A kind of automobile engine shield and its preparation process

A technology for automobile engines and raw materials, which can solve the problems of low material strength, high price, and heavy weight, and achieve the effect of light material

Active Publication Date: 2015-12-23
宁波江宸智能装备股份有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Cons: easily damaged
[0010] Cons: heavy
[0014] Disadvantages: high price, low material strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] An automobile engine guard plate, each component is measured by weight, and each component is measured by weight, 30 parts of low-density polyethylene, 20 parts of silicon, 5 parts of copper, 5 parts of nickel, 3.5 parts of manganese, and 0.2 parts of metallocene material share.

[0027] Its preparation process: put the compounds of various alloying elements in a smelting furnace, add high-density polyethylene and metallocene materials when they are completely melted, remove impurities, and then press them into 6-10mm plates according to the required size. Can.

Embodiment 2

[0029] A protective plate for an automobile engine. The components are, by weight, 30 parts of high-density polyethylene, 20 parts of silicon, 3 parts of copper, 2 parts of nickel, 2 parts of manganese and 0.05 parts of metallocene material.

[0030] Its preparation process is with embodiment 1.

Embodiment 3

[0032] A protective plate for an automobile engine. The components are, by weight, 50 parts of high-density polyethylene, 50 parts of silicon, 10 parts of copper, 8 parts of nickel, 5 parts of manganese and 0.3 parts of metallocene material.

[0033] Its preparation process is with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an automobile engine guard plate. The components are calculated in parts by weight, including 30-50 parts of high-density polyethylene, 20-50 parts of silicon, 3-10 parts of copper, 2-8 parts of nickel and 2-5 parts of manganese. parts, metallocene material 0.05-0.3 parts. Its preparation process: put the compounds of various alloying elements in a smelting furnace, add high-density polyethylene and metallocene materials when they are completely melted, remove impurities, and then press them into 6-10mm plates according to the required size. Can. The engine fender provided by the present invention breaks the limitation concept of materials in the prior art, combines the polymer material with the alloy, and combines the polymer material with the alloy element according to the structure and performance of the alloy element to form a The material is light, and at the same time, it can meet the super impact resistance and has the characteristics of low cost.

Description

technical field [0001] The invention relates to an automobile engine guard plate and a manufacturing process thereof, belonging to the field of mechanical manufacturing. Background technique [0002] The engine protection plate is an engine protection device designed according to various models. Its design is first to prevent the engine from being wrapped in mud and cause poor heat dissipation of the engine, and secondly to prevent the engine from being hit by the uneven road during driving. Engine damage, through a series of designs to prolong the service life of the engine, to avoid engine damage caused by external factors during travel. The current engine guards are divided into the following three categories, but each has its own advantages and disadvantages, and its materials cannot achieve satisfactory results: [0003] 1. Hard plastic and resin guard plate. [0004] The price is relatively cheap, and the production process is simple, but it should be noted that the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08K3/02C08K3/08
Inventor 陈凌
Owner 宁波江宸智能装备股份有限公司