A kind of high adhesion airtight type TPU coated fabric and preparation method thereof
A fabric-coated, high-adhesion technology, applied in chemical instruments and methods, lamination, layered products, etc., can solve problems such as low tensile strength, inability to meet the processing requirements of new inflatable products, and poor flex resistance. Achieve stable performance, unique performance advantages, and simple process technology.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0008] 210D high-strength silk nylon Oxford cloth is impregnated with solvent-based polyurethane adhesive, and the amount of impregnation is 20g / m 2 , the production line speed is 20m / min, the drying temperature is 120-130-130°C, and it is cooled after drying. Then it is transported to the extrusion casting production line for TPU casting coating. The casting coating process conditions are: infrared pre-baking temperature is 120 ° C, extrusion melt temperature is 190 ° C, cooling roll temperature is 50 ° C, production line speed is 25m / min, extrusion cast coating weight 100g / m 2 , after extrusion coating, it is cooled and shaped to form a total weight of about 220g / m 2 High adhesion TPU coated fabric.
[0009] The adhesive is a one-liquid-and-a-half type with a solid content of 15%, the ratio of the solvent is DMF:TOL:MEK=1:3:3, the ratio of the curing agent to the main glue is 1:20, the accelerator and the curing The ratio of the agent is 1:10.
[0010] The TPU is a hydro...
Embodiment 2
[0013] 420D high-strength silk nylon Oxford cloth is impregnated with solvent-based polyurethane adhesive, and the amount of impregnation is 30g / m 2 , the production line speed is 20m / min, the drying temperature is 120-130°C, and cool after drying. Then it is transported to the extrusion casting production line for TPU casting coating. The casting coating process conditions are: infrared pre-baking temperature is 120 ° C, extrusion melt temperature is 190 ° C, cooling roll temperature is 50 ° C, production line speed is 25m / min, extrusion cast coating weight is 300g / m 2 , after extrusion coating, it is cooled and shaped to form a total weight of about 460g / m 2 High adhesion TPU coated fabric. When double-sided TPU-coated fabric is required, coat the fabric side of the single-sided TPU-coated fabric made above with 300g / m 2 TPU, forming a total weight of about 700g / m 2 High adhesion double-sided TPU coated fabric
[0014] The adhesive is a one-liquid-and-a-half type with a...
PUM
Property | Measurement | Unit |
---|---|---|
Hardness | aaaaa | aaaaa |
Hardness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap