Bamboo-fiber electric-heating mosquito-repellent incense piece and preparation method thereof

A technology of bamboo fiber and mosquito-repellent coils, which is applied to botany equipment and methods, chemicals for biological control, insecticides, etc., can solve the problems of restricting large-scale use, unfavorable ecological protection, and cutting down large trees, and achieves Light weight, beneficial to ecological protection, the effect of drawing a wide range of materials

Inactive Publication Date: 2012-08-01
HANGZHOU JIADEHAO COMMODITY
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The large-scale use of cotton pulp in the field of electric heating mosquito coils is limited due to its high price and low output
Wood

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The paper raw sheet of a bamboo fiber electric heating mosquito-repellent incense sheet in this embodiment includes the following components by weight percentage: 80% bamboo fiber and 20% wood fiber.

[0027] The bamboo fiber electric heating mosquito coil is prepared by the following steps:

[0028] 1) Bamboo fiber raw materials are pulped and refined to make bamboo pulp, wherein the pulping concentration is 2.0%, the refining concentration is 2.0%, and the beating degree after refining is 35oSR.

[0029] 2) The wood fiber raw material is pulped and refined to make wood pulp, wherein the pulping concentration is 1.5%, the refining concentration is 1.5%, and the beating degree after refining is 30oSR.

[0030] 3) According to the ratio of 80% bamboo fiber and 20% wood fiber, mix bamboo pulp with a knocking degree of 35oSR and wood pulp with a knocking degree of 30oSR, add water to dilute to a concentration of 0.9%, stir evenly, and then make it by copying Tablet base. ...

Embodiment 2

[0035] The paper raw sheet of a bamboo fiber electric heating mosquito-repellent incense sheet in this embodiment comprises the following components by weight percentage: 70% of bamboo fiber and 30% of wood fiber.

[0036] The bamboo fiber electric heating mosquito coil is prepared by the following steps:

[0037] 1) Bamboo fiber raw materials are pulped and refined to make bamboo pulp, wherein the pulping concentration is 2.5%, the refining concentration is 2.5%, and the beating degree after refining is 30oSR.

[0038] 2) The wood fiber raw material is pulped and refined to make wood pulp, wherein the pulping concentration is 2.5%, the refining concentration is 2.5%, and the beating degree after refining is 45oSR.

[0039] 3) According to the ratio of 70% bamboo fiber and 30% wood fiber, mix bamboo pulp with 30oSR and 45oSR wood pulp, dilute with water to 1.0% concentration and stir evenly, and then make it by copying Tablet base.

[0040] 4) After the tablet substrate is d...

Embodiment 3

[0044] The paper raw sheet of a bamboo fiber electric heating mosquito-repellent incense sheet in this embodiment comprises the following components by weight percentage: 60% bamboo fiber and 40% wood fiber.

[0045] The bamboo fiber electric heating mosquito coil is prepared by the following steps:

[0046] 1) Bamboo fiber raw materials are pulped and refined to make bamboo pulp, wherein the pulping concentration is 1.5%, the refining concentration is 1.5%, and the beating degree after refining is 40oSR.

[0047] 2) The wood fiber raw material is pulped and refined to make wood pulp, wherein the pulping concentration is 2.0%, the refining concentration is 2.0%, and the beating degree after refining is 30oSR.

[0048] 3) According to the ratio of 60% bamboo fiber and 40% wood fiber, mix bamboo pulp with 40oSR degree of percussion and wood pulp with 30oSR degree of percussion, dilute with water to 1.2% concentration and stir evenly, and then make it by copying Tablet base.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a bamboo-fiber electric-heating mosquito-repellent incense piece and a preparation method thereof. A paper raw piece of the bamboo-fiber electric-heating mosquito-repellent incense piece comprises the following components, by weight, 30%-90% of bamboo fiber, 0-70% of wood fiber and 0-70% of cotton fiber. After heated, the bamboo-fiber electric-heating mosquito-repellent incense piece has faint scent of bamboos, can purify the air and is light and thin. The preparation method of the bamboo-fiber electric-heating mosquito-repellent incense piece sequentially comprises the following steps: making a bamboo fiber raw material into bamboo pulp after pulping and jordaning; making a wood fiber raw material into wood pulp after pulping and jordaning; making a cotton fiber raw material into cotton pulp after pulping and jordaning; mixing the bamboo pulp, the wood pulp and the cotton pulp, determining proportions of the components according to any proportion of the right claim, adding water to dilute the mixture, evenly mixing, and making a tablet base material after manufacturing paper with the pulp; making the paper raw piece after punching of the tablet base material; and spraying a mosquito-repellent agent on the paper raw piece. The preparation method reduces production cost and is simple in process.

Description

technical field [0001] The invention relates to an electric heating mosquito-repellent incense sheet and a preparation method thereof, in particular to a bamboo fiber electric heating mosquito-repellent incense sheet and a preparation method thereof. Background technique [0002] The electric heating mosquito coils sold on the market are mainly made of wood pulp and cotton pulp. The large-scale use of cotton pulp in the field of electric heating mosquito coils is limited due to its high price and low output. Wood pulp is made from wood raw materials, which need to cut down a large number of trees, which is not conducive to ecological protection. Therefore, there is an urgent need to find a new fiber raw material to replace cotton pulp and wood pulp, reduce the amount of cotton pulp and wood pulp, and ensure the effect of repelling (killing) mosquitoes while also being cheap, safe and environmentally friendly. Contents of the invention [0003] The invention provides a sa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A01N25/34A01N25/18A01N25/08A01P17/00A01P7/04
Inventor 邵伟权
Owner HANGZHOU JIADEHAO COMMODITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap