Method for preparing aventurine fluoride-free opal glass
A technology of opaque glass and Venus glass, applied in the field of preparation of Venus fluorine-free opaque glass, can solve the problems of chronic poisoning, environmental pollution, volatilization of fluoride, etc., and achieve the effect of soft color and luster
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0018] Example 1:
[0019] A preparation method of Venus fluorine-free opal glass, which comprises the following steps:
[0020] 1) Selection of raw materials: The basic composition range of the Venus fluorine-free opal glass used in the present invention is shown in Table 1:
[0021] Table 1 (parts by mass)
[0022]
[0023] Calculate the ingredients according to the content of the components in Table 1 to obtain the ingredients list. Use mineral raw materials and chemical raw materials to introduce various oxides, and then weigh and mix them to obtain glass batches. See Table 2 for the ingredient list of glass raw materials.
[0024] Table 2 Glass raw material ingredients list
[0025] Raw materials
[0026] 2) Put the glass batch in step 1) into a horseshoe flame glass melting furnace for melting, the melting temperature range is 1500-1530°C, the heating rate is 10-20°C / min, and the holding time is 2-8 hours. At this temperature, the molten glass is clarified and homogenized; the...
Example Embodiment
[0031] Example 2:
[0032] A preparation method of Venus fluorine-free opal glass, which comprises the following steps:
[0033] 1) Selection of raw materials: The basic composition range of Venus fluorine-free opal glass used in the present invention is shown in Table 3:
[0034] Table 3 (number of parts by mass)
[0035]
[0036]
[0037] Calculate the ingredients based on the content of the components in Table 3 to obtain the ingredient list. Use mineral raw materials and chemical raw materials to introduce various oxides, and then weigh and mix them to obtain glass batches. See Table 4 for the ingredient list of glass raw materials.
[0038] Table 4 Glass raw material ingredients list
[0039] Raw materials
[0040] 2) Put the glass batch in step 1) into a horseshoe flame glass melting furnace for melting, the melting temperature range is 1500-1530°C, the heating rate is 10-20°C / min, and the holding time is 2-8 hours. At this temperature, the molten glass is clarified and homoge...
Example Embodiment
[0045] Example 3:
[0046] A preparation method of Venus fluorine-free opal glass, which comprises the following steps:
[0047] 1) Selection of raw materials: The basic composition range of Venus fluorine-free opal glass used in the present invention is shown in Table 5:
[0048] Table 5 (parts by mass)
[0049]
[0050] Calculate the ingredients based on the content of the components in Table 5 to obtain the ingredient list. Use mineral raw materials and chemical raw materials to introduce various oxides, weigh and mix them to obtain glass batches. See Table 6 for the ingredient list of glass raw materials.
[0051] Table 6 Ingredients list of glass raw materials
[0052] Raw materials
[0053] 2) Put the glass batch in step 1) into a horseshoe flame glass melting furnace for melting, the melting temperature range is 1500-1530°C, the heating rate is 10-20°C / min, and the holding time is 2-8 hours. At this temperature, the molten glass is clarified and homogenized; the qualified mol...
PUM
Property | Measurement | Unit |
---|---|---|
Strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap