A cooling intensity, semi-continuous technology, applied in the crystallizer field, can solve problems such as uneven cooling of ingots, surface cracks, etc., to achieve the effect of increasing turbulence, reducing pressure, and improving metallurgical quality

Active Publication Date: 2012-07-18
CHINA NON-FERROUS METALS PROCESSING TECH CO LTD
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in this cooling mode, when the cooling water flow rate increases to a certain level, due to the excessive water pressure, the cooling water flow with a high incident angle hits the surface of the ingot and spreads out, which w

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Crystallizer with changeable cooling intensity in semicontinuous casting of aluminum alloy
  • Crystallizer with changeable cooling intensity in semicontinuous casting of aluminum alloy
  • Crystallizer with changeable cooling intensity in semicontinuous casting of aluminum alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] Such as figure 1 , figure 2 , image 3 , Figure 4 , Figure 5 As shown, a crystallizer with variable cooling intensity for aluminum alloy semi-continuous casting, the crystallizer 1 is provided with an upper water chamber 6 and a lower water chamber 5, the bottom of the upper water chamber 6 is provided with a decompression chamber 10, the top of the lower water chamber 5 and The bottom is provided with a decompression chamber 10, the bottom of the upper water chamber 6 is separated from the decompression chamber 10 by installing a water diversion plate 3, the top and bottom of the lower water chamber 5 are separated from the decompression chamber 10 by installing a water diversion plate 3, and the upper water chamber 6 The decompression chamber 10 of the decompression chamber 10 is provided with a third group of cooling water holes 8, the decompression chamber 10 at the top of the lower water chamber 5 is provided with a first group of cooling water holes 7, and t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a crystallizer with changeable cooling intensity in semicontinuous casting of aluminum alloy. The crystallizer is provided with an upper water cavity and a lower water cavity; a decompression cavity is arranged at the bottom of the upper water cavity; decompression cavities are arranged on the top and the bottom of the lower water cavity; a third group of cooling water holes are arranged on the decompression cavity of the upper water cavity; a first group of cooling water holes are arranged on the decompression cavity at the top of the lower water cavity; a second group of cooling water holes are arranged on the decompression cavity at the bottom of the lower water cavity; the first group of cooling water holes and the second group of cooling water holes are in a same vertical plane and are in intersection with the third group of cooling water holes; the angles of the first group of cooling water holes and the second group of cooling water holes are bigger than 40 degrees; and the angles of the third group of cooling water holes are less than 40 degrees. According to the invention, two groups of cooling water flow with high incident angles are adopted, and the pressure of cooling water flow with the high incident angle can be greatly reduced under the same quantity of cooling water flow, so that the water returning phenomenon caused by excessive pressure and surface cracks of a cast ingot caused by the water returning phenomenon can be effectively avoided.

Description

technical field [0001] The invention relates to a crystallizer with variable cooling intensity for aluminum alloy semi-continuous casting, and belongs to the technical field of aluminum alloy semi-continuous casting. Background technique [0002] Direct cooling semi-continuous casting is currently the main way for aluminum alloy enterprises to produce aluminum alloy round ingots and flat ingots. The liquid aluminum melt is poured into the space surrounded by the crystallizer and the dummy head. The aluminum melt is cooled by the mold and the dummy head and solidified along its boundaries. When the aluminum melt reaches a certain height in the crystallizer and the solidified shell has sufficient strength to support the aluminum melt, the dummy head will move downward at a given casting speed. The solidified ingot will descend together with the dummy head. When the ingot is pulled out of the crystallizer, the cooling water in the crystallizer is directly sprayed onto the sur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22D11/055
Inventor 刘金炎长海博文郭世杰薛冠霞王乐酉
Owner CHINA NON-FERROUS METALS PROCESSING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap