Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Aluminum alloy, and aluminum alloy casting

A technology of aluminum alloy castings and aluminum alloys, applied in the field of aluminum alloy castings, can solve the problems of mass production of stainless steel and the realization of precise product shape limitations, stainless steel weight, etc.

Inactive Publication Date: 2013-04-24
INTERPLEX QUANTUM
View PDF6 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, although stainless steel can be formed by pressing or forging, stainless steel has limitations in mass production and the realization of precise product shapes, and is heavier than stainless steel with a specific gravity of about 8.00g / cm3

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum alloy, and aluminum alloy casting
  • Aluminum alloy, and aluminum alloy casting
  • Aluminum alloy, and aluminum alloy casting

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The present invention will now be described more fully hereinafter with reference to the accompanying drawings, in which exemplary embodiments of the invention are shown. This invention may, however, be embodied in many different forms and should not be construed as limited to the embodiments set forth in this specification; rather, these embodiments are provided so that this disclosure will be thorough and complete, and will convey information to those skilled in the art. Fully express the concept of the present invention.

[0019] In an embodiment of the present invention, weight % (wt %) means the weight of a component expressed as a percentage in the total weight of the alloy. When the weight % range is greater than or lower than the boundary value, it can be understood that the boundary value is not included; and when it is indicated simply as a range or as equal to or greater than or equal to or less than, the boundary value is included.

[0020] In an embodiment...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a metal alloy, and more specifically, to an aluminum alloy used in electrical, electronic, mechanical parts and the like, and an aluminum alloy casting prepared by using the same. An aluminum alloy according the one embodiment comprises 4-13 wt% of silicon (Si), 1-5 wt% of copper (Cu); zinc (Zn) in an amount equal to or more than 26 wt% and less than 40 wt%; and the remaining aluminum (Al) and inevitable impurities.

Description

technical field [0001] The present invention relates to metal alloys, more particularly aluminum alloys for electrical, electronic and mechanical components, and aluminum alloy castings made using said aluminum alloys. Background technique [0002] Recently, as electronic products such as notebook computers and mobile phones have become more complex in appearance and function, there has been an increasing demand for high-strength materials that are more resistant to deformation. In particular, some components, such as brackets that support part of a liquid crystal display (LCD) panel and hinges that are thin and complex in shape, require lightweight materials for portability and high strength similar to stainless steel (such as 304 stainless steel) . However, although stainless steel can be formed by pressing or forging, stainless steel has limitations in mass production and realization of precise product shapes, and is heavier than stainless steel with a specific gravity o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/10
CPCC22C21/10C22C30/06C22C30/02C22C30/04
Inventor 李胜珍李炯澈
Owner INTERPLEX QUANTUM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More