Anti-aging plastic wood composite material and preparation method thereof

A wood-plastic composite material and anti-aging technology, applied in the field of composite materials, can solve the problems of high manufacturing cost of plastic wood, low anti-aging performance, environmental pollution of waste plastics, etc., to reduce usage, enhance surface aging resistance, improve The effect of service life

Inactive Publication Date: 2013-02-13
GEM CO LTD
View PDF5 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide an economical and practical anti-aging plastic-wood composite material and its preparation method to solve the problems of high manufacturing cost, low anti-aging performance and huge environmental pollution caused by waste plastics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Raw material components by weight

[0030] 29 parts of polyethylene (PE), 43 parts of wood flour, 3 parts of vinyl tris(methoxyethoxy) silane, 6 parts of PE grafted maleic anhydride, 15 parts of ammonium polyphosphate, 2 parts of zinc stearate, 2 parts of dioctyl phthalate, 0.5 parts of anti-aging agent filler (antioxidant 168) and 1.2 parts of coloring agent.

[0031] Add the above raw materials into a high-speed mixer until they are evenly mixed, and then react and extrude the mixed materials in a twin-screw extruder to make pellets. The melting temperature of the screw is 190°C and the speed is 180 rpm. The granulator cuts into granules to obtain pellets.

[0032] Put the obtained pellets into an extruder for extrusion molding to obtain the wood-plastic composite material of the present invention, and the bending strength of the obtained profile reaches 26MPa after testing.

Embodiment 2

[0034] Raw material components by weight

[0035] 30 parts of polypropylene (PP), 42 parts of wheat straw fiber powder, 4 parts of vinyltrimethoxysilane, 6 parts of PP grafted maleic anhydride, 14 parts of ammonium polyphosphate, 2 parts of zinc stearate, phthalic acid 3 parts of dibutyl ester, 1 part of anti-aging filler (antioxidant 168) and 1.2 parts of colorant.

[0036] Add the above-mentioned raw materials into a high-speed mixer until they are evenly mixed, and then react and extrude the mixed materials in a twin-screw extruder to make pellets. The granulator cuts into granules to obtain pellets.

[0037] Put the obtained pellets into an extruder for extrusion molding to obtain the wood-plastic composite material of the present invention, and the bending strength of the obtained profile reaches 51 MPa after testing.

Embodiment 3

[0039] Step 1. After sorting, crushing, cleaning and drying the recovered waste plastics, add them to the high-speed mixer and mix them well for later use. The mixing time is controlled within 5-10 minutes; if it is new plastics, directly mix them at high speed The machine is fully mixed and ready for use, and the mixing time is controlled at 5-10 minutes;

[0040] Step 2: In parts by weight, take 16 parts of plastics treated in step 1, 21 parts of wood flour and wheat straw powder mixture, 1.5 parts of hexamethyldisiloxane, 3 parts of PP grafted maleic anhydride, triphenyl phosphate 6.5 parts of ester, 1 part of sodium stearate, 0.25 part of dibutyl phthalate, 0.75 part of colorant titanium dioxide, 0.01 part of anti-aging filler (antioxidant DLTP), and fully mix in a high-speed mixer, The mixing time is controlled within 10-20 minutes;

[0041] Step 3: In parts by weight, take 16 parts of plastics treated in step 1, 21 parts of wood flour and wheat straw powder mixture, 1.5...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
bending strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a composite material, and particularly relates to an anti-aging plastic wood composite material and a preparation method thereof. The anti-aging plastic wood composite material of the invention is characterized in that the composite material is prepared by the following raw materials by mass: 20%-35% of plastics, 20%-70% of natural wood fibers, 5%-45% of a fire retardant, 1%-10% of a compatibilizer, 0.1%-3% of a lubricant, 0.5%-3% of a plasticizer, 0.1%-2% of a anti-aging filling material, and 0.5%-3% of a coloring agent. According to the invention, the reinforcing anti-aging filling material is added into the plastic wood composite material, which provides the plastic wood profile with both general functions and superpower anti-aging performance, effectively enhances the surface anti-aging performance of the plastic wood profile, and improves the service life of the plastic wood product.

Description

technical field [0001] The invention relates to composite materials, in particular to an anti-aging plastic-wood composite material and a preparation method thereof. Background technique [0002] Wood-plastic composite material is a new type of environmentally friendly composite material. It uses various waste natural wood fibers and plastics to compound, adds special additives, and extrudes a new type of environmentally friendly composite material that is both similar to wood and better than wood. . This material has the advantages of good dimensional stability, high specific strength, and repeated recycling, and has been widely used in indoor and outdoor construction, transportation, packaging and other fields. [0003] It is precisely because of the many advantages of wood-plastic composite materials that the market has grown rapidly, and the rapidly expanding market has put forward higher performance requirements for wider applications of wood-plastic composite material...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08L23/06C08L23/12C08L27/06C08L25/06C08L55/02C08L69/00C08K13/02B29B9/06B29C47/92B29C48/92
Inventor 闫梨张翔程青民黄旭江
Owner GEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap