realizes the demand of high adhesive strength on rubber shoes.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to a water-soluble adhesive and a preparation method thereof. Background technique [0002] Adhesive glue for rubber shoes, also known as adhesive, commonly known as glue, its purpose is to bond the rubber shoes skirt and shoe upper, so that the rubber shoes skirt film and the shoe upper form a firm whole. The main indicator for judging the performance of the adhesive is the bonding strength between the rubber shoe skirt film and the shoe upper. The measured value of the bond strength between the rubber shoe skirt film and the shoe upper is often used to indicate the adhesive performance of the adhesive on the rubber shoes. [0003] Under normal circumstances, the adhesive mortar of rubber shoes is a solvent-based mortar that uses rubber compound rubber as the solute and an organic solvent as the solvent. The solvent-based mortar usually uses 120# gasoline or toluene as the solven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J107/02A43B9/12
Inventor 晋齐怀陈松雄杜江周川泉杨东田吉王永生彭德彪
Owner 际华制鞋工业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap