Anticorona and consumption-reducing coating for ultra (extra)-high-voltage lines

A technology of ultra-high voltage and anti-fouling flashover coatings, which is applied in conductive coatings, coatings, etc.

Inactive Publication Date: 2013-08-21
NORTH CHINA ELECTRIC POWER UNIV (BAODING) +1
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the causes of corona, such as the voltage level and the geometric shape of the transmission line, cannot be adjusted at will, so they can only passively bear the energy loss caused by corona

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anticorona and consumption-reducing coating for ultra (extra)-high-voltage lines
  • Anticorona and consumption-reducing coating for ultra (extra)-high-voltage lines

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Embodiment 1, raw materials are weighed according to the proportion: 20Kg of hydroxyl-terminated polydimethylsiloxane, 1 Kg of silicone oil; 4.5 Kg of fumed silica, 2 Kg of mica powder; 3.5 Kg of aluminum hydroxide, 2 Kg of titanium dioxide, Methyltriacetoxysilane 1 Kg, di-tert-butyldiacetoxysilane 1 Kg, organotin 0.1 Kg, xylene 25 Kg, carbon black 22Kg.

Embodiment 2

[0025] Embodiment 2, raw materials were weighed according to the proportioning ratio: 28 Kg of hydroxyl-terminated polydimethylsiloxane, 2 Kg of silicone oil; 7 Kg of fumed silica, 2.8 Kg of mica powder; 4 Kg of aluminum hydroxide, 3 Kg of titanium dioxide, Methyltriacetoxysilane 3 Kg, di-tert-butyldiacetoxysilane 2 Kg, organotin 0.4 Kg, xylene 30Kg, carbon black 30Kg.

Embodiment 3

[0026] Embodiment 3, raw materials were weighed according to the proportion: 22 Kg of hydroxyl-terminated polydimethylsiloxane, 1.5 Kg of silicone oil; 6.5 Kg of fumed silica, 4 Kg of mica powder; 3.1 Kg of aluminum hydroxide, 3 Kg of titanium dioxide, Methyltriacetoxysilane 2 Kg, di-tert-butyldiacetoxysilane 1.2 Kg, organotin 0.3 Kg, xylene 35 Kg, carbon black 28Kg.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an anticorona and consumption-reducing coating for ultra (extra)-high-voltage lines, which is prepared from the following raw materials in parts by mass: 21-32 parts of an anti-contamination flashover coating, 6-11 parts of a reinforcing agent, 5-7 parts of a flame retardant, 1-3 parts of a crosslinking agent, 1-2 parts of an additive, 0.1-0.5 part of a catalyst, 25-35 parts of a solvent, and 20-30 parts of an electric conduction agent. When the coating disclosed by the invention is used, the coating is selectively coated on brush discharge points on an electric transmission line, and can carry out effective suppression on the brush discharge of guide lines. Tests show that after the coating is coated, the corona power loss of ultra (extra)-high-voltage lines is significantly lowered, and the critical coronal voltage is increased by near 20 kV (increased from 95 kV to 115 kV), therefore, the coating disclosed by the invention has a good anticorona effect. Compared with traditional anticorona techniques, the coating disclosed by the invention has the advantages of low cost, easiness for production, easiness for application, simple maintenance, strong repair power, strong environment adaptability, convenience for transportation and storage, and the like.

Description

technical field [0001] The invention relates to a coating, in particular to an anti-halation and consumption-reducing coating for ultra-high voltage lines used for power transmission lines and a preparation method thereof. Background technique [0002] In an extremely uneven electric field, when the maximum field strength is higher than the air breakdown field strength, it will cause air ionization, which is called corona discharge. The free strength of air molecules is generally 20-30kV / cm. When the electric field strength on the surface of the transmission line wire exceeds this value, you will hear a "sizzling" discharge sound, smell the smell of ozone, and you can also see the emission around the electrodes at night. The blue-violet fluorescence, which is the corona discharge of the transmission line. The charged ions produced by corona discharge move back and forth around the wire under the action of alternating voltage, accompanied by air ionization and light and radi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/06C09D183/04C09D5/24C09D7/12
Inventor 刘云鹏许自强代杭娟李忍朱雷顼佳宇
Owner NORTH CHINA ELECTRIC POWER UNIV (BAODING)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com