Superfine glass wool insulation board and production method thereof

A technology of ultra-fine glass wool and production methods, applied in glass manufacturing equipment, manufacturing tools, etc., can solve the problems of affecting the quality of glass wool glass wool products, restricting the development of glass wool products, and large deviations in glass wool diameters to achieve uniformity Good, environmental protection, simple operation effect

Inactive Publication Date: 2011-01-19
苏州维艾晋新材料有限公司
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, the production methods of ultra-fine glass wool on the market are very complicated, and the diameter deviation of the obtained glass wool is large, and the minimum diameter of the ultra-fine glass wool produced is also 3 μm to 5 μm
This will seriously affect the quality of glass wool and glass wool products, and limit the development of glass wool products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] An ultra-fine glass wool heat insulation board, which is composed of the following materials: broken glass: 600 parts; feldspar 70 parts; borax decahydrate 110 parts; soda ash 30 parts.

[0027] The method of the above-mentioned superfine glass wool insulation board is:

[0028] (a) reclaim cullet, clean and break it;

[0029] (b) Prepare raw materials: feldspar, borax, soda ash, and analyze the composition of raw materials;

[0030] (c) According to requirements: 600 parts of glass, 70 parts of feldspar, 30 parts of soda ash, and 110 parts of borax decahydrate; calculate the amount of various raw materials; then weigh and mix the raw materials and cullet to make a batch;

[0031] The main chemical composition in the batch is SiO 2 65.5%; AL 2 o 3 with Fe 2 o 3 The sum is 2.7%; B 2 C 3 4.85%; the sum of CaO and MgO: 10.8%; Na 2 O and K 2 The sum of O is 15.8%;

[0032] (d) Dissolving the batch material to obtain uniform, pure and transparent glass liquid;

...

Embodiment 2

[0037] An ultra-fine glass wool heat insulation board, which is composed of the following materials: broken glass: 650 parts; feldspar 75 parts; borax pentahydrate 80 parts; soda ash 30 parts.

[0038] The method of the above-mentioned superfine glass wool insulation board is:

[0039] (a) reclaim cullet, clean and break it;

[0040] (b) Prepare raw materials: feldspar, borax, soda ash, and analyze the composition of raw materials;

[0041] (c) According to requirements: 650 parts of glass, 75 parts of feldspar; 80 parts of borax pentahydrate; 30 parts of soda ash; calculate the amount of various raw materials; then weigh and mix the raw materials and cullet to make a batch;

[0042] The main chemical components in the batch are: SiO 2 65.1%; AL 2 o 3 with Fe 2 o 3 The sum is 2.8%; B 2 C 3 5%; the sum of CaO and MgO: 10.7%; Na 2 O and K 2 The sum of O is 15.9%.

[0043] (d) Dissolving the batch material to obtain uniform, pure and transparent glass liquid;

[0044...

Embodiment 3

[0048] An ultra-fine glass wool heat insulation board, which is composed of the following materials: broken glass: 635 parts; feldspar 72 parts; borax pentahydrate 37.5 parts; borax decahydrate 50 parts; soda ash 30 parts.

[0049] The method of the above-mentioned superfine glass wool insulation board is:

[0050] (a) reclaim cullet, clean and break it;

[0051] (b) Prepare raw materials: feldspar, borax, soda ash, and analyze the composition of raw materials;

[0052] (c) According to requirements: cullet: 635 parts; 72 parts of feldspar; 37.5 parts of borax pentahydrate; 50 parts of borax decahydrate; 30 parts of soda ash; Quantify, mix and make batches;

[0053] The main chemical components in the batch are: SiO 2 64.8%; AL 2 o 3 with Fe 2 o 3 The sum is 2.7%; B 2 C 3 4.9%; the sum of CaO and MgO: 10.7%; Na 2 O and K 2 The sum of O is 15.9%.

[0054] (d) Dissolving the batch material to obtain uniform, pure and transparent glass liquid;

[0055](e) The glass ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a superfine glass wool insulation board which is mainly composed of the following components in parts by weight: 600-650 parts of cullet, 70-75 parts of feldspar, 80-110 parts of borax and 30 parts of soda ash. The invention also discloses a production method of the superfine glass wool insulation board. The superfine glass wool insulation board of the invention has high flexibility and good evenness. The production method disclosed by the invention adopts recyclable cullet as a main raw material to realize the cyclic utilization of resources, protect environment and save cost. Meanwhile, the production method of the invention has simple and uncomplicated operation.

Description

technical field [0001] The invention relates to an ultrafine glass wool heat insulation board, in particular to a lightweight, uniform diameter ultrafine glass wool heat insulation board and a production method thereof. Background technique [0002] Ultra-fine glass wool heat insulation board is a new type of fibrous receptacle material. It has excellent properties such as light weight, heat preservation, fire prevention, sound absorption, moth resistance, and corrosion resistance. It is widely used in chemical industry, metallurgy, light industry, electric power, petroleum and achitechive. However, at present, the production methods used for ultra-fine glass wool on the market are very complicated, and the diameter deviation of the obtained glass wool is large, and the minimum diameter of the produced ultra-fine glass wool is also 3 μm to 5 μm. This will have a strong impact on the quality of glass wool and its glass wool products, limiting the development of glass wool pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/00C04B28/00C04B14/42C03B37/04C03C13/00C03C6/02
Inventor 周介明
Owner 苏州维艾晋新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com