Production method of 5052-H34 aluminum alloy plate strip
A technology of aluminum alloy strip and production method, which is applied in the field of aluminum alloy manufacturing, can solve the problems of high temperature uniformity and precision requirements of annealing furnace, change of annealing temperature range, large dispersion of mechanical properties, etc., and achieve temperature measurement accuracy and furnace Reduced temperature uniformity requirements, stable performance after annealing, and large temperature range
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0025] The production method of the 5052-H32 aluminum alloy plate and strip in this embodiment includes the following production process: melting and casting→sawing→face milling→heating→hot rolling→cold rolling→finished product annealing→finishing.
[0026] (1) Melting and casting: the mass percentage of the chemical composition of the ingot after melting and casting is:
[0027] Al
Si
Fe
Cu
mn
97.0772
0.0598
0.1568
0.0029
0.0228
Mg
Ti
Cr
Zn
Ni
2.4062
0.0161
0.2436
0.0116
0.003
[0028] The melting temperature is 740-755°C, the refining temperature is 720-735°C, and the casting temperature is 675-680°C.
[0029] (2) Heating: After the ingot is heated to 500°C, the holding time is 4 hours.
[0030] (3) Hot rolling: the finishing temperature of hot rough rolling is 440°C, the finishing temperature of hot finishing rolling is 333°C, and the thickness of hot rolling billet: 2.5mm ...
Embodiment 2
[0036] The production method of the 5052-H34 aluminum alloy plate and strip in this embodiment includes the following production process: melting and casting→sawing→face milling→heating→hot rolling→cold rolling→finished product annealing→finishing.
[0037] (1) Melting and casting: the mass percentage of the chemical composition of the ingot after melting and casting is:
[0038] Al
Si
Fe
Cu
mn
96.7989
0.0623
0.2621
0.0044
0.0196
Mg
Ti
Cr
Zn
Ni
[0039] 2.6577
0.0148
0.1682
0.0095
0.0025
[0040] The melting temperature is 740-755°C, the refining temperature is 725-740°C, and the casting temperature is 680-695°C.
[0041] (2) Heating: the ingot heating temperature is 515°C, and the holding time is 2.5 hours.
[0042] (3) Hot rolling: the finishing temperature of hot rough rolling is 448°C, the finishing rolling temperature of hot finishing rolling is 340°C, and the t...
Embodiment 3
[0049] The short-process production method of 5052-H34 aluminum alloy plate and strip in this embodiment includes the following production process: melting and casting→sawing→face milling→heating→hot rolling→cold rolling→finished product annealing→finishing.
[0050] (1) Melting and casting: the mass percentage of the chemical composition of the ingot after melting and casting is:
[0051] Al
Si
Fe
Cu
mn
97.1321
0.0639
0.1642
0.0039
0.0127
Mg
Ti
Cr
Zn
Ni
2.3576
0.0213
0.2241
0.0166
0.0036
[0052] The melting temperature is 735-750°C, the refining temperature is 720-740°C, and the casting temperature is 680-690°C.
[0053] (2) Heating: the heating temperature of the ingot is 490°C, and the holding time is 5 hours.
[0054] (3) Hot rolling: the finishing temperature of hot rough rolling is 433°C, the finishing temperature of hot finishing rolling is 340°C, and the thickness of ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com