High-strength and low-expansion coefficient alloy wire and manufacturing method thereof

A low expansion coefficient, alloy wire technology, applied in the field of alloy and its manufacturing, can solve the problems of low thermal expansion coefficient, low strength of Invar alloy wire, etc.

Active Publication Date: 2013-01-23
宝武特种冶金有限公司
View PDF8 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The alloy wire rod of the present invention adopts the strengthening method of intermetallic compound strengthening and cold deformation strengthening, on the basis of the chemical composition of Fe-36Ni Invar alloy, by effectively utilizing Ti and Al, and limiting them within an appropriate composition range , using a...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength and low-expansion coefficient alloy wire and manufacturing method thereof
  • High-strength and low-expansion coefficient alloy wire and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-5 and comparative example 1-5

[0036] According to the following steps, the high-strength low-expansion coefficient alloy wire rod of the present invention is manufactured, and the specific process parameters of each step are shown in Table 2:

[0037] (1) smelting with a 150Kg vacuum induction furnace, and casting obtains a 135Kg ingot, and its chemical composition mass percentage distribution is as shown in Table 1;

[0038] (2) Forging the spindle into a round bar with a diameter of φ50mm;

[0039] (3) Heating the round bar to 1050-1100°C and rolling it into a wire rod, the diameter of the wire rod is φ10mm;

[0040] (4) Carry out cold drawing for the first time to wire rod, and deformation amount is 20~75%;

[0041] (5) Carry out solution heat treatment, the temperature is 1000~1150 ℃;

[0042] (6) Pickling and peeling;

[0043] (7) Carry out aging heat treatment, the temperature is 600~700 ℃;

[0044] (8) Carry out the second cold drawing, and the deformation amount is ≥55%.

[0045] Table 1. (Bal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Coefficient of expansionaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-strength and low-expansion coefficient alloy wire. The matrix is of austenite. The austenitic matrix is dispersedly distributed with Ni3(Ti, Al). The chemical elements of the high-strength low-expansion coefficient alloy wire includes by mass percent: no more than 0.05% of C; no more than 0.50% of Si; no more than 0.60% of Mn; 36.0-42.0% of Ni; 1.5-3.0% of Ti; 0.3-1.0% of Al; the balance being Fe and other unavoidable impurities. Accordingly, the present invention also discloses a manufacturing method of the high-strength and low-expansion coefficient alloy wire. The tensile strength of the high-strength and low-expansion coefficient alloy wire described by the invention is greater than or equal to 1500 Mpa, and the average linear expansion coefficient is less than or equal to 3.5*10-6/DEG C in the range of 20-100 DEG C temperature.

Description

technical field [0001] The invention relates to an alloy and a manufacturing method thereof, in particular to an alloy wire rod and a manufacturing method thereof. Background technique [0002] Invar alloy Fe-36Ni, the chemical composition is: C≤0.05%, Si≤0.20%, P≤0.020%, S≤0.020%, Ni: 35.7~37.0%, Mn: 0.20~0.60%, the rest is Fe and not The impurity to be avoided is a low expansion coefficient alloy whose expansion coefficients are ≤1.5×10 in the temperature ranges of 20-100°C and 20-300°C respectively -6 / °C and ≤5.1×10 -6 / °C. Invar alloys are widely used due to their very low coefficient of expansion. For example, it can be used to manufacture standard rulers, inner walls of liquefied natural gas ship cabins, carbon fiber composite molds, etc. However, the strength of ordinary Invar alloy is very low, about 400-500MPa, which limits its use in low-expansion structural parts. [0003] At present, the main method to improve the strength of Invar alloy is to use Fe-36Ni a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/14C21D8/06
Inventor 陆建生
Owner 宝武特种冶金有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap