Fire-fighting material with excellent smoke suppression for spraying in coal mine and preparation method thereof

A technology for fire prevention and performance, applied in the direction of fire retardant coatings, coatings, etc., can solve a large number of problems such as smoke and safety hazards, and achieve the effect of improving flame retardant performance and smoke suppression performance.

Active Publication Date: 2013-08-21
BEIJING UNIV OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, such materials produce a large amount of smoke during the carbonization process, and there are still certain safety hazards in coal mine fires.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] 1) In a water bath, add 6g of polyvinyl alcohol to 20g of tap water and stir to dissolve, control the temperature at 90°C, and stir for 5 hours;

[0020] 2) Mix and dissolve 2g of phosphoric acid and 2g of urea in 10g of tap water and slowly add to the solution obtained in step 1), after the dropwise addition, add 40g of tap water and react at a water bath temperature of 85°C for a reaction time of 5 hours;

[0021] 3) After the reaction is complete, when the solution is cooled to room temperature, add 20g of white latex and stir until uniform;

[0022] 4) Add 10g of talcum powder, 5g of kaolin and 5g of mica powder into the flame retardant solution obtained in step 3) and fully stir for 2 hours.

[0023] 5) Add 80g ammonium molybdate to the flame retardant material obtained in step 4), stir for 2h

[0024] The surface of the sprayed anti-fire extinguishing material for coal mines obtained with excellent smoke suppression performance is smooth and shiny particles exist...

Embodiment 2

[0026] 1) In a water bath, add 6g of polyvinyl alcohol into 10g of tap water and stir to dissolve, keep the temperature at 90°C, and stir for 5 hours;

[0027] 2) Mix and dissolve 2 g of phosphoric acid and 2 g of urea in 10 g of tap water, then slowly add to the solution obtained in step 1), after the dropwise addition, add 50 g of tap water and react at a water bath temperature of 85°C for a reaction time of 5 hours;

[0028] 3) After the reaction is complete, when the solution is cooled to room temperature, add 20g of white latex and stir until uniform;

[0029] 4) Add 10g of talcum powder, 10g of kaolin and 10g of mica powder into the flame retardant solution obtained in step 3) and stir well for 2h.

[0030] 5) Add 30 g of ammonium molybdate to the flame retardant material obtained in step 4), and stir for 2 h

[0031] The surface of the sprayed anti-fire extinguishing material for coal mines obtained with excellent smoke suppression performance is smooth and shiny parti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a fire-fighting material with excellent smoke suppression for spraying in a coal mine and a preparation method thereof, and belongs to the technical field of the fire-fighting material. The fire-fighting material is prepared from the components by weight percent: 60-80% of polyving akohol flame-resistant material and 20-40% of ammonium molybdate, which are mutually mixed and evenly stirred, wherein the polyving akohol flame-resistant material is prepared from 3-7% of polyving akohol, 1-4% of phosphoric acid, 1-4% of urea, 8-25% of white emulsion, 17-33% of inorganic aggregate and running water in a reaction manner; and the inorganic aggregate is one or any combination of more of kaoline, talcum powder and mica powder. By adopting the method, the smoke suppression of the material is greatly improved; and only a trace of smoke is generated in a combustion process.

Description

technical field [0001] The invention relates to a spray-coated anti-fire extinguishing material for coal mines with excellent smoke suppression performance and a preparation method thereof, belonging to the technical field of anti-fire extinguishing materials. Background technique [0002] my country's coal occupies a dominant position in China's energy structure, which has great strategic significance for our country and has brought huge benefits to the country and the people. However, the conditions in my country's coal mine field are complex and the environment is harsh, and various accidents will cause huge losses to the country every year. Economic and property losses, these accidents have brought great physical and psychological harm to people. After the coal seam is mined, the air volume exchange between the ground and the air inlet roadway, between the air inlet roadway and the return air roadway, and between the air return roadway and the ground gradually increases, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D131/04C09D129/04C09D5/18C09D7/12
Inventor 索红莉陈立佳王鼎元马麟田辉张腾郭艾东
Owner BEIJING UNIV OF TECH