Processing method for verticality of non-magnetic sheet-shaped material
A technology of sheet materials and processing methods, applied in metal processing equipment, manufacturing tools, machine tools suitable for grinding workpiece planes, etc., can solve problems such as waste of electricity, low yield rate, local air pollution, etc., and achieve reliable production quality , low production cost and low environmental pollution
Active Publication Date: 2012-11-07
北京石晶光电科技股份有限公司
View PDF5 Cites 3 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0004] 1. Use paraffin or cold glue for sticking. After processing, it needs to be melted. The wax or cold glue on the edge of the material is not easy to clean, which directly affects the follow-up high-precision polishing yield. It takes a long time after paraffin or cold glue is bonded Chemical weights, paraffin or cold glue are toxic, causing local air pollution, waste of water and electricity, slow turnover between processes and low efficiency
[0005] 2. There is no processing reference plane during grinding, resulting in low yield, and the verticality of the four corners of the sheet material cannot meet the high-precision requirements
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0026] The technical solutions of the present invention will be described in further detail below through specific implementation methods.
[0027] A method for processing the perpendicularity of a non-magnetic sheet material, comprising the following steps:
[0028] Step 1, making crystal lump: with the main plane of the sheet material as the adjacent surface, stack multiple pieces of the sheet material into a cuboid crystal lump, and the main planes of the outermost two sheet materials of the cuboid crystal lump are respectively used as cuboids The front side and the back side of the crystal lump, the remaining four sides of the cuboid crystal lump are respectively used as the upper edge face, the lower edge face, the left edge face and the right edge face of the cuboid crystal block according to the prescribed position, and a plurality of sheet-like The materials are stacked together to form a cuboid crystal lump;
[0029] Step 2, install the crystal: clamp the cuboid crys...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention provides a processing method for verticality of a non-magnetic sheet-shaped material. The processing method comprises a first step of making a crystal lump, namely folding the sheet-shaped material into the cuboid crystal lump after soaking the sheet-shaped material; a second step of installing the crystal lump, namely enabling the cuboid crystal lump to be clamped on a working table of a vertical shaft full-automatic surface grinder; a third step of fixing the crystal lump, namely knocking a gasket, a movable gasket and the cuboid crystal lump, enabling the gasket and the movable gasket to clamp the cuboid crystal lump, and fixing the movable gasket after knocking; a fourth step of grinding the crystal lump, namely setting processing parameters according to the processing requirements to grind the cuboid crystal lump; and a fifth step of separating the crystal lump, namely separating the processed cuboid crystal lump. The processing method for the verticality of the non-magnetic sheet-shaped material has the advantages of being scientific in design, short in process flow, high in production efficiency, reliable in production quality, low in production quality and small in environmental pollution.
Description
technical field [0001] The invention relates to a method for processing perpendicularity of materials, in particular to a method for processing perpendicularity of non-magnetic sheet materials. Background technique [0002] At present, the sticking process is used in China to process the shape of non-magnetic sheet materials. The traditional processing process includes sticking sheet materials into mounds, surface grinding, inspection, 9S grinding, inspection and mounding. The specific production process is as follows: After a certain amount of flake materials are bonded into mounds, they are put into special tooling and then processed on special equipment. Revolutionary movement, grinding upper and lower processing. Since there is a gap after the mound is put into the tooling, the height of the tooling is not exactly the same as that of the mound. During the process of revolution and rotation, the four sides of the mound will be used as the processing reference plane and t...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine