Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

High refractive index evaporation material lanthanum titanate mixture and preparation method thereof

A technology of high refractive index and mixture, applied in titanium compounds, chemical instruments and methods, optics, etc., can solve problems such as long sintering time, low yield, and many powders, so as to achieve easy melting and evaporation, reduce sintering time, and reduce use conditional effect

Active Publication Date: 2011-05-18
FUJIAN ACETRON NEW MATERIALS CO LTD
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The existing preparation method of oxide film material is that the powder is directly vacuum sintered by molding or the powder is directly vacuum sintered and broken into particles. The sintering time is long, and it is broken after sintering. The initial powder is more and the yield is low.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Raw material TiO 2 and La(OH) 3 According to the molar ratio La: Ti = 1: 1 configuration, the preliminary catalytic reaction is carried out by water and ethanol as an organic catalyst at room temperature, and then the composite produced by the above catalytic reaction is processed into a certain specification shape by a press, and the semi-finished product obtained is The placed crucible is moved to an atmospheric pressure high-temperature furnace, and the temperature of the furnace is raised to 1300°C for pretreatment to make the product preliminarily shaped, and then the semi-finished product obtained is placed in a vacuum sintering furnace, and the vacuum is evacuated to 10 -3 Pa, keep cooling after 4 hours, and prepare the lanthanum titanate mixture material (La 2 Ti 2 o 7 and La 4 Ti 9 o 24 ). In specific practice, a small amount of Ti can be added to the raw material.

Embodiment 2

[0017] The raw materials TiO2, Ti and La(OH)3 are configured in a molar ratio of 1:2, and the preliminary catalytic reaction is carried out by water and glycerol as an organic catalyst at room temperature, and then the compound produced by the above catalytic reaction is processed by a press Shape into a certain specification, move the crucible of the obtained semi-finished product to an atmospheric pressure high-temperature furnace, raise the temperature of the furnace to 700°C for pretreatment, and make the product preliminarily shaped, then place the obtained semi-finished product in a vacuum sintering furnace and vacuumize to 10 -3 Pa, keep cooling after 2 hours, and prepare the lanthanum titanate mixture material (La 2 Ti 2 o 7 and La 4 Ti 9 o 24 ). In specific practice, a small amount of Ti can be added to the raw material.

[0018] The preparation method of the present invention effectively solves the problem of shape and size through pre-molding and pre-treatmen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a high refractive index evaporation material lanthanum titanate mixture and a preparation method thereof. The mixture is composed of La2Ti2O7 and La4Ti9O24 in a chemical formula. The preparation method thereof comprises the following steps: taking TiO2 and La(OH)3 as raw materials, and mixing to be uniform; carrying out an initial catalytic reaction at normal temperature, and obtaining the required shape by cold pressing or hot pressing; transferring a crucible filled with the obtained semi-finished product into a normal-pressure high-temperature furnace, and heating the furnace to 700-1300 DEG C for processing, thus the product is initially sized; and placing the semi-finished product into a vacuum sintering furnace, heating the whole system to 1400-1600 DEG C and vacuumizing, insulating for 2-4 hours, and cooling to obtain the lanthanum titanate mixture material. The preparation method has high production efficiency, manufacturing cost is low, and lanthanum titanate mixture in arbitrary shape can be prepared, the melting point of the prepared lanthanum titanate mixture is low, and the prepared lanthanum titanate mixture is easy to be melted and evaporated to form a stable optical coating.

Description

【Technical field】 [0001] The invention relates to a high refractive index evaporation material lanthanum titanate mixture and a preparation method thereof. 【Background technique】 [0002] High refractive index optical film materials are widely used in the design of various optical film systems. They are mainly used in conjunction with low refractive index materials or medium refractive index materials to prepare various antireflection films. These films are mainly used in optical instruments. Lenses, prisms, mirrors, etc. Currently widely used high refractive index materials mainly include various titanium, zirconium, hafnium, tantalum, niobium oxides and their mixed materials. [0003] Now, with the continuous update and development of optical applications and the continuous improvement of performance requirements, the evaporated thin film materials must also develop synchronously. The oxide thin film material is an important part of the thin film material, and various el...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G02B1/10C01G23/00
Inventor 陈本宋陈钦忠
Owner FUJIAN ACETRON NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com