Preparation method of hot-melt reaction type adhesive for composite material
A composite material, reactive technology, applied in the direction of adhesive types, polyurea/polyurethane adhesives, adhesives, etc., can solve the problems of poor environmental protection performance of materials, poor operating environment, and wide variety, and achieve excellent weather resistance, The effect of good handling stability and high compound fastness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0017] Embodiment 1 of the present invention provides a method for preparing an adhesive for hot-melt reactive composite materials. The prepared adhesive has high initial adhesion fastness and stable performance, and is suitable for various composite substrates to prepare environmentally friendly composite materials. , the preparation method specifically includes:
[0018] Preparation of polyester polyol:
[0019] a. Esterification:
[0020] 10-20 parts by mass of dimethyl terephthalate, 25-35 parts by mass of ethylene glycol, 15-30 parts by mass of adipic acid, 5-10 parts by mass of sebacic acid, 25-35 parts by mass of Add 1,4-butanediol into the polyester synthesis kettle, heat up to 210-240°C, react for 6-8 hours, and the esterification is completed;
[0021] In the above-mentioned esterification step, keep the distillate of the distillate of the polyester synthesis tank at 1 to 3 parts by mass / hour; after the esterification reaction is completed, take a sample to measure...
Embodiment 2
[0032] This embodiment 2 provides a preparation method of an adhesive for hot-melt reactive composite materials. The prepared adhesive has high initial adhesion fastness and stable performance, and is suitable for various composite substrates to prepare hot-melt reactive environmental protection adhesives. Composite material, the preparation method specifically includes:
[0033] (1) Preparation of polyester polyol:
[0034] Get each raw material according to the following ratio:
[0035] Raw material ratio (parts by mass)
[0036] Dimethyl terephthalate 15
[0037] Ethylene glycol 25
[0038] Adipic acid 26
[0039] Sebacic acid 6
[0040] 1,4 Butanediol 28
[0041] The preparation method of polyester polyol:
[0042] a. Primary esterification:
[0043] 15 mass parts of dimethyl terephthalate, 25 mass parts of ethylene glycol, 6 mass parts of adipic acid, 6 mass parts of sebacic acid, 28 mass parts of 1,4 butanediol were added to In the polyester synthesis kettle, he...
Embodiment 3
[0058] Embodiment 2 of the present invention provides a method for preparing an adhesive for hot-melt reactive composite materials. The prepared adhesive has high initial adhesion fastness and stable performance, and is suitable for various composite substrates to prepare hot-melt reactive adhesives. The environmentally friendly composite material, the preparation method specifically includes:
[0059] (1) Preparation of polyester polyol:
[0060] Get each raw material by following mass ratio:
[0061] Raw material ratio (parts by mass)
[0062] Dimethyl terephthalate 20
[0063] Ethylene glycol 30
[0064] Adipic acid 15
[0065] Sebacic acid 10
[0066] 1,4 Butanediol 25
[0067] The method for preparing polyester polyol in this example is basically the same as the method for preparing polyester polyol given in Example 2. Please refer to Example 2, and will not repeat the description here.
[0068] (2) Compounding:
[0069] Get each raw material according to the foll...
PUM
Property | Measurement | Unit |
---|---|---|
Viscosity | aaaaa | aaaaa |
Viscosity | aaaaa | aaaaa |
Viscosity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap