Cerium-ion activated flashing light-emitting material for X-ray detection and method for preparing the same

A scintillation luminescence and X-ray technology, applied in luminescent materials, chemical instruments and methods, etc., to achieve the effects of high light yield, simple preparation process and easy control of conditions

Inactive Publication Date: 2010-10-20
SUN YAT SEN UNIV
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is no relevant report on the use of alkaline earth metal ch

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cerium-ion activated flashing light-emitting material for X-ray detection and method for preparing the same
  • Cerium-ion activated flashing light-emitting material for X-ray detection and method for preparing the same

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0012] Example 1

[0013] Weigh anhydrous sodium carbonate (Na 2 CO 3 )0.0021g, cerium oxide (CeO 2 )0.0069g, aluminum oxide (Al 2 O 3 ) 0.4078g, strontium carbonate (SrCO 3 ) 1.1692g, strontium chloride (SrCl 2 ·6H 2 O) 1.0665g, grind and mix evenly in a mortar, transfer to alumina crucible, 5% H 2 -95% N 2 It is calcined at 1000°C for 5 hours in an atmosphere. Cooling and grinding, the X-ray powder diffraction results of the sample and Sr 3 Al 2 O 5 Cl 2 The standard card (JCPDS no80-0564) is consistent, and the composition formula is Sr 2.98 Ce 0.01 Na 0.01 Al 2 O 5 Cl 2 Powder scintillating material. When the scintillation material is excited at 340nm, its fluorescence wavelength is between 350-600nm, its strongest emission peak is about 440nm, and the corresponding fluorescence lifetime is 33.8 nanoseconds. Combine the sample with the reference sample BaF 2 Test and compare under the same conditions, such as figure 1 Shown. Calculated sample Sr 2.98 Ce 0.01 Na 0.01 Al 2 O ...

Example Embodiment

[0014] Example 2

[0015] This embodiment is basically the same as embodiment 1, except that Ce is increased 3+ The doping content. Weigh anhydrous sodium carbonate (Na 2 CO 3 )0.0212g, cerium oxide (CeO 2 )0.0688g, aluminum oxide (Al 2 O 3 ) 0.4078g, strontium carbonate (SrCO 3 )1.0629g, strontium chloride (SrCl 2 ·6H 2 O) 1.0665g, grind and mix evenly in a mortar, transfer to alumina crucible, 5% H 2 -95% N 2 It is calcined at 1000°C for 5 hours in an atmosphere. The powder scintillation material is obtained by cooling and grinding.

Example Embodiment

[0016] Example 3

[0017] This embodiment is basically the same as Embodiments 1 and 2, except that Ce is further increased. 3+ The doping content. Weigh anhydrous sodium carbonate (Na 2 CO 3 )0.0636g, cerium oxide (CeO 2 ) 0.2065g, aluminum oxide (Al 2 O 3 ) 0.4078g, strontium carbonate (SrCO 3 )0.8267g, strontium chloride (SrCl 2 ·6H 2 O) 1.0665g, grind and mix evenly in a mortar, transfer to alumina crucible, 5% H 2 -95% N 2 It is calcined at 1000°C for 5 hours in an atmosphere. The powder scintillation material is obtained by cooling and grinding.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses cerium-ion activated flashing light-emitting material for X-ray detection and a method for preparing the same. The cerium-ion activated flashing light-emitting material has the chemical formula of M3-2xCexM'xAl2O5Cl2, wherein the M is one or more components comprising Sr, Ca and Ba, the M' is one or more components comprising Li, Na, K, Rb and Cs, and the x is molar weight of the Ce-displaced M and is more than 0 and less than or equal to 0.5. The cerium-ion activated flashing light-emitting material has the light yield of three times or more higher than the commercialBaF2 under the activation of the X-ray, short fluorescence decay time of 10-40 ns and good physicochemical properties and flashing and light emitting properties, is stable, can not deliquesce easily in the air and can emit the fluorescent wave with the length of 350-600 nm and the highest peak of 440 nm. The cerium-ion activated flashing light-emitting material is synthesized with the traditional high-temperature solid-phase method and the simple process safely and conveniently in the controllable condition, and the method for preparing the cerium-ion activated flashing light-emitting material is easy to operate.

Description

technical field [0001] The invention relates to a scintillation luminescent material, in particular to a scintillation luminescent material activated by trivalent cerium ions for X-ray detection and a preparation method thereof. Background technique [0002] The scintillation luminescent material is transparent in the scintillation wavelength range, and it responds to incident radiation by emitting a light pulse, that is, after being irradiated by X-rays, gamma-rays and other high-energy rays, it absorbs part of the energy and converts it into visible light. The more photons the scintillation material emits after absorbing specific high-energy radiation, the better, so that the accuracy of the detection signal is improved. The fluorescence decay time of the scintillation material is kept as short as possible in order to increase the operating frequency of the detector. If it is used in the field of nuclear medicine imaging, it can greatly reduce the inspection time, improve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09K11/86
Inventor 梁宏斌陈万平苏锵
Owner SUN YAT SEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap