A phase transition material, room temperature vulcanization technology, applied in the field of two-component addition type room temperature vulcanized silicone rubber, can solve the problems of reducing the physical and mechanical properties of the silicone rubber material, shortening the service life of the material, etc.

Inactive Publication Date: 2010-02-10
合肥凯蒙新材料有限公司
View PDF1 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It directly mixes the phase-change material accounting for more than 40% of the weight of silicone rubber with silicone rubber, which reduces the physical and mechanical properties of the silicone rubber material. The liquid phase-change material will separate from the silicone rubber in a short time and precipitate, greatly shortening the material. service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0049] A two-component addition type room temperature vulcanizing silicone rubber containing a phase change material, including a base component and a catalyst component in separate packages:

[0050] (1), basic components, each raw material component has:

[0051] (1) Methyl vinyl silicone oil: 20%-40% by weight, linear methyl vinyl silicone oil with a viscosity of 50 centipoise to 65,000 centipoise can be used, and several methyl vinyl silicone oils with different viscosities can be mixed Adjust to the required viscosity, but the linear methyl vinyl silicone oil with two vinyl end groups on each molecule is more suitable, the vinyl molar content of the methyl vinyl silicone oil is 0.05-0.5%, such as Zhejiang Xin'an Chemical Group Production of methyl vinyl silicone XHG-110 series;

[0052] (2), methyl hydrogen-containing silicone oil crosslinking agent, weight percentage 0.5-3%, viscosity 20-50 centipoise, hydrogen content 0.3-1.0%. It is required that hydrogen atoms on met...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses a dual composition addition type room temperature silicon disulfide rubber containing phase transformation material, comprising a basic composition and a catalyst composition with the volume ratio being 1:1; the basic composition comprises the following raw material components: 20-40% of methyl vinyl silicone oil, 0.5-3% of cross linking agent methyl silicone oil containinghydrogen, 0.01-0.5% of inhibitor, 1-10% of plasticizer, 30-60% of silicon dioxide premix filler, 3-15% of other filler, 1-5% of additive, and 0-5% of pigment; the catalyst composition comprises the following raw material components: 20-40% of methyl vinyl silica gel, methyl vinyl oxosilane coordination platinum complex catalyst, 1-10% of plasticizer, 30-60% of silicon dioxide premix filler, 3-15%of other filler, and 1-5% of additive. The invention ensures the room temperature vulcanization velocity of the dual composition addition type room temperature silicon disulfide rubber to maintain constant basically in a wider temperature range, is suitable for manufacturing dental impression and ear impression materials, heat insulation protection materials, curtains, vehicle seat cushions, drugpackage materials, cold-proof materials and the like.

Description

technical field [0001] The invention relates to the field of silicone rubber, in particular to a two-component addition type room temperature vulcanized silicone rubber containing a phase transition material. Background technique [0002] Addition RTV silicone rubber is divided into two components before vulcanization, one component is mainly methyl vinyl silicone oil and methyl hydrogen-containing silicone oil crosslinking agent, and the other component is mainly a platinum complex catalyst. When using, mix the two components evenly in a certain proportion, and vulcanize at room temperature. The principle of the vulcanization reaction of two-component addition type room temperature vulcanized silicone rubber is an addition reaction. The vinyl group on the methyl vinyl silicone oil molecule is catalyzed by the platinum complex with the silane hydrogen (-SiH) of the methyl hydrogen silicone oil crosslinking agent. Hydrogen) undergoes an addition reaction to generate -CH 2 -...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/07C08L83/05C08K13/06C08K3/36C08K5/01C08K3/24C08K3/28C08K3/30C08K3/32
Inventor 何流
Owner 合肥凯蒙新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap