Non-woven fabric and method for producing non-woven fabric

A manufacturing method and technology of non-woven fabrics, applied in the direction of textiles and papermaking, non-woven fabrics, fabric elongation, etc., can solve the problem of non-woven fabric breaking strength, non-woven fabric damage, and manufacturing speed that are difficult to reduce fluffed non-woven fabrics Slow and so on

Active Publication Date: 2013-05-01
KAO CORP
View PDF15 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] However, both the method of producing a fluffed nonwoven fabric described in Patent Document 4 and the method of processing a napped sheet described in Patent Document 5 use sandpaper to process the nonwoven fabric, so the nonwoven fabric is subjected to a Large damage, it is difficult to reduce the drop of the nonwoven breaking strength of the raised nonwoven fabric obtained
In addition, since the method for producing a nonwoven fabric described in Patent D

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-woven fabric and method for producing non-woven fabric
  • Non-woven fabric and method for producing non-woven fabric
  • Non-woven fabric and method for producing non-woven fabric

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0166] [Example 1]

[0167] Using a spunbond layer composed of ethylene propylene copolymer resin with a fiber diameter of 14.7 μm, the weight per square meter is 15 g / m 2 The nonwoven fabric (spunbond-meltblown-spunbond laminated nonwoven fabric, also referred to as SMS hereinafter) (the nonwoven fabric in this state is referred to as Comparative Example 5). Next, pass the SMS non-woven fabric through image 3 The matching embossed steel roller 43 shown in Figure 4 The convex roller 51 shown in is subjected to surface treatment and two-stage treatment to obtain a nonwoven fabric. The height of each convex part 410 in the roller 41 of the matching embossed steel roller 43 used is 2.8 mm, and the meshing depth of each convex part 410 of the roller 41 and each concave part 420 of the roller 42 is 2.7 mm. In addition, the distance (gap) between the convex portions 410 adjacent to each other in the rotation axis direction is 7 mm, and the distance (gap) between the convex portions 4...

Example Embodiment

[0168] [Example 2]

[0169] Using a spunbond layer composed of acrylic resin with a fiber diameter of 17.7μm, and a weight of 15g / m per square meter 2 Non-woven fabric (spunbond-meltblown-spunbond laminated non-woven fabric, hereinafter also referred to as SMS). Next, this SMS nonwoven fabric was subjected to two-stage treatment under the same conditions as in Example 1 to obtain a nonwoven fabric.

Example Embodiment

[0170] [Example 3]

[0171] Using a spunbond layer composed of ethylene propylene copolymer resin with a fiber diameter of 12.9 μm, the weight per square meter is 18 g / m 2 Non-woven fabric (spunbond-spunbond-meltblown-spunbond laminated non-woven fabric, hereinafter also referred to as SSMS. Softener is mixed into the spunbond layers on both sides of the SSMS non-woven fabric). Next, this SSMS nonwoven fabric was subjected to two-stage treatment under the same conditions as in Example 1 to obtain a nonwoven fabric.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention provides a non-woven fabric (1) wherein a web comprising a long fiber (2) is fixed by a heat sealing part (3). The non-woven fabric (1) according to the invention is provided with a fiber (21) wherein the long fiber (2) is partially broken and one end (20a) thereof is exclusively fixed by the heat sealing part (3) while the free end (20b) in the other end side is thickened. In the non-woven fabric (1) according to the invention, the fiber (21) having the thickened free end (20b) shows an increase in the terminal diameter of the fiber of 15% or greater.

Description

technical field [0001] The present invention relates to nonwoven fabrics comprising long fibers. Background technique [0002] For example, in absorbent articles such as disposable diapers, spun-bonded nonwoven fabrics are often used for reasons of high breaking strength, excellent processing suitability, and economy. However, spun-bonded nonwoven fabrics have insufficient overall soft and fluffy feeling in terms of their manufacturing methods, and it is difficult to improve the skin touch (hand feel). [0003] For example, Patent Document 1 describes a nonwoven fabric in which short fibers are laminated on a spunbonded nonwoven fabric as a base material, and the laminate is subjected to needle punching to have arc-shaped fiber loops protruding from the surface. . However, if the nonwoven fabric with protruding arc-shaped fiber loops described in Patent Document 1 is used for absorbent articles such as disposable diapers, the arc-shaped fiber loops will catch on the skin, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D04H11/08D04H3/14D06C11/00
CPCD04H1/08D04H3/14D04H11/08D06C11/00D04H3/16D06C3/06
Inventor 衣笠由彦小林秀行
Owner KAO CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap