Synthetic magnetic field type on-line steel rail welding seam normalizing treatment method and normalizing middle-frequency inductor

A technology of synthetic magnetic field and normalizing treatment, which is applied in the direction of track, track laying, track maintenance, etc., can solve the problems of poor normalizing quality, low heating efficiency, slow internal heating, etc., to improve the surface quality of rails and the quality of normalizing. , to ensure the effect of consistency

Active Publication Date: 2010-08-04
WUHAN LEADDO MEASURING & CONTROL CO LTD
View PDF7 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] (1) Open fire heating, the surface heats up quickly, the internal temperature rises slowly, and the heating efficiency is low;
[0005] (2) Flame heating, large temperature difference between core and surface, uneven heating, and poor normalizing quality;
[0006] (3) Oxygen is used for combustion in the flame normalizing process, which causes the surface of the rail to be oxidized, resulting in a thicker scale, which affects the surface quality of the rail;
[0007] (4) Open flame heating is difficult to achieve automatic control and temperature detection, so it is difficult to ensure the consistency of weld normalizing quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Synthetic magnetic field type on-line steel rail welding seam normalizing treatment method and normalizing middle-frequency inductor
  • Synthetic magnetic field type on-line steel rail welding seam normalizing treatment method and normalizing middle-frequency inductor
  • Synthetic magnetic field type on-line steel rail welding seam normalizing treatment method and normalizing middle-frequency inductor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0030] Below in conjunction with accompanying drawing and specific embodiment the present invention is described in further detail:

[0031] figure 1 and figure 2 It is a schematic structural diagram of using an annular hollow coil inductor to cover the weld of the rail 3 for electromagnetic induction heating in the existing rail welding workshop. Its working principle has been introduced in detail in the background technology section, so it will not be repeated here.

[0032] Since the annular inductor cannot be set on the laid rail 3, the present invention proposes a method of normalizing the online rail by utilizing two sub-inductors that can be separated and closed. The heating process is as follows: two independent and identical sub-inductors are coated on the outer surface of the weld seam of the online rail, and the inner shape of the two sub-inductors after fastening is consistent with the cross-sectional shape of the rail; After covering, the contact surfaces of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to a synthetic magnetic field type on-line steel rail welding seam normalizing treatment method and a normalizing middle-frequency inductor, which relate to the field of middle-frequency induction heating and are used for overcoming the defects of roaring flame normalizing treatment. The method adopts two separate and identical sub-inductors to coat the external surface of an on-line steel rail welding seam, and the inner form of the two buckled sub-inductors fits into the external form of the section of a steel rail; the contact surfaces of the two sub-inductors are mutually insulated, a middle-frequency alternating current is introduced into the two sub-inductors so that a vortex is produced at the on-line steel rail welding seam for heating, and thus, the normalizing treatment process is completed. The normalizing middle-frequency inductor comprises a pair of identical and symmetrical sub-inductors of which the inner forms respectively correspond to the external form of the half section of the steel rail, and the two buckled sub-inductors are used for coating the on-line steel rail; and the contact surfaces between the two sub-inductors after coating are mutually insulated. The inductor can be conveniently buckled and coated to the steel rail welded into a line, and the on-line middle-frequency normalizing treatment of the steel rail welding seam is realized.

Description

technical field [0001] The invention relates to the field of intermediate frequency induction heating, in particular to a synthetic magnetic field type online rail weld seam normalizing treatment method and a normalizing intermediate frequency inductor. Background technique [0002] The laying process of modern railways is to first weld the 100-meter-long short rails into 500-meter long rails with a flash welding machine in the rail welding workshop, then transport the long rails to the line, and use the flash welding on the mobile rail welding car The machine welds the long rails into lines. [0003] No matter in the rail welding workshop or on the laying line, every time the flash welding machine welds, a weld will be produced. Due to the high temperature of the weld, the brittleness of the metal structure at the weld will increase and the toughness will decrease. In order to improve the plasticity and toughness of the weld and improve the comprehensive mechanical propert...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): E01B31/18
Inventor 叶新民江惠生张保军陈斌方开慧
Owner WUHAN LEADDO MEASURING & CONTROL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products