A technology of wool fiber and core-spun yarn, which is applied in the direction of yarn, textiles and papermaking, etc. It can solve the problems of poor covering effect, achieve good covering effect and reduce the effect of bare phenomenon

Inactive Publication Date: 2013-02-20
XI'AN POLYTECHNIC UNIVERSITY
View PDF8 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a method for preparing wool fiber core-spun yarn, which solves the problem of poor covering effect of the short fibers of the existing core-spun yarn on the outside of the filament core yarn

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Step 1: On the dual-zone three-roller drafting mechanism of the ring spinning frame, the wool roving sliver is fed from the bell mouth and drafted by the cradle drafting mechanism; the polyester filament is drawn from the front roller gripper Mouth feeding, merged with the drawn wool roving sliver;

[0027] Step 2: The polyester filament is conveyed by the front roller and fed into the twisting area of ​​the wool roving sliver. The filament is conveyed through a precision-made yarn guide device and aligned with the center of the wool roving sliver. After merging with the wool roving sliver , and enter into the twisting triangle area of ​​ring spinning together for twisting;

[0028] Step 3: Control the tension of the filament through the filament tension control device, and the filament tension value is 30cN; Carry out wool fiber coating twisting to filament for the first time, and the twist coefficient of its coating twisting is 260 respectively, twist direction S;

...

Embodiment 2

[0032] Step 1: On the dual-zone three-roller drafting mechanism of the ring spinning frame, the wool roving sliver is fed from the bell mouth and drafted by the cradle drafting mechanism; the polyester filament is drawn from the front roller gripper Mouth feeding, merged with the drawn wool roving sliver;

[0033] Step 2: The polyester filament is conveyed by the front roller and fed into the twisting area of ​​the wool roving sliver. The filament is conveyed through a precision-made yarn guide device and aligned with the center of the wool roving sliver. After merging with the wool roving sliver , and enter into the twisting triangle area of ​​ring spinning together for twisting;

[0034] Step 3: Control the tension of the filament through the filament tension control device, and the filament tension value is 40cN; Carry out the wool fiber coating twisting for the first time to the filament, the twist coefficient of the coating twisting is 240 respectively, and the twist dir...

Embodiment 3

[0038] Step 1: On the dual-zone three-roller drafting mechanism of the ring spinning frame, the wool roving sliver is fed from the bell mouth and drafted by the cradle drafting mechanism; the polyester filament is drawn from the front roller gripper Mouth feeding, merged with the drawn wool roving sliver;

[0039] Step 2: The polyester filament is conveyed by the front roller and fed into the twisting area of ​​the wool roving sliver. The filament is conveyed through a precision-made yarn guide device and aligned with the center of the wool roving sliver. After merging with the wool roving sliver , and enter into the twisting triangle area of ​​ring spinning together for twisting;

[0040] Step 3: Control the tension of the filament through the filament tension control device, and the filament tension value is 20cN; Carry out wool fiber coating twisting for the first time to filament, and the twist coefficient of its coating twisting is 280 respectively, twist direction Z;

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of wool fiber core spun yarn. Filaments are mainly taken as core yarn, wool fiber coating is performed on the surface of the core yarn twice, the twisting direction of wool fibers during the first coating is opposite to the twisting direction of the wool fibers during the second coating, the content of filament core yarn in the wool fiber core spun yarn produced through the method is 20%-35%, and the content of wool fibers is 65%-80%. According to the preparation method of the wool fiber core spun yarn, the filament is coated by the wool fibers twice and twisting directions of coating are opposite, so that sliding of the wool fibers on the surface of the filament core yarn is reduced or avoided, exposed filament core yarn on the surface of fabric is reduced, and the coating effect is good.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a preparation method of wool fiber core-spun yarn. Background technique [0002] Core-spun yarn is generally a yarn made of synthetic fiber filaments with good strength and elasticity as the core yarn, and short fibers such as cotton, wool, and viscose fibers are twisted and spun together. The more common core-spun yarns include polyester-cotton core-spun yarn, which uses polyester filament as the core yarn and outsources cotton fibers; and spandex core-spun yarn, which uses spandex filament as the core yarn and outsources yarn made of other fibers. The disadvantage of these core-spun yarns is that the short fibers are covered only once outside the filament core yarn, and the short fibers in the yarn will slip on the filaments, causing the filaments to be exposed in some segments of the yarn, on the surface of the fabric. Defects occur and the coating effect is poor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/36D02G3/26D02G3/04
Inventor 李龙韩惠民
Owner XI'AN POLYTECHNIC UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap