Pyrochlore structural rare-earth zirconate material and preparation method and application thereof

A technology of pyrochlore structure and zirconate, which is applied in metal material coating process, coating, fusion spraying, etc., can solve the problem of increased thermal stress of coating, violent fluctuation of thermal expansion coefficient, and reduced thermal cycle life of coating etc. to achieve the effects of reducing thermal stress, improving low-temperature fluctuations, and low thermal conductivity

Active Publication Date: 2011-05-25
SHANGHAI INST OF CERAMIC CHEM & TECH CHINESE ACAD OF SCI
View PDF4 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the thermal expansion coefficients of the zirconate and cerate materials and their single-component doped materials fluctuate sharply in the low temperature range (200-400°C)
Therefore, during use, the thermal stress of the coating increases due to the mismatch of thermal expansion coefficients, and the thermal cycle life of the coating decreases

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pyrochlore structural rare-earth zirconate material and preparation method and application thereof
  • Pyrochlore structural rare-earth zirconate material and preparation method and application thereof
  • Pyrochlore structural rare-earth zirconate material and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Example 1: 0.4La 2 o 3 -0.5Sm 2 o 3 -0.1R″ 2 o 3 -2ZrO 2 Preparation of Ceramic Material Powder

[0040] The rare earth element R" selected in this embodiment is Yb 2 o 3 、Gd 2 o 3 or Dy 2 o 3 , The selected raw material composition is shown in Table 1.

[0041] The first step: the La 2 o 3 、Sm 2 o 3 , R″ 2 o 3 , ZrO 2 Mix at a molar ratio of 0.4:0.5:0.1:2, and place the mixed powder in a ball mill;

[0042] Step 2: Add an appropriate amount of absolute ethanol and zirconia grinding media equal in mass to the mixed powder, mix and grind at a speed of 250r / min for 10 hours, and then dry the slurry at 80°C;

[0043] Step 3: Put the mixed powder in a zirconia crucible and compact it, heat at 1400°C for 6 hours and cool to room temperature, then crush the obtained material, sieve, and ball mill for 12 hours to obtain a powder with a particle size of less than 1 μm;

[0044] The fourth step: put the powder obtained in the third step into a zirconia cruci...

Embodiment 2

[0050] 0.3La 2 o 3 -0.5Sm 2 o 3 -0.2R″ 2 o 3 -2ZrO 2 Preparation of Ceramic Material Powder

[0051] The difference between this embodiment and Embodiment 1 is that La 2 o 3 、Sm 2 o 3 , R″ 2 o 3 , ZrO 2 The proportioning ratio is 0.3:0.5:0.2:2. Other steps are the same as Embodiment 1.

Embodiment 3

[0053] 0.25La 2 o 3 -0.5Sm 2 o 3 -0.25R″ 2 o 3 -2ZrO 2 Preparation of Ceramic Material Powder

[0054] The difference between this embodiment and Embodiment 1 is that La 2 o 3 、Sm 2 o 3 , R″ 2 o 3 , ZrO 2 The proportioning ratio is 0.25:0.5:0.2:25. Other steps are the same as Embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a pyrochlore structural rare-earth zirconate material system capable of being used for a heat barrier coating. The chemical composition of the material is (0.5-x)R'2O3-0.5Sm2O3-xR''2O3-2ZrO2, wherein x is more than 0 and less than or equal to 0.25; the R' is rare-earth elements or composition thereof, the ion radius of which is greater than that of Sm; and R'' is rare-earth elements or composition thereof, the ion radius of which is smaller than that of Sm. The material provided by the invention has low thermal conductivity, high thermal stability and high-temperature sintering resistance; the thermal expansion performance of the material is stable compared with a single pyrochlore structural material; and the material is favorable for reducing thermal stress generated by mismatching of thermal expansion coefficients in the thermal cycle process, and can prolong the thermal cycle life of the coating. Because of good high-temperature phase stability, the pyrochlore structural rare-earth zirconate material can be used for designing and preparing a novel high-temperature heat barrier coating material, the use temperature of which is below 1,550 DEG C.

Description

technical field [0001] The invention relates to a high-temperature thermal barrier coating material and its preparation method and application, in particular to a pyrochlore structure rare earth zirconate material and its preparation method and application. Background technique [0002] Thermal barrier coating refers to a ceramic coating deposited on the surface of metal parts with good heat insulation effect. This coating can reduce the working temperature of the substrate, protect the metal substrate from high-temperature gas erosion, and improve its high-temperature working life. Thermal barrier coatings are mainly used for thermal protection of hot end components. Thermal barrier coating materials need to have low thermal conductivity, high melting point, high chemical stability, thermal expansion coefficient matching the metal substrate, and good anti-sintering performance. [0003] The widely used thermal barrier coating materials are mainly yttria-stabilized zirconia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/48C04B35/50C04B35/622C23C4/12C23C4/10C23C4/11C23C4/134
Inventor 于建华陶顺衍赵华玉周霞明丁传贤
Owner SHANGHAI INST OF CERAMIC CHEM & TECH CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com