Anti-light reflection ultraviolet light curing coating for plastic surfaces

A technology of curing coatings and ultraviolet light, applied in polyurea/polyurethane coatings, coatings, etc., can solve the problems of poor heat resistance and anti-light reflection performance, low hardness, and limit the use of polyester plastic films, etc., to achieve good wear resistance Scratch resistance, high surface hardness, light reflectance reduction effect

Inactive Publication Date: 2010-07-14
WUJIANG YOUXIN NEW MATERIAL TECH
View PDF1 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to its low hardness, poor heat resistance and anti-light

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A kind of anti-light reflective ultraviolet light curable paint for plastic surface, comprises following component:

[0036] Urethane acrylate (CN9010): 41.5%

[0037] Difunctional acrylate monomer (HDDA): 25%

[0038] Difunctional acrylate monomer (SR368): 15%

[0039] UV initiator (1104): 3%

[0040] Organosiloxane type leveling agent (DEUCHEM-432): 3%

[0041] Degussa (LTW): 1%

[0042] Nano silica: 1.5%

[0043] Ethyl acetate: 10%

[0044] After mixing the above-mentioned components except ethyl acetate in a closed container, add ethyl acetate and mix evenly, spray on a 0.188mm PET film, dry in an oven at 50 degrees for 3 minutes, and Test after curing by high-pressure mercury lamp: the pencil hardness of the coated biaxially oriented PET film is 3H, and when observed with the naked eye under a yellow monochromatic light source, the rainbow pattern is significantly lower than that of the sample of the comparative example. The coated sample was wiped 20 times ...

Embodiment 2

[0046] A kind of anti-light reflective ultraviolet light curable paint for plastic surface, comprises following component:

[0047] Polyurethane acrylate (CN9010): 20%

[0048] Urethane acrylate (CN710): 25%

[0049] Difunctional acrylate monomer (HDDA): 42%

[0050] UV initiator (1104): 4%

[0051] Organosiloxane type leveling agent (DEUCHEM-432): 3%

[0052] Nano Titanium Dioxide: 4%

[0053] Butyl acetate: 5%

[0054] After mixing the above-mentioned components except butyl acetate in a closed container, add butyl acetate and mix evenly, spray it on a 0.188mm PET film, dry it in an oven at 50 degrees for 3 minutes, and Test after curing by high-pressure mercury lamp: the pencil hardness of the biaxially oriented PET film after coating is 2H. When observed with the naked eye under a yellow monochromatic light source, the rainbow pattern is significantly lower than that of the sample of the comparative example. The coated sample was wiped 20 times with 000# steel wool (...

Embodiment 3

[0056] A kind of anti-light reflective ultraviolet light curable paint for plastic surface, comprises following component:

[0057] Urethane acrylate (CN710): 15%

[0058] Monofunctional acrylate monomer (cyclohexyl acrylate): 60%

[0059] UV initiator (benzophenone): 1%

[0060] Organosiloxane-free defoamer (BYK-055): 0.5%

[0061] Degussa LTH: 20%

[0062] Nano magnesium difluoride: 0.1%

[0063] Ethanol: 3.4%

[0064] Mix the above-mentioned components except ethanol in an airtight container, then add ethanol and mix evenly, spray it on a 0.188mm PET film, dry it in an oven at 50 degrees for 3 minutes, and cure it with a high-pressure mercury lamp Test: the pencil hardness of the biaxially stretched PET film after coating is 2H, and the rainbow pattern is lower than that of the sample of the comparative example when observed with the naked eye under a yellow monochromatic light source. The coated sample was wiped 20 times with 000# steel wool (500 g force), without tr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an anti-light reflection ultraviolet light curing coating for plastic surfaces, which comprises urethane acrylate containing vinyl unsaturated groups, acrylate activated monomers containing vinyl unsaturated groups, UV initiators, additives and solvents and is characterized by also being added with nano-scale magnesium fluoride, silicon dioxide or titanium dioxide. The nano-scale magnesium fluoride, silicon dioxide or titanium dioxide is added into the curing coating component of the product of the invention, so that the prepared product has obvious effect on preventing light reflection of ultraviolet light. Compared with the product which is not added with nano-scale magnesium fluoride, silicon dioxide or titanium dioxide, by observation under a yellow monochromatic source by naked eyes, the rainbow patterns of the product of the invention are obviously reduced.

Description

technical field [0001] The invention relates to a coating composition for plastics, in particular to an anti-reflection ultraviolet curing coating composition for plastic surfaces, and belongs to the field of coatings for plastics. Background technique [0002] With the rapid development of plastic film products in the world, companies are actively committed to the research and development and promotion of special performance plastic films, and new functional plastic films are constantly being applied to various fields of production, life and consumption. Japan's Sumitomo Bakelite, Toray, Dongshan, General Electric (GE) in the United States, and SKC (Sunkyong) in South Korea all have some unique functional plastic film products. The development of special plastic films with independent intellectual property rights according to special purposes has become the only way for the development of the plastics industry. The coating on the surface of plastic film is an important way...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/14C09D7/12
Inventor 陈敏田家乐
Owner WUJIANG YOUXIN NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap