Ceramic crystal paint for metal surface and preparation method thereof

A metal surface and coating technology, applied in the direction of coating, etc., can solve the problems of suffocation and death, affecting the durability and stain resistance of fluorocarbon coatings, and achieve the effects of good durability, long construction period and excellent stain resistance

Active Publication Date: 2014-10-08
ZHUHAI FUTE TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, with the acceleration of industrialization in our country, there are more and more pollutants such as industrial waste gas and automobile exhaust in cities. These pollutants will significantly affect the durability and stain resistance of fluorocarbon coatings; Organic coatings release large amounts of fumes, which can easily lead to suffocation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic crystal paint for metal surface and preparation method thereof
  • Ceramic crystal paint for metal surface and preparation method thereof
  • Ceramic crystal paint for metal surface and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Aluminum alloy curtain wall light blue ceramic coating formula

[0037]

[0038]

[0039] The preparation method of light blue ceramic crystal coating for aluminum alloy curtain wall is as follows:

[0040] Step 1. In the batching tank, add the raw materials of the organic modified product, the wetting and dispersing agent and the ethylene glycol ether acetate in sequence according to the parts by weight, and mix evenly;

[0041] Step 2. Slowly add titanium dioxide (TS-6200), fumed silica and diamond blue into the batching tank according to parts by weight and disperse evenly, and then use a sand mill to grind to a fineness of ≤25 μm;

[0042] Step 3, add aluminum silicate sol and isopropanol paint in turn, mix well;

[0043] Finally, after degreasing and degreasing the aluminum plate, use 120-mesh corundum for sandblasting, then use high-pressure air to remove dust, mix the paint evenly and then spray it. The thickness of the paint film is controlled at 20-30μm....

Embodiment 2

[0049] Aluminum alloy curtain wall light blue ceramic coating formula

[0050]

[0051] The preparation method of light blue ceramic crystal coating for aluminum alloy curtain wall is as follows:

[0052] Step 1. In the batching tank, add the raw materials of the organic modified product, the wetting and dispersing agent and the ethylene glycol ether acetate in sequence according to the parts by weight, and mix evenly;

[0053] Step 2. Slowly add titanium dioxide (TS-6200), fumed silica and diamond blue into the batching tank according to parts by weight and disperse evenly, and then use a sand mill to grind to a fineness of ≤25 μm;

[0054] Step 3, add aluminum silicate sol and isopropanol paint in turn, mix well;

[0055] Finally, after degreasing and degreasing the aluminum plate, use 120-mesh corundum for sandblasting, then use high-pressure air to remove dust, mix the paint evenly and then spray it. The thickness of the paint film is controlled at 20-30μm.

[0056] T...

Embodiment 3

[0061] Aluminum alloy curtain wall light blue ceramic coating formula

[0062]

[0063] The preparation method of light blue ceramic crystal coating for aluminum alloy curtain wall is as follows:

[0064] Step 1. In the batching tank, add the raw materials of the organic modified product, the wetting and dispersing agent and the ethylene glycol ether acetate in sequence according to the parts by weight, and mix evenly;

[0065] Step 2. Slowly add titanium dioxide (TS-6200), fumed silica and diamond blue into the batching tank according to parts by weight and disperse evenly, and then use a sand mill to grind to a fineness of ≤25 μm;

[0066] Step 3, add aluminum silicate sol and isopropanol paint in turn, mix well;

[0067] Finally, after degreasing and degreasing the aluminum plate, use 120-mesh corundum for sandblasting, then use high-pressure air to remove dust, mix the paint evenly and then spray it. The thickness of the paint film is controlled at 20-30μm.

[0068] T...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a ceramic crystal coating for metal surfaces and a preparation method thereof. The ceramic crystal coating for metal surfaces is composed of nano-oxides or nano silicate colloids, high-temperature-resistant pigments and fillers, organic modifiers and additives, has the characteristics of high temperature resistance, no stain sticking, super weather resistance, super wear resistance, non combustion, fire prevention and high hardness, can be used on the surfaces of iron and steel or aluminum alloys required to be high-temperature-resistant and wear-resisting, and also can be applied to the coating of aluminum sheets, aluminum honeycomb panels or other metal plates for outdoor and indoor decoration.

Description

【Technical field】 [0001] The invention belongs to the technical field of coatings, in particular to inorganic-based coating compositions. 【Background technique】 [0002] The existing non-stick pans have been used around the world for decades, but the debate on it has never stopped. Until a few years ago, the U.S. Environmental Protection Agency (EPA) released the results of long-term follow-up tests, and finally made a ruling, ordering eight chemical companies including DuPont to gradually reduce or stop using the core components required to manufacture Teflon non-stick coatings Ammonium perfluorooctanoate (PFOA). In addition, according to the requirements of the EPA, the use of PFOA should be reduced by 95% in 2010, and its use should be completely banned by 2015. In addition, the high temperature resistance of Teflon non-stick pans is not good, and the risk of coating decomposition increases greatly when the temperature is higher than 250 ° C. Once these organic coatings...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D1/00C09D7/12
Inventor 黄玉科侯汉亭
Owner ZHUHAI FUTE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com