Flame-retardant type wood-plastic material

A wood-plastic material, flame-retardant technology, applied in the field of wood-plastic materials, can solve the problems of limited flame-retardant performance, poor heat resistance, etc., achieve high flame-retardant performance, dense material, and avoid burns

Inactive Publication Date: 2016-06-08
ANHUI YINUO WOOD PLASTIC SHEET TECH CO LTD
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the main components of existing wood-plastic materials are flammable materials, which have poor heat resistance and limited flame retardant performance. Therefore, the market is currently increasing the research on flame retardant materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A flame-retardant wood-plastic material, made of the following raw materials in parts by weight: 60 parts of wood powder, 11 parts of pentaerythritol, 21 parts of modified flame retardant, 21 parts of modified smoke suppressant, 17 parts of polypropylene, high-density 17 parts of polyethylene, 8 parts of vermiculite, 5 parts of dioctyl phthalate, 6 parts of polyethylene glycol distearate, 12 parts of unsaturated polyester resin, 5 parts of vinyltrimethoxysilane, 2 parts of loofah vine, 2 parts of polyethylene wax, 1 part of PE wax, 1 part of magnesium oxide, 1 part of graphite, 1 part of dandelion, 1 part of wormwood, 0.1 part of peanut oil; , co-extruded, cooled and formed into wood-plastic materials.

[0013] The modified flame retardant consists of the following raw materials: 21 parts of hexabromocyclododecane, 13 parts of 2-chloroethyl-2-bromoethyl phosphate, 6 parts of kaolin, 3 parts of melamine cyanurate, 3 parts of melamine phosphate After the parts are dried,...

Embodiment 2

[0016] A flame-retardant wood-plastic material, made of the following raw materials in parts by weight: 32 parts each of rice straw and rice husk, 13 parts of pentaerythritol, 25 parts of modified flame retardant, 25 parts of modified smoke suppressant, and 21 parts of polypropylene 21 parts of high-density polyethylene, 11 parts of vermiculite, 7 parts of dioctyl phthalate, 10 parts of polyethylene glycol distearate, 13 parts of unsaturated polyester resin, vinyl trimethoxy 7 parts of silane, 3 parts of loofah vine, 3 parts of polyethylene wax, 2 parts of PE wax, 2 parts of magnesium oxide, 1.5 parts of graphite, 1.5 parts of dandelion, 1.5 parts of wormwood, 0.2 part of peanut oil; Then it is mixed, co-extruded, and cooled to make wood-plastic materials.

[0017] The modified flame retardant consists of the following raw materials: 24 parts of hexabromocyclododecane, 17 parts of 2-chloroethyl-2-bromoethyl phosphate, 9 parts of kaolin, 5 parts of melamine cyanurate, 5 parts o...

Embodiment 3

[0020] A flame-retardant wood-plastic material, made of the following raw materials in parts by weight: 70 parts of reed stalks, 16 parts of pentaerythritol, 28 parts of modified flame retardants, 28 parts of modified smoke suppressants, 25 parts of polypropylene, high-density 25 parts of polyethylene, 13 parts of vermiculite, 9 parts of dioctyl phthalate, 13 parts of polyethylene glycol distearate, 15 parts of unsaturated polyester resin, 9 parts of vinyltrimethoxysilane, 5 parts of loofah vine, 5 parts of polyethylene wax, 3 parts of PE wax, 3 parts of magnesium oxide, 2 parts of graphite, 2 parts of dandelion, 2 parts of wormwood, 0.3 part of peanut oil; , co-extruded, cooled and formed into wood-plastic materials.

[0021] The modified flame retardant consists of the following raw materials: 27 parts of hexabromocyclododecane, 22 parts of 2-chloroethyl-2-bromoethyl phosphate, 12 parts of kaolin, 7 parts of melamine cyanurate, 7 parts of melamine phosphate After the parts ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a flame-retardant type wood-plastic material. The material is prepared from, by weight, 60-70 parts of wood fibers, 11-16 parts of pentaerythritol, 21-28 parts of modified fire retardant, 21-28 parts of modified smoke inhibitor, 17-25 parts of polypropylene, 17-25 parts of high-density polyethylene, 8-13 parts of vermiculite, 5-9 parts of dioctyl phthalate, 6-13 parts of polyethylene glycol monostearate, 12-15 parts of unsaturated polyester resin, 5-9 parts of vinyl trimethoxy silane, 2-5 parts of luffa stems, 2-5 parts of polyethylene wax, 1-3 parts of PE wax, 1-3 parts of magnesia, 1-2 parts of graphite, 1-2 parts of herba taraxaci, 1-2 parts of ligusticum sinense olivers and 0.1-0.3 part of peanut oil. The wood-plastic material has high flame retandance and a good smoke inhabitation effect and does not release toxic and harmful substances at the high temperature, secondary harm to the human body is avoided, the heat insulation property is quite good, scalds to the human body are avoided, the quite good insulating property is achieved, and meanwhile the wood-plastic material is compact in material, good in mechanical performance and quite durable.

Description

technical field [0001] The invention relates to the field of wood-plastic materials, in particular to a flame-retardant wood-plastic material. Background technique [0002] Wood-plastic composite (WPC) is prepared by compounding thermoplastics and wood fibers or plant fibers. This material has the dual characteristics of wood and plastics. High abrasiveness and impact resistance, the product can be recycled. However, the main components of existing wood-plastic materials are flammable materials, which have poor heat resistance and limited flame-retardant performance. Therefore, the market is currently increasing research on flame-retardant materials. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a waterproof and anti-skid, water is not easy to aggregate on the floor surface, and becomes dispersed, accelerates the volatilization of water, keeps the floor surface dry, resistant to bacterial erosion and insect-pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08L23/12C08L23/06C08L71/00C08L67/06C08K13/02C08K5/02C08K5/521C08K5/3492C08K5/57C08K3/22C08K3/26C08K5/053C08K3/34C08K5/12C08K5/5425C08K3/04
CPCC08L97/02C08L2201/02C08L2205/02C08L2205/035C08L2205/16C08L2207/062C08L23/12C08L23/06C08L71/00C08L67/06C08K13/02C08K5/02C08K5/521C08K3/346C08K5/34924C08K5/57C08K2003/2255C08K2003/265C08K2003/2272C08K5/053C08K3/34C08K5/12C08K5/5425C08K2003/222C08K3/04
Inventor 艾华
Owner ANHUI YINUO WOOD PLASTIC SHEET TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products