Manufacturing method of potassium hexatitanate whisker high-temperature thermal insulation material

A technology of potassium hexatitanate whisker and thermal insulation, which is applied in the field of manufacturing potassium hexatitanate whisker high-temperature thermal insulation materials, and can solve the problem of affecting the thermal insulation effect, easy powdering and warping of the surface, and harm to human health. and other problems, to achieve the effect of prolonged heat dissipation time, significant infrared reflectivity, and strong reflectivity

Active Publication Date: 2012-08-08
上海秀普复合材料有限公司
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The disadvantage of the above two building materials is that the surface is easy to pulverize and warp and deform under high temperature, which affects the heat preservation effect; at the same time, the production process has a certain degree of harm to human health.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of potassium hexatitanate whisker high-temperature thermal insulation material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] ①, Potassium hexatitanate whiskers and water were weighed and mixed in a weight ratio of 100:0.5, stirred thoroughly and evenly, and left to soak for 30 minutes to become the soaking raw material;

[0019] ② Weigh and mix the above impregnation raw materials and silica sol in a ratio of 100:45 by weight, and stir fully and evenly to become raw materials for billet making;

[0020] Or, after diluting the water and the coupling agent in a weight ratio of 25:1, then mixing with the above-mentioned impregnating raw materials in a weight ratio of 100:20, and fully and uniformly stirring, to become the billet-making raw material;

[0021] ③Put the raw materials mentioned above into a wooden or steel mold, and use a 100-ton friction press to press the mold blank. The mold blank can be demoulded when the volume density is 1.5g / cm3, and then the demoulded mold The blank is placed in a drying room at 80°C to dry and dehumidify, so that its moisture content is ≤13% and becomes a m...

Embodiment 2

[0026] ①. Potassium hexatitanate whiskers and water are weighed and mixed in a weight ratio of 100:10, stirred thoroughly and evenly, and left to soak for 1 minute to become the soaking raw material;

[0027] ②Weighing and mixing the above infiltrating raw materials and silica sol according to the ratio of 100:15 by weight, and fully and evenly stirring to become raw materials for billet making;

[0028] Or, after diluting the water and the coupling agent in a ratio of 5:1 by weight, they are then mixed with the above-mentioned impregnation raw materials in a ratio of 100:2 by weight, and fully and evenly stirred to become raw materials for billet making;

[0029] ③Put the above raw materials into the wooden or steel mold, and use a 400-ton vibrating press to press the mold blank. The bulk density of the mold blank is 1.8g / cm 3 It can be demoulded when the time is right, and then the demoulded mold base is placed in a drying room at 160°C to dry and dehumidify, so that its moi...

Embodiment 3

[0034] A method for manufacturing potassium hexatitanate whisker high-temperature thermal insulation material, the technological process is as follows:

[0035] ①, Potassium hexatitanate whiskers and water were weighed and mixed in a ratio of 100:5 by weight, stirred thoroughly and evenly, and left to soak for 15 minutes to become the soaking raw material;

[0036] ②Weighing and mixing the above infiltrating raw materials and silica sol in a ratio of 100:30 by weight, and fully and evenly stirring them to become billet-making raw materials;

[0037] Or, after diluting the water and the coupling agent in a ratio of 15:1 by weight, they are then mixed with the above-mentioned impregnation raw materials in a ratio of 100:10 by weight, and fully and evenly stirred to become raw materials for billet making;

[0038] ③Put the above blank-making raw materials into wooden or steel molds, and use a 250-ton hydraulic press to press the mold blanks. The bulk density of the mold blanks is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a manufacturing method of a potassium hexatitanate whisker high-temperature thermal insulation material, comprising the following steps of: mixing potassium hexatitanate whiskers with silica sol or a coupling agent, filling into a die, compacting into a moulded die blank, demoulding and drying, and placing into a high-temperature kiln for baking to obtain the finished product. The whole technological process is simple without pollution. According to the invention, specific excellent properties of the potassium hexatitanate whisker material such as high-temperature resistance, hydrochloric acid corrosion resistance, high mechanical strength, low coefficient of thermal conductivity and significant infrared reflectivity are well-maintained. The potassium hexatitanate whisker high-temperature thermal insulation material manufactured by the method is a thermal insulation material which has excellent quality as well as extensive applications.

Description

technical field [0001] The invention belongs to a method for manufacturing a new type of thermal insulation material by using potassium hexatitanate whiskers of inorganic salt whiskers Background technique [0002] There is a calcium silicate board, which is a hard thermal insulation material. The main components are silicon powder and calcium powder as the main base material, natural wood fiber as the reinforcement material, and other auxiliary materials. A building material produced by high pressure curing, which can be produced in various shapes through molds. [0003] There is also a kind of ceramic fiber cotton, which is made of high-purity alumina silica powder synthetic material, melted in a resistance furnace, blown or spun into fibers. It is a kind of soft material, which can be attached to the outside of the object to be insulated by mechanical bending to form an insulation layer. [0004] The disadvantages of the above two building materials are that the surface...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66
Inventor 赵力力许茂军赵力杰陆志国
Owner 上海秀普复合材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap