High low temperature toughness carbon steel covered electrode

A high-toughness, carbon steel technology, applied in welding media, welding equipment, welding/cutting media/materials, etc., can solve the problems affecting the low temperature toughness of the electrode, increase the moisture absorption performance of the electrode, low temperature brittle failure, etc., and achieve outstanding economic benefits. and social benefits, beautiful molding, and the effect of improving low temperature toughness

Inactive Publication Date: 2011-01-19
台州海翔焊接材料有限公司 +1
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the price of lithium water glass is 8-10 times that of ordinary water glass; soda ash will increase the moisture absorption performance of the elect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High low temperature toughness carbon steel covered electrode

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0016] The ferromanganese powder described in Example 2 is medium-carbon ferromanganese powder with a carbon content of 1.2%; the carbonate powder is magnesium carbonate powder.

Example Embodiment

[0017] The ferromanganese powder described in Example 3 is a medium-carbon ferromanganese powder with a carbon content of 1.0%; the carbonate powder is calcium carbonate powder, magnesium carbonate powder, and barium carbonate powder, and the weight ratio of the three is 3. : 2:5.

Example Embodiment

[0018] Example 1

[0019] According to the weight part of the carbon steel electrode coating in Example 1 in Table 1, add the coating to the mixer as required, then mix with water glass binder, stir and mix evenly, and then add it to the special electrode coating machine for coating After the carbon steel welding core, it enters the dryer to dry and finalize the shape, and finally, after inspection and packaging, various carbon steel electrodes of different specifications are made.

[0020] Example 2

[0021] According to the distribution ratio of the carbon steel electrode coating in parts by weight in Example 2 in Table 1, other processes are the same as in Example 1, and will not be repeated.

[0022] Example 3

[0023] According to the distribution ratio of the carbon steel electrode coating in Example 3 by weight in Table 1, the other processes are the same as in Example 1, and will not be repeated.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a high low temperature toughness carbon steel covered electrode, belonging to the technical field of metal welding tool. The invention solves the problem that the low temperature toughness of the existing electrode is low. The high low temperature toughness carbon steel covered electrode of the invention comprises a core wire and a coating which is extruded and pressed on the core wire; wherein the coating is composed of the following components by parts by weight: 39-45 parts of reduced ilmenite powder, 3-6 parts of mica powder, 1-6 parts of rutile powder, 10-23 parts of fluorite powder, 4-27 parts of wollastonite powder, 6-16 parts of ferro manganese powder, 0-5 parts of titanium powder, 4-6 parts of carbonate powder, 2-6 parts of marble powder and 3-5 parts of boron powder, and the powders containing the components are mixed to be uniform, so as to obtain the coating of the electrode. The invention has less welding spatter, beautiful moulding, easy slag detaching, high deposition rate and good welding performance; especially low temperature toughness is improved, and low temperature brittleness is prevented from being destroyed; and production cost is low, application range is wide, and use is convenient.

Description

technical field [0001] The invention relates to a welding rod, in particular to a low-temperature high-toughness carbon steel welding rod, which belongs to the field of metal welding tools. Background technique [0002] With the rapid development of the metal manufacturing and processing industry, the technical requirements for the welding electrodes used in the welding process are also getting higher and higher. In the prior art, the raw materials of existing carbon steel welding electrodes such as carbon steel spot welding electrodes with titanium-calcium coating are generally made of rutile, titanium dioxide, reduced ilmenite, medium carbon ferromanganese, white clay, mica, marble, It is composed of clay, wood powder, cellulose and other raw materials; its electrode has defects in material selection and ingredients. In actual use, its electrode spatters larger particles during welding, the arc is unstable, and the surface of the weld seam is prone to pitting after welding...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K35/365
Inventor 金鹏
Owner 台州海翔焊接材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap