Novel over-speed bright quenching oil composition

A technology of quenching oil and composition, which is applied in the direction of quenching agent, heat treatment equipment, manufacturing tools, etc. It can solve the problems of affecting the quality of heat treatment of parts, low moisture content, accidents, etc., and achieve excellent bright performance, fast cooling speed, and easy The effect obtained

Inactive Publication Date: 2013-07-03
TIANJIN ZHONGCHUAN LUBRICANT
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

5. The water content is low. Excessive water in the oil will affect the heat treatment quality of the parts, causing soft spots, quenching cracks or deformation of the parts, and may also cause oil splashes and accidents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel over-speed bright quenching oil composition
  • Novel over-speed bright quenching oil composition
  • Novel over-speed bright quenching oil composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A new ultra-fast bright quenching oil composition, the components are shown in the following table:

[0021] name Mass % 150SN base oil 100 polyisobutylene 3 Formamide 0.3 imidazoline oleate 1.0 methyl terpene resin 1.0 T501 antioxidant 0.5

[0022] Siben 80 0.3

[0023] Preparation

[0024] 1. Put formamide, Siben 80, imidazoline oleate and polyisobutylene into a mixing tank.

[0025] 2. Add methyl terpene resin and T501 antioxidant to 5 parts of 150SN base oil, heat and stir until completely dissolved, then pour into the mixing tank.

[0026] 3. Put the remaining 95 parts of 50SN base oil into the stirring tank, and stir thoroughly. If the room temperature is too low, heat it properly.

[0027] The excellent characteristics of the novel ultra-fast bright quenching oil composition prepared by the present invention are as follows:

[0028] Ultra-speed bright quenching oil is suitable f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a novel over-speed bright quenching oil composition, which contains mineral lubricating oil, a cooling accelerant, anti-oxidation additives and brightening additives. The quenching oil has good cooling properties, heating stability, oxidation stability and brightness. The preparation process of the quenching oil is simple, and the raw materials are domestic and therefore easy to get with low price. The quenching oil is suitable for the quenching of spring steel, bearing steel and mold steel and large-sized steel, particularly for the quenching of small-sized and medium-sized carbon tool steel.

Description

technical field [0001] The invention relates to a quenching oil for metal heat treatment, in particular to a novel super-speed bright quenching oil composition and a preparation method thereof. Background technique [0002] Quenching oil is a process oil used as a quenching medium. Quenching oil must have the following characteristics: Good cooling performance 1. Cooling performance is an important performance of quenching medium. Its quality directly affects the quality of quenched parts. Good cooling performance can ensure that the quenched parts have a certain hardness and pass 2. High flash point and ignition point. When quenching, the temperature of the oil will rise instantaneously. If the flash point and ignition point of the oil are low, ignition may occur. Therefore, the quenching oil should have a higher flash point and ignition point. Generally, the flash point should be 60-80°C higher than the temperature of the used oil; 3. Good thermal oxidation stability. Qu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21D1/58
Inventor 孙兰凤
Owner TIANJIN ZHONGCHUAN LUBRICANT