A production method and film technology, applied in dyeing, textiles and papermaking, etc., can solve the problems of low film production efficiency, high production cost, color difference, etc., and achieve the effects of increasing corporate income, facilitating market acceptance, and convenient processing

Inactive Publication Date: 2013-05-22
JIANGXI KEWEI FILM NEW MATERIALS
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, after buying a new car, it is necessary to decorate and beautify the car. The solar film is an essential part of the new car beauty process. The use of the solar film can not only insulate heat and heat, but also prevent solar radiation and skin diseases. Prolong the service life of car interior decorations; in the production process of solar film, different metal materials are usually sputtered on the surface of transparent PET film, so as to achieve the effect of heat insulation and radiation protection. However, the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0007] The present invention is achieved in this way, the method steps are: directly fix the transparent PET film on the roller of the dyeing machine, and the transparent PET film is dyed through the jigger pool, the dyeing raw material in the jigger pool is cationic dye, cationic dye The temperature is 60 o C, the dyeing time is 10 minutes, the PET film is dried after dyeing, and then rinsed, and the rinse water temperature is 60 o C, finally drying to form a colored PET film; in order to achieve the effect of deepening the color, the above steps can be repeated.

Embodiment 2

[0009] The present invention is achieved in this way, the method steps are: directly fix the transparent PET film on the roller of the dyeing machine, and the transparent PET film is dyed through the jigger pool, the dyeing raw material in the jigger pool is cationic dye, cationic dye The temperature is 110 o C, the dyeing time is 1 minute, the PET film is dried after dyeing, and then rinsed, and the rinse water temperature is 110 o C, finally drying to form a colored PET film; in order to achieve the effect of deepening the color, the above steps can be repeated.

Embodiment 3

[0011] The present invention is achieved in this way, the method steps are: directly fix the transparent PET film on the roller of the dyeing machine, and the transparent PET film is dyed through the jigger pool, the dyeing raw material in the jigger pool is cationic dye, cationic dye The temperature is 80 o C, the dyeing time is 7 minutes, the PET film is dried after dyeing, and then rinsed, and the rinse water temperature is 80 o C, finally drying to form a colored PET film; in order to achieve the effect of deepening the color, the above steps can be repeated.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for manufacturing a dyed PET (Polyethyleneglycol Terephthalate) film. The method comprises the following steps: directly fixing a transparent PET film on a rotary drum of a jig dyeing machine and dyeing the transparent PET film through a jig dyeing pool, wherein a dyeing raw material in the jig dyeing pool is a cationic dye, the temperature of the cationic dye is 60-110 DEG C, and the dyeing time is 1-10 minutes; after dyeing the PET film, drying the PET film and then rinsing, wherein the rinsing water temperature is 60-110 DEG C; and finally drying the dyed PET film so as to form a colored PET film. The method has the technical effects that the operation of directly manufacturing an ordinary transparent PET films into dyed PET films is an origination in the industry, not only can the manufacturing be convenient, but also the manufacturing of existing ordinary PET films is not affected, the cost is low, the market acceptance is facilitated, and the profit of enterprises is increased.

Description

technical field [0001] The invention relates to a method for making a PET film, in particular to a method for making a dyed PET film. Background technique [0002] At present, after buying a new car, it is necessary to decorate and beautify the car. The solar film is an essential part of the new car beauty process. The use of the solar film can not only insulate heat and heat, but also prevent solar radiation and skin diseases. Prolong the service life of car interior decorations; in the production process of solar film, different metal materials are usually sputtered on the surface of transparent PET film, so as to achieve the effect of heat insulation and radiation protection. However, the color of PET film cannot be changed. The color of the solar film is single, which affects the driver's driving vision and easily causes traffic accidents. Although there are colored PET films on the market, this kind of PET film is made by dyeing the raw materials of the PET film fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06P3/52D06P1/41
Inventor 柯秋平时招军
Owner JIANGXI KEWEI FILM NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap