Aluminium alloy paint stripper and preparation method thereof

A paint stripper, aluminum alloy technology, applied in the direction of chemical paint/ink remover, coating, etc., can solve the problems of aluminum alloy and light metal corrosion, few types of removed coatings, poor construction safety, etc., to achieve low toxicity , The effect of fast paint stripping and high safety construction

Active Publication Date: 2013-04-24
西安经建油漆有限责任公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the preparation method and especially the problem of the composition of the widely used paint removers, there are generally few types of removed coatings, long paint removal time, poor construction safety, strong odor, and serious damage to metals, especially aluminum alloys and light metals. Corrosion and other issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Take dichloromethane (CH 2 CL 2 ) 73.5kg, turpentine 3kg, titanium dioxide (TiO 2 ) 0.1 kg, phenol (C 6 H 6 O) 15 kg, defoamer NXZ 0.2 kg, octylphenol ethoxylate 0.6 kg, hydroxyethyl cellulose 0.6 kg, corrosion inhibitor A-40 1.0 kg, water 1.2 kg, paraffin 0.5 kg, petrolatum 1.9 kg , corrosion inhibitor AMP-95 0.08 kg, deodorant 1 kg; add hydroxyethyl cellulose and titanium dioxide into the kettle, add 50% of dichloromethane, stir for 3-5 minutes, add phenol, defoamer and Octylphenol polyoxyethylene ether; add corrosion inhibitor A-40 and corrosion inhibitor AMP-95 under stirring; add turpentine and the remaining half of the dichloromethane under stirring; add and melt at 400-600 rpm of vaseline and paraffin, stirring for 5-10 minutes; adding deodorant, stirring evenly to obtain the invention product.

Embodiment 2

[0051] Take 70 kg of methylene chloride, 1 kg of turpentine, 0.1 kg of titanium dioxide, 15 kg of phenol, 0.1 kg of defoamer NXZ, 0.2 kg of octylphenol polyoxyethylene ether, 0.6 kg of hydroxyethyl cellulose, and corrosion inhibitor A-40 0.8 kg, water 1 kg, paraffin 0.3 kg, petrolatum 1 kg, corrosion inhibitor AMP-95 0.01 kg, deodorant 1 kg;

[0052] The preparation method is the same as in Example 1.

Embodiment 3

[0054] Take 75 kg of methylene chloride, 5 kg of turpentine, 0.8 kg of titanium dioxide, 20 kg of phenol, 0.3 kg of defoamer NXZ, 0.9 kg of octylphenol polyoxyethylene ether, 1.2 kg of hydroxyethyl cellulose, and corrosion inhibitor A- 40 3 kg, water 1.4 kg, paraffin 0.8 kg, petrolatum 2 kg, corrosion inhibitor AMP-95 0.1 kg, deodorant 2 kg;

[0055] The preparation method is the same as in Example 1.

[0056] The deodorant described in the above embodiment is a physical deodorant, which is a plant extract (such as natural aromatic oils, spices and other substances), purchased from Shaanxi Taihe Chemical Industry, address: No. 7, Zhuhong Road, Weiyang District, Xi'an City 1- 2405; the corrosion inhibitor A-40 is an aqueous solution of a metal salt, which is purchased from Shenzhen Haichuan Technology Industry and Trade Co., Ltd., address: Building C, D, Building F3-8, Tianan Digital City, Chegongmiao, Futian District, Shenzhen City, Guangdong Province 7th and 8th floors; the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a paint stripper used for removing metal, especially removing old paint films on the surface of aluminum alloy, and also relates to a preparation method of the paint stripper. The paint stripper is characterized by consisting of the following components according to parts by weight: 70-75 parts of dichloromethane, 1-5 parts of turpentine, 0.1-0.8 part of titanium dioxide,15-20 parts of phenol, 0.1-0.3 part of defoamer NXZ, 0.2-0.9 part of Octylphenols polyoxyethylene ether, 0.6-1.2 part of hydroxyethyl celluloses, 0.8-3parts of corrosion inhibitor A-40, 1-1.4 parts of water, 0.3-0.8 part of paraffin, 1-2 parts of Vaseline, 0.01-0.1 part of corrosion inhibitor AMP-95 and 1-2 parts of deodorant. The paint stripper is applicable to depriving metal of various old paint films, characterized by quick paint stripping speed, high construction safety, small toxicity, mild gas and the like. Especially, the product has no corrosion to aluminum alloy.

Description

technical field [0001] The invention relates to a paint remover for removing old paint films on the surface of metal—especially aluminum alloy metal, and also relates to a preparation method of the paint remover. Background technique [0002] The paint coating on the metal surface is often peeled off with a paint stripper because it is old or unqualified. Due to the preparation method and especially the problem of the composition of the widely used paint removers, there are generally few types of removed coatings, long paint removal time, poor construction safety, strong odor, and serious damage to metals, especially aluminum alloys and light metals. Corrosion etc. Contents of the invention [0003] In order to solve the above-mentioned technical problems, the object of the present invention is to provide a kind of aluminum alloy paint remover and its preparation method, the paint remover of the present invention is a kind of fast paint removal, high efficiency, wide ran...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D9/00
Inventor 杜宏印王萍王文月
Owner 西安经建油漆有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com