Austenite stainless steel thin strip for electronic product shell

A technology of austenitic stainless steel and electronic products, which is applied in the field of stainless steel alloys, can solve the problems of not being able to meet the needs of use, achieve good polishing performance, and improve the overall performance

Inactive Publication Date: 2012-02-15
YONGXIN PRECISION MATERIAL WUXI
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it has been found through practice that some indicators cannot reach the claimed value, and even if it can reach its value, it still cannot meet the needs of some high-end products with high requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A thin strip of austenitic stainless steel used for housings of electronic products, the austenitic stainless steel contains the following components by weight percentage: C 0.06%, Cr 16.5%, Ni 11.0%, Mn 1.8%, Si 0.3%, Mo 0.8%, Nb 0.3%, B 0.005%, Al 0.010%, N 0.20%, P≤0.03%, S≤0.005%, O≤0.0050%; the balance is Fe and unavoidable impurities; and the Ni- The range of bal is 1.5, and the Ni-bal is calculated by the following formula: Ni-bal%=Ni%+30(C%+N%+B%)+0.5Mn%-1.5(Cr%+1.5Si%+Mo %+0.5Nb%)+8.5%.

Embodiment 2

[0022] A thin strip of austenitic stainless steel used for housings of electronic products, the austenitic stainless steel contains the following components by weight percentage: C 0.08%, Cr 14.5%, Ni 13.0%, Mn 1.4%, Si 1.0%, Mo 0.5%, Nb 0.6%, B 0.001%, Al 0.060%, N 0.05%, P≤0.03%, S≤0.005%, O≤0.0050%; the balance is Fe and unavoidable impurities; and the Ni- The range of bal% is 0.93, and the described Ni-bal% is calculated by the following formula: Ni-bal%=Ni%+30(C%+N%+B%)+0.5Mn%-1.5(Cr%+1.5Si% +Mo%+0.5Nb%)+8.5%.

Embodiment 3

[0024] A thin strip of austenitic stainless steel for electronic product casings, the austenitic stainless steel contains the following components by weight percentage: C 0.07%, Cr 15.5%, Ni 12%, Mn 1.6%, Si 0.7%, Mo 0.6%, Nb 0.5%, B 0.004%, Al 0.04%, N 0.12%, P≤0.03%, S≤0.005%, O≤0.0050%; the balance is Fe and unavoidable impurities; and the Ni- The range of bal% is 1.0, and the described Ni-bal% is calculated by the following formula: Ni-bal%=Ni%+30(C%+N%+B%)+0.5Mn%-1.5(Cr%+1.5Si% +Mo%+0.5Nb%)+8.5%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an austenite stainless steel thin strip for an electronic product shell. The austenite stainless steel comprises the following components by weight percent: 0.06-0.08% of C, 14.5-16.5% of Cr, 11.0-13.0% of Ni, 1.4-1.8% of Mn, 0.3-1.0% of Si, 0.5-0.8% of Mo, 0.3-0.6% of Nb, 0.001-0.005% of B, 0.010-0.060% of Al, 0.05-0.20% of N, no more than 0.03% of P, no more than 0.005% of S, no more than 0.0050% of O and the balance of Fe and inevitable impurities. The Ni-bal% range of the stainless steel is 0.5-1.5 and Ni-bal% is calculated according to the following formula: Ni-bal% = Ni% + 30(C% + N% + B%) + 0.5Mn%-1.5(Cr% + 1.5Si% + Mo% + 0.5Nb%) + 8.5%.

Description

technical field [0001] The invention relates to the field of stainless steel alloys, in particular to an austenitic stainless steel thin strip for electronic product casings. Background technique [0002] Along with the raising of people's living standard, electronic devices such as mobile phone, PDA (personal digital assistant, personal digital assistant), MP3 and palmtop computer enter people's life and work in a large number, bring convenience and fun to people. At present, people not only require powerful functions for the above-mentioned various electronic devices, but also hope that they have a beautiful appearance and a good surface texture. Therefore, the processing precision and roughness of the shell surface of the electronic device are highly required. [0003] At present, 304 austenitic stainless steel is commonly used in the manufacture of housings of electronic devices, especially cold-rolled sheets, because cold-rolled sheets have relatively good surface quali...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/58C22C38/54
Inventor 濮晓芳
Owner YONGXIN PRECISION MATERIAL WUXI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap