Macromolecular fluorescent microspheres and preparation method thereof
A technology of fluorescent microspheres and polymers, which is applied in the field of preparation of fluorescent sensing materials, can solve the problems of poor solubility of conjugated polymers, difficulties in the adjustment and controllability of fluorescent properties, and achieve easy characterization, heterogeneous Simple and controllable effects
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0022] Example one:
[0023] 1. Using Wessling's salt polymer precursor method: In a 50ml two-necked flask, protected with nitrogen, add 1.0g benzene ring with dodecyloxy side chain polymerized monomer and dissolve in 10ml tetrahydrofuran solution , Magnetically stir to make it completely dissolved, put it in an ice water bath, keep the reaction system at 0~5℃ under the protection of nitrogen, slowly add 2.4ml of 1.25M NaOH / MeOH solution, after reacting for 1 hour, add HCl to stop the reaction. The reaction solution is put into a dialysis bag with a molecular weight of 14000 and dialyzed in water for 24 hours to prepare a precursor of polymer PPV. The synthesis route is as follows:
[0024]
[0025] Among them, n is the number of repeating units.
[0026] See attached figure 1 , It is the nuclear magnetic map (HNMR) of the above-mentioned polystyrene (PPV) precursor, with deuterated chloroform as the solvent, at 7.0~6.7ppm, 4.5ppm, 3.9ppm, 2.9ppm, 1.9ppm and 0.9ppm, etc. It is the ...
Example Embodiment
[0030] Embodiment two:
[0031] 1. In a 50ml two-necked flask, protected with nitrogen, add 0.5g of polymer monomer without side groups, dissolve it in 10ml of water, magnetically stir to dissolve it completely, put it in an ice water bath, make the reaction system under nitrogen protection Keep 0~5℃, add 1.25M NaOH / H 2 1ml of O solution, after reacting for 1 hour, add HCl to terminate the reaction, put the reaction solution into a dialysis bag with a molecular weight of 14000 and dialyze in water for 24 hours to prepare the precursor of polymer PPV. The synthesis route is as follows:
[0032]
[0033] 2. Add 0.5 g of the precursor prepared in step 1 into an Erlenmeyer flask, dissolve it with 10 ml of water, and add 0.5 g of monodisperse polystyrene microspheres with a particle size of 25 microns on the surface, using 1.25M Adjust the pH value of NaOH to 9 and ultrasonically vibrate in an ultrasonic vibrator for 1 hour. After keeping the water temperature of the ultrasonic vibrator...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap