Self-adhesive polymer modified bituminous polyester fiber waterproof sheet material and preparation technology thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of modified asphalt and waterproof membrane, which is applied in water conservancy projects, asphalt layered products, and roofs using flexible materials, etc. Good elasticity, increased flexibility, good physical properties
Inactive Publication Date: 2010-02-10
北京立高科技股份有限公司 +1
View PDF0 Cites 27 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] The invention provides a self-adhesive polymer modified bituminous polyester tire waterproofing membrane and its preparation process, to solve the te
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0041] Embodiment 1, this kind of self-adhesive polymer modified asphalt polyester tire waterproof membrane includes polyester cloth, oil-impregnated coating layer and film layer, and the material ratio of the oil-impregnated coating layer is as follows :
[0042] 40 parts of 90# asphalt;
[0043] 13 parts of engine oil;
[0044] 5 parts of SBS glue;
[0045] 7 parts of SBR glue;
[0046] 7 parts of EPDM rubber powder;
[0047] 2 parts butyl rubber powder;
[0048] 25 parts of talcum powder;
[0049] 1 part petroleum resin.
Embodiment 2
[0050] Embodiment 2, this self-adhesive polymer modified asphalt polyester tire waterproofing membrane includes polyester cloth, oil-impregnated coating layer and film layer, and the material ratio of the oil-impregnated coating layer is as follows in parts by mass :
[0051] 42 parts of 90# asphalt;
[0052] 8 parts of engine oil;
[0053] 7 parts of SBS glue;
[0054] 4 parts of SBR glue;
[0055] 4 parts of EPDM rubber powder;
[0056] 4 parts butyl rubber powder;
[0057] 28 parts of talcum powder;
[0058] 3 parts petroleum resin.
[0059] The oil-impregnated layer may also contain conventional inorganic or organic reinforcing agents such as carbon black.
Embodiment 3
[0060] Embodiment 3, this self-adhesive polymer modified asphalt polyester tire waterproof membrane includes polyester cloth, oil-impregnated coating layer and film layer, and the material ratio of the oil-impregnated coating layer is as follows in parts by mass :
[0061] 37 parts of asphalt;
[0062] 18 parts of engine oil;
[0063] 10 parts of SBS glue;
[0064] 2 parts of SBR glue;
[0065] 2 parts of EPDM rubber powder;
[0066] 2 parts butyl rubber powder;
[0067] 25 parts of talcum powder;
[0068] 4 parts petroleum resin.
[0069] The oil-impregnated layer may also contain conventional inorganic or organic reinforcing agents such as carbon black.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides a self-adhesive polymer modified bituminous polyester fiber waterproof sheet material and preparation technology thereof. The waterproof sheet material comprises polyester cloths, an immersion oil coating layer and a film-mulching layer. The immersion oil comprises the following materials in parts by mass: 37-47 parts of bitumen, 8-18 parts of machine oil, 5-10 parts of SBSrubber, 2-12 parts of SBR rubber, 2-12 parts of EPDM rubber powder, 2-7 parts of butyl rubber powder, 25-35 parts of talc powder and 1-10 parts of petroleum resins. The bitumen is 90# one. The invention has the effects as follows: the waterproof sheet material uses the EPDM modified bitumen as the base material and polyester cloths as the matrices; the back of the adhesive side is covered by the reinforced self-adhesive waterproof sheet material of abherent, thus achieving the effect of sticking while adhering and improving the construction efficiency; the waterproof sheet material is characterized by solvent-free construction, safety and no scald; the waterproof sheet material has shining surface and good elasticity, and the properties of the waterproof sheet material are not obviously changed after aging through laboratory test.
Description
technical field [0001] The invention relates to a building waterproof coiled material and a preparation process of the waterproof coiled material. Background technique [0002] Waterproof membrane is a commonly used building material in building construction. In underground engineering and water conservancy engineering construction, waterproof membrane is of great significance to reduce leakage and withstand high water pressure. The existing EPDM waterproof membrane has excellent properties such as high strength, high elongation, high tear strength, high and low temperature resistance, ozone resistance, and aging resistance, so it is widely used in building construction. However, after the existing EPDM waterproofing membrane is laid, the waterproof base material cannot be closely combined with the building base, and water leakage is easy to occur. In case of local water seepage in the waterproof layer, it will also cause "water channeling" under the entire waterproof layer...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more