Priming paint for plastic cement

A primer and plastic technology, applied in the direction of coating, etc., can solve the problems of long production cycle, labor-intensive, high energy consumption, etc., and achieve the effect of solving high energy consumption, saving electricity, and reducing consumption

Inactive Publication Date: 2012-11-14
KUSN WANSHENG CHEM
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The invention solves the problems of high energy consumption, manpower consumption, long production cycle and serious pollution in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Priming paint for plastic cement
  • Priming paint for plastic cement
  • Priming paint for plastic cement

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0084] The preparation method of the plastic primer of the present invention is given below (the components in the following steps are added in proportion):

[0085] Step 1: Add the thermoplastic acrylic resin, the polymer copolymer containing the pigment affinity group, the unsaturated polyamic acid homopolymer, the silicone, and the cellulose ester in order and then stir and mix at 800RPM for 5 minutes;

[0086] Step 2: Add pigments and nano-sized fillers to the solution obtained in Step 1, stir evenly at 2000-3000RPM, and grind until the fineness is less than or equal to 10μm;

[0087] Step 3: Add a multi-functional reactive diluent and a bi-functional reactive diluent to the solution obtained in step 2, and stir it evenly at 800RPM;

[0088] Step 4. Mix the cleavage type photoinitiator, hydrogen abstraction type photoinitiator, acylphosphine oxide photoinitiator and ethyl acetate until it becomes clear and transparent, and then add the mixed solution to the solution obtained in ste...

Embodiment 1

[0091] Thermoplastic acrylic resin 39%;

[0092] 2% polymer copolymer with pigment affinity group;

[0093] 0.3% of unsaturated polyamic acid homopolymer;

[0094] 0.1% organic silicon;

[0095] Cellulose acetate butyrate 22%;

[0096] Titanium dioxide 4%;

[0097] Nano-scale silica filler 5%;

[0098] Pentaerythritol triacrylate 6%;

[0099] Dipropylene glycol diacrylate 4%;

[0100] 1-hydroxy-cyclohexyl phenone 1%;

[0101] 2,4-Dihydroxybenzophenone 0.6%;

[0102] 2,4,6-Trimethylbenzoyl-diphenylphosphine oxide 1%;

[0103] Ethyl acetate 15%.

Embodiment 2

[0105] Thermoplastic acrylic resin 20%;

[0106] 2% polymer copolymer with pigment affinity group;

[0107] 0.1% of unsaturated polyamic acid homopolymer;

[0108] Aralkyl modified silicone 0.1%;

[0109] Nitrocellulose ester 33%;

[0110] Carbon black 10%;

[0111] Nano-sized zirconia filler 3%;

[0112] Pentaerythritol triacrylate 10%;

[0113] Dipropylene glycol diacrylate 5%;

[0114] 1-hydroxy-cyclohexyl phenone 3%;

[0115] 2,4-Dihydroxybenzophenone 0.8%;

[0116] 2,4,6-Trimethylbenzoyl-diphenylphosphine oxide 1%;

[0117] Ethyl acetate 13%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses priming paint for plastic cement. The priming paint comprises the following components by weight: 20-40% of thermoplastic acrylic resin, 0-2% of pigment contained affine perssad macromolecule interpolymer, 0.1-0.3% of unsaturation polyamic acid homopolymer, 0.1-0.2% of organosilicon, 20-40% of cellulose ester, 2-10% of pigment, 3-5% of nanometer stage padding, 5-10% of polyfunctional group reactive diluent, 2-5% of dual-functional group reactive diluent, 1-3% of cracking-type photoinitiator, 0.5-1% of hydrogen taking type photoinitiator, 0.5-1% of acyl phosphine oxidate photoinitiator and 10-15% of acetic ether. The priming paint is an ultraviolet photocureable coating and has good flame plating viscosity in a work progress. The priming paint solidifies under irradiation of ultraviolet lamps and only needs 3-4minutes of solidifying time, and a larger amount of electric power is saved. Consumption of the priming paint of each electrombile respectively is reduced by 34% and 45%. The priming paint has good hardness and ground floor adhesive force, and the priming paint for the plastic cement is combined with finish paint for the plastic cement for use and can keep good ply adhesion with the finish paint for the plastic cement on an upper layer.

Description

Technical field [0001] The invention relates to coatings, in particular to a primer for plastics. Background technique [0002] People’s awareness of environmental protection is constantly improving, and environmental protection regulations are gradually introduced and implemented, and are constantly being improved. This situation forces companies in the manufacturing field to continuously improve their production processes to improve the affinity of products with nature. At present, the coating industry is gradually developing in the direction of environmental protection and energy saving water-based and UV (ultraviolet light curing). UV curing coatings are quickly accepted and promoted by the market due to their environmental protection, fast speed and low energy consumption, and the application range is becoming wider and wider. However, the spray paint used for plastic parts in the motorcycle and electric vehicle industries still has problems such as high energy consumption,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D4/06C09D7/12
Inventor 杨兴泉
Owner KUSN WANSHENG CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap