Lead-free low-temperature alloy for making fuse core of thermal fuse and preparation method thereof

A thermal fuse and low-temperature alloy technology, applied in the field of alloys, can solve problems such as endangering human health and environmental pollution, and achieve the effects of narrow melting point range, uniform composition, and low cost

Inactive Publication Date: 2011-12-28
TIANJIN BAIRUIJIE WELDING MATERIAL
View PDF11 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Fusible core is the heart of the thermal fuse and the technical core of the thermal fuse production process. Traditional thermal fuses are mostly tin-lead alloys. Lead, a substance harmful to the environment, is harmful to human health during production and use. The environment is very polluted

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The present invention is further described below in conjunction with specific embodiment; It should be emphasized that: for those of ordinary skill in the art, can improve or change according to the above description, and all these improvements and changes should belong to the appended claims of the present invention protected range.

[0017] A lead-free low-temperature alloy used to make a fuse core of a thermal fuse, the specific composition of which is Sn 61 Bi 35 Zn 4 , see the following table for specific ingredients and weight ratio:

[0018] chemical composition%

sn

Bi

Zn

sn 61 Bi 35 Zn 4

59.5-62.5

34-36

3.5-4.5

[0019] A method for preparing a lead-free low-temperature alloy for making a fuse core of a thermal fuse, the steps of which are:

[0020] Put metal tin into a stainless steel crucible according to the weight ratio, heat it on the electric furnace until the tin melts, and then add metal zin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a lead-free low-temperature alloy used for making a fuse core of a thermal fuse. Its raw material composition and its weight percentage range are respectively: Bi: 34%-36%; Zn: 3.5%-4.5%; Sn: balance The preparation method has the following steps: put metal tin into a stainless steel crucible, heat it in an electric furnace, after the tin is melted, add metal zinc at 250-280°C, and after melting, then add metal bismuth to melt After cleaning, conventional degassing and slag removal are performed by adding a degassing agent, and cast into a low-temperature alloy rod of the required size. The lead-free low-temperature alloy containing Sn, Bi and Zn involved in the present invention is used for making the fuse core of the thermal fuse, and the melting point is 132±2° C. It has low characteristics and is a lead-free environmental protection material, which itself has good social and economic benefits.

Description

technical field [0001] The invention belongs to the field of alloys, and relates to a lead-free low-temperature alloy, in particular to a lead-free low-temperature alloy for making a fuse core of a thermal fuse and a preparation method thereof. Background technique [0002] Fusible core is the heart of the thermal fuse and the technical core of the thermal fuse production process. Traditional thermal fuses are mostly tin-lead alloys. Lead, a substance harmful to the environment, is harmful to human health during production and use. The environment is extremely polluted. [0003] Low-temperature alloys can be used for the protection of electronic circuits in the electronics industry, and are mostly used to make fuse cores for thermal fuses. At present, the manufacturers of low-temperature alloys leading the world's advanced technology are Alpha in the United States and Senju in Japan. [0004] Through searching, a published patent document related to this patent application...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C13/02C22C1/02
Inventor 黄永利赵世有李洪福付宏宇
Owner TIANJIN BAIRUIJIE WELDING MATERIAL
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com