Superfine fiber leather and preparation method thereof

A technology of superfine fiber leather and additives, which is applied in the direction of chemical instruments and methods, textiles and papermaking, synthetic resin layered products, etc. It can solve the problems of poor moisture permeability and difficulty in simultaneously improving moisture permeability and wear resistance. Achieve the effect of improving wearing life and improving comfort

Inactive Publication Date: 2011-06-22
HUAFON MICROFIBER SHANGHAI
View PDF2 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The technical problem to be solved by the present invention is to overcome the defects that the moisture permeability of polyurethane synthetic leather in the prior art is much worse than that of natural leather, and it is difficult to achieve simultaneous improvement of moisture permeability and wear resistance, and to provide a high moisture permeability, Superfine fiber leather with wear resistance comparable to prior art and manufacturing method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Superfine fiber leather and preparation method thereof
  • Superfine fiber leather and preparation method thereof
  • Superfine fiber leather and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] The formula of dry slurry is:

[0045] Surface layer: 60 parts of polyurethane resin (TQS-1), 40 parts of polyurethane resin (TQS-5), 30 parts of DMF, 30 parts of MEK, 5 parts of colorant, 3 parts of anti-friction additive 9206-F, hydrophilic additive DS -32991.5 copies.

[0046] Middle layer: 50 parts of polyurethane resin (TQS-1), 50 parts of polyurethane resin (TQS-5), 20 parts of DMF, 30 parts of MEK, 5 parts of colorant, 3 parts of anti-friction additive 9206-F, hydrophilic additive DS- 32991.5 copies.

[0047] Adhesive layer: 100 parts of polyurethane resin (JF-A-5025), 80 parts of water-absorbing resin (Yilicheng 2009X), 10 parts of MEK, 1 part of anti-friction additive 9206-F, 1 part of hydrophilic additive DS-3299.

[0048] Microfiber leather preparation method:

[0049] (1) Preparation of dyed base fabric: Nylon 6 (PA6) and low-density polyethylene (LDPE) are blended and spun to make a non-woven fabric. After ironing, impregnate polyurethane resin (PU), and...

Embodiment 2

[0052] The formula of dry slurry is:

[0053] Surface layer: 60 parts of polyurethane resin (TQS-1), 40 parts of polyurethane resin (TQS-5), 30 parts of DMF, 30 parts of MEK, 5 parts of colorant, 6 parts of anti-friction additive 9206-F, hydrophilic additive DS -32991.5 copies.

[0054] Middle layer: 50 parts of polyurethane resin (TQS-1), 50 parts of polyurethane resin (TQS-5), 20 parts of DMF, 30 parts of MEK, 5 parts of colorant, 6 parts of anti-friction additive 9206-F, hydrophilic additive DS- 32991.5 copies.

[0055] Adhesive layer: 100 parts of polyurethane resin (JF-A-5025), 80 parts of water-absorbing resin (Yilicheng 2009X), 10 parts of MEK, 6 parts of anti-friction additive 9206-F, 1 part of hydrophilic additive DS-3299.

[0056] Microfiber leather preparation method:

[0057] (1) with embodiment 1 step (1);

[0058] (2) Dry veneer: apply a layer of layer slurry on the release paper, dry it in an oven, then apply a layer of middle layer slurry, dry it in an oven...

Embodiment 3

[0060] The formula of dry slurry is:

[0061] Surface layer: 60 parts of polyurethane resin (TQS-1), 40 parts of polyurethane resin (TQS-5), 30 parts of DMF, 30 parts of MEK, 5 parts of colorant, 3 parts of anti-friction additive 9206-F, hydrophilic additive DS -32995 copies.

[0062] Middle layer: 50 parts of polyurethane resin (TQS-1), 50 parts of polyurethane resin (TQS-5), 20 parts of DMF, 30 parts of MEK, 5 parts of colorant, 3 parts of anti-friction additive 9206-F, hydrophilic additive DS- 32995 copies.

[0063] Adhesive layer: 100 parts of polyurethane resin (JF-A-5025), 80 parts of water-absorbing resin (Yilicheng 2009X), 10 parts of MEK, 1 part of anti-friction additive 9206-F, 5 parts of hydrophilic additive DS-32999.

[0064] Microfiber leather preparation method:

[0065] (1) with embodiment 1 step (1);

[0066] (2) Dry veneer: apply a layer of layer slurry on the release paper, dry it in an oven, then apply a layer of middle layer slurry, dry it in an oven, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of superfine fiber leather, which comprises the steps of: coating a surface layer, a middle layer and an adhesive layer on a piece of release paper; laminating the release paper with dyed suede leather; drying; and removing the release paper to obtain the superfine fiber leather, wherein a sizing agent of the surface layer and the middle layer contains 100 parts of polyurethane resin, 10 to 60 parts of polar solvent, 1 to 6 parts of friction resistant additive and 0.5 to 5 parts of hydrophilic additive; a sizing agent of the adhesive layer contains 100 parts of polyurethane resin, 10 to 60 parts of polar solvent, 1 to 6 parts of friction resistant additive, 0.5 to 5 parts of hydrophilic additive and 70 to 90 parts of absorbent resin; a fluorine modified polyethylene wax substance is adopted as the friction resistant additive; and a hydrophilic organic silicon substance is adopted as the hydrophilic additive. The invention also discloses superfine fiber leather which has the moisture permeability higher than or equal to 850 grams per square meter for every 24 hours, which is higher than that of the natural leather. The preparation method disclosed by the invention can also improve the wear resistant time which is higher than 10000 times in the preferable embodiment of the invention.

Description

technical field [0001] The invention relates to the field of artificial leather, in particular to a superfine fiber leather and a preparation method thereof. Background technique [0002] Beam-shaped microfiber PU synthetic leather, known as the third-generation synthetic leather in the industry, is gradually replacing genuine leather with its excellent physical and chemical properties, and is widely used in gloves, footwear, luggage, furniture, ball games, and automotive interiors. Jewelry, clothing and other fields. In recent years, with the improvement of people's living standards, people have higher and higher requirements for the quality of clothing. In addition to requiring clothing to have excellent color fastness, more consumers have put forward requirements for clothing comfort, which is bound to increase Become the future development direction of high-end clothing. [0003] Polyurethane synthetic leather, because of its dense film on the surface, makes its moistu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/14B32B27/12
Inventor 于晓成孙向浩刘勇胜胡忠杰贺璇刘立强刘国
Owner HUAFON MICROFIBER SHANGHAI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap