Carbon steel pickling inhibitor and preparation method and application thereof

A technology of corrosion inhibitor and carbon steel acid, which is applied in the field of steel pickling corrosion inhibitor and its preparation, can solve the problems of poor environmental friendliness, prone to pitting corrosion, unsafe use, etc., and achieve high corrosion inhibition effect and corrosion inhibition The effect of stable performance and low cost

Inactive Publication Date: 2010-04-07
深圳市爱康泉水处理有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Among the currently commonly used corrosion inhibitors, inorganic compounds such as chromate, nitrate, and nitrite, due to their toxic side effects, poor environmental friendliness, and some are unsafe to use and prone to pitting corrosion, their applications are being restricted and will gradually disuse

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Weigh 2-amino-5-p-hydroxyphenyl-1,3,4-thiadiazole 1g and 2-amino-5-(4-pyridyl)-1,3,4-thiadiazole 30g and mix to make It is a corrosion inhibitor, dissolved in the pickling solution, the pickling solution is dilute hydrochloric acid, the concentration is 0.5mol / L, the amount of pickling solution is 100L, and the carbon steel to be cleaned is immersed in the pickling solution for 4 hours at 20°C .

[0023] The corrosion inhibition efficiency obtained through the experimental test is 91%, which shows that it is an efficient corrosion inhibitor.

Embodiment 2

[0025] Weigh 2-amino-5-p-hydroxyphenyl-1,3,4-thiadiazole 10g and 2-amino-5-(3-pyridyl)-1,3,4-thiadiazole 20g and mix to make It is a corrosion inhibitor, dissolved in the pickling solution, the pickling solution is dilute hydrochloric acid, the concentration is 0.5mol / L, the amount of pickling solution is 100L, and the carbon steel to be cleaned is immersed in the pickling solution for 4 hours at 20°C .

[0026] The corrosion inhibition efficiency obtained through the experimental test is 93%, which shows that it is an efficient corrosion inhibitor.

Embodiment 3

[0028] Weigh 0.5 g of 2-amino-5-p-hydroxyphenyl-1,3,4-thiadiazole and 25 g of 2-amino-5-(3-pyridyl)-1,3,4-thiadiazole and mix As a corrosion inhibitor, dissolve in the pickling solution, the pickling solution is dilute hydrochloric acid, the concentration is 1mol / L, the amount of pickling solution is 100L, and the carbon steel to be cleaned is immersed in the pickling solution for 4 hours at 20°C .

[0029] The corrosion inhibition efficiency obtained through the experimental test is 92%, which shows that it is an efficient corrosion inhibitor.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a carbon steel pickling inhibitor, a preparation method and application thereof, in particular to a thiadiazole carbon steel pickling inhibitor, a preparation method and application thereof. The inhibitor is a mixture of any two or three of 2-amino-5-(p-hydroxyphenyl)-1,3,4-thiadiazole, 2-amino-5-(4-pyridyl)-1,3,4-thiodiazol or 2-amino-5-(3-pyridyl)-1,3,4-thiodiazol. The inhibitor in the invention can effectively prevent the carbon steel materials from being corroded by sulfuric acid in the pickling process, and has the advantages of environment protection, low usage amount, high corrosion inhibition efficiency, stable performance and the like.

Description

technical field [0001] The invention relates to a steel acid pickling corrosion inhibitor and its preparation method and application, in particular to a thiadiol used to prevent carbon steel and its products from being corroded by acid on carbon steel materials and excessive consumption of acid solution in the process of sulfuric acid pickling An azole carbon steel pickling corrosion inhibitor and its preparation method and application. Background technique [0002] In metal materials, machinery, metallurgy, chemical industry and other industries, sulfuric acid is often used to clean the rust and dirt on the surface of metal materials in systems such as pipelines and boilers, so pickling is of great significance to maintain the normal operation of equipment. [0003] Because in the pickling process, the strong acid will also corrode the metal equipment while removing the rust and dirt, so the phenomenon of "over-corrosion" often occurs in the pickling process, resulting in c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23G1/06C23G1/08
Inventor 杨晓远唐永明刘英尹晓爽杨文忠万嵘
Owner 深圳市爱康泉水处理有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com