Preparation method for high-strength and high-hardness nanocrystalline tungstate-cobalt hard alloy

A cemented carbide, high hardness technology, applied in the field of cemented carbide preparation, can solve the problem of low high temperature hardness and high temperature strength of alloys, increase the difficulty of manufacturing high-quality cemented carbide, and difficult to unify wear resistance and toughness. problems, to achieve the effect of improving the overall performance of the alloy, reducing the defects, and slowing down the irregular growth.

Inactive Publication Date: 2013-03-27
HUNAN CENTURY SPECIAL ALLOY
View PDF6 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the continuous development of the cemented carbide industry, the requirements for its raw material WC powder (ie tungsten carbide powder) are getting higher and higher, especially the preparation of nano-sized cemented carbide has strict requirements on the particle size of WC powder. At present, The degree of aggregation of WC powder is relatively high, and it is difficult for tungsten carbide powder manufacturers to control the powder particle size to meet the requirements of nanocrystalline cemented carbide manufacturing. The WC powder produced has WC particle aggregates.
Due to the different degree of combination of aggregates, it is more difficult to manufacture high-quality cemented carbide, making it difficult to achieve a high degree of uniformity in wear resistance and

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A method for preparing high-strength, high-hardness nanocrystalline tungsten-cobalt cemented carbide, which includes the following process steps: conventional raw material intensive grinding, batching, wet grinding, drying, mixing forming agents, granulation, compression molding and pressure sintering ;Using sub-fine WC powder with a particle size of 0.6~0.8μm (FSSS) as raw material, 1‰VC and 2.5‰Cr 2 C is an inhibitor. The chemical reagent Tween 80 and the mass ratio of acetone and n-hexane mixture are 1:9 for grinding. The ball milling medium is a mixture of acetone and n-hexane, and the mass ratio is 6:4. , the sub-fine WC powder is jet-grinded, dispersed and classified for 28 hours; the coarse-grained WC particles are removed, and the sieved coarse-grained WC is re-grinded, and the final average particle size is 0.1~0.4μm (FSSS) WC powder with superfine particle size; 0.2~0.4μm (FSSS) ultrafine particle size cobalt powder and 0.1~0.4μm (FSSS) superfine particle size...

Embodiment 2

[0029] A method for preparing high-strength, high-hardness nanocrystalline tungsten-cobalt cemented carbide, which includes the following process steps: conventional raw material intensive grinding, batching, wet grinding, drying, mixing forming agents, granulation, compression molding and pressure sintering ;Using sub-fine WC powder with a particle size of 0.6~0.8μm (FSSS) as raw material, 1.5‰VC and 3.5‰Cr 2 C is an inhibitor. The chemical reagent Tween 80 and the mass ratio of acetone and n-hexane mixture are 1.5:8.5 for grinding. The grinding medium is a mixture of acetone and n-hexane, and the mass ratio is 7:3. , through 36 hours of jet grinding, dispersing and classifying and sieving the sub-fine WC powder; remove the coarse-grained WC particles, and re-grind the sieved coarse-grained WC, and finally select the average particle size of 0.1~0.4μm (FSSS) WC powder with superfine particle size; 0.2~0.4μm (FSSS) ultrafine particle size cobalt powder and 0.1~0.4μm (FSSS) sup...

Embodiment 3

[0032]A method for preparing high-strength, high-hardness nanocrystalline tungsten-cobalt cemented carbide, which includes the following process steps: conventional raw material intensive grinding, batching, wet grinding, drying, mixing forming agents, granulation, compression molding and pressure sintering ;Using sub-fine WC powder with a particle size of 0.6~0.8μm (FSSS) as raw material, 1‰VC and 4.5‰Cr 2 C is an inhibitor. The chemical reagent Tween 80 and the mass ratio of acetone and n-hexane mixture are 1:9. The enhanced grinding process is combined. The ball milling medium is a mixture of acetone and n-hexane, and the mass ratio is 7:3. , the sub-fine WC powder is jet-grinded, dispersed and classified for 42 hours; the coarse-grained WC particles are removed, and the sieved coarse-grained WC is re-grinded, and the final average particle size is 0.1~0.4μm (FSSS) WC powder with superfine particle size; 0.2~0.4μm (FSSS) ultrafine particle size cobalt powder and 0.1~0.4μm (...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Average grain sizeaaaaaaaaaa
Average flexural strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method for a high-strength and high-hardness nanocrystalline tungstate-cobalt hard alloy, which is finished by adopting eight process flows of reinforced grinding machining, proportioning, wet-grinding, drying, forming agent doping, granulating, press-forming and pressure-sintering for the conventional raw material, namely, sub-fine WC (tungstate-cobalt) powder; in the method, common sub-fine-grain WC powder having a Fsss (furnace safeguard supervisory system) granularity of 0.6-0.8 mum, and metal Co powder having a granularity of 0.2-0.4 mum; and the granularity and the granularity distribution of the sub-fine WC are changed by the added working procedure of reinforced grinding treatment, so that the advantage granularity of WC in the obtained super-coarse-grain hard alloy achieves 0.2-0.4 mum, and the hard alloy is high in toughness, complete in crystallization, few in defects, small in microstrain, uniform in sub-fine grains, high in microhardness, and greatly improves the wear resistance and impact toughness.

Description

technical field [0001] The invention relates to a preparation method of cemented carbide, in particular to a preparation method of high-strength and high-hardness nanocrystalline tungsten-cobalt cemented carbide. Background technique [0002] With the continuous development of the cemented carbide industry, the requirements for its raw material WC powder (ie tungsten carbide powder) are getting higher and higher, especially the preparation of nano-sized cemented carbide has strict requirements on the particle size of WC powder. At present, The degree of aggregation of WC powder is relatively high, and it is difficult for tungsten carbide powder manufacturers to control the powder particle size to meet the requirements of nanocrystalline cemented carbide manufacturing. The WC powder produced has WC particle aggregates. Due to the different degree of combination of aggregates, it is more difficult to manufacture high-quality cemented carbide, making it difficult to achieve a h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C1/05C22C29/08
Inventor 李亚兰肖华
Owner HUNAN CENTURY SPECIAL ALLOY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka