O-shaped rubber sealing ring and production technology thereof

A rubber sealing ring and production process technology, applied in the field of rubber products, can solve the problems of low production efficiency, poor aging resistance, low tensile strength, etc., and achieve the effects of stable product quality, improved stability and long service life

Inactive Publication Date: 2013-09-11
JIAOZUO WANRUI IND & TRADE CO LTD
View PDF3 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The rubber sealing products have poor oil resistance, liquid resistance, aging resist

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] An O-shaped rubber sealing ring is made of the following raw materials in parts by weight: 95 parts of nitrile rubber; 10 parts of zinc oxide; 3 parts of stearic acid; 1 part of antioxidant 4010; 3 parts of paraffin; 5 parts of carbon black N660; 8 parts of coumarone resin; 1 part of anti-aging agent RD; 7 parts of fluorescent whitening agent CBS; 2 parts of dibutyl fat; 2 parts of sulfur; 1 part of accelerator TMTD.

[0025] Its production process comprises the following steps:

[0026] 1) Put 95 parts of nitrile rubber into the internal mixer for masticating, and then park it for 24 hours for use;

[0027] 2) Put the plasticized nitrile rubber into the internal mixer, add 10 parts of zinc oxide; 3 parts of stearic acid; 1 part of anti-aging agent 4010; 3 parts of paraffin; 5 parts of carbon black N660; 8 parts of coumarone resin ; 1 part of anti-aging agent RD; 7 parts of fluorescent whitening agent CBS; 2 parts of dibutyl fat, after banburying, park for 24 hours for...

Embodiment 2

[0034] An O-shaped rubber sealing ring is made of the following raw materials in parts by weight: 100 parts of nitrile rubber; 15 parts of zinc oxide; 5 parts of stearic acid; 3 parts of antioxidant 4010; 5 parts of paraffin; 7 parts of carbon black N660; 10 parts of coumarone resin; 2 parts of anti-aging agent RD; 9 parts of fluorescent whitening agent CBS; 4 parts of dibutyl ester; 3 parts of sulfur; 1.2 parts of accelerator TMTD.

[0035] Its production process comprises the following steps:

[0036] 1) Put 100 parts of nitrile rubber into the internal mixer for mastication, and then park it for 24 hours for use;

[0037] 2) Put the plasticized nitrile rubber into the internal mixer, add 15 parts of zinc oxide; 5 parts of stearic acid; 3 parts of anti-aging agent 4010; 5 parts of paraffin; 7 parts of carbon black N660; 10 parts of coumarone resin ; 2 parts of anti-aging agent RD; 9 parts of fluorescent whitening agent CBS; 4 parts of dibutyl fat, after banburying, park for...

Embodiment 3

[0044] An O-shaped rubber sealing ring is made of the following raw materials in parts by weight: 100 parts of nitrile rubber; 15 parts of zinc oxide; 3 parts of stearic acid; 1 part of anti-aging agent 4010; 5 parts of paraffin; 7 parts of carbon black N660; 10 parts of coumarone resin; 2 parts of anti-aging agent RD; 7 parts of fluorescent whitening agent CBS; 2 parts of dibutyl fat; 2 parts of sulfur; 1.2 parts of accelerator TMTD.

[0045] Its production process comprises the following steps:

[0046] 1) Put 95-100 parts of nitrile rubber into the internal mixer for masticating, and then park it for 24 hours for use;

[0047] 2) Put the plasticized nitrile rubber into the internal mixer, add 15 parts of zinc oxide; 3 parts of stearic acid; 1 part of anti-aging agent 4010; 5 parts of paraffin; 7 parts of carbon black N660; 10 parts of coumarone resin ; 2 parts of anti-aging agent RD; 7 parts of fluorescent whitening agent CBS; 2 parts of dibutyl fat, after banburying, park...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an O-shaped rubber sealing ring and a production technology thereof. The O-shaped rubber sealing ring is prepared by mixing the following raw materials: 95-100 parts of butadiene nitrile rubber, 10-15 parts of zinc oxide, 3-5 parts of stearic acid, 1-3 parts of an antioxidant 4010, 3-5 parts of paraffin, 5-7 parts of a carbon black N660, 8-10 parts of a coumatone resin, 1-2 parts of an antioxidant RD, 7-9 parts of a fluorescent whitening agent CBS, 2-4 parts of dibutyl phthalate, 2-3 parts of sulphur and 1-1.2 parts of a promoter TMTD. The production technology is reasonable, various raw materials are mixed uniformly and a uniformly-mixed product is obtained. The O-shaped rubber sealing ring has advantages of aging resistance, liquid resistance, good tensile strength and elongation, no phenomena of wearing and oil leakage, steady product quality, long service life and the like.

Description

technical field [0001] The invention relates to the technical field of rubber products, in particular to an O-shaped rubber sealing ring and a production process thereof. Background technique [0002] With the development of industry, the application of seals is becoming more and more extensive. Usually, the production of rubber seals adopts the method of molding with fixed specifications. [0003] O-shaped rubber sealing rings are widely used in various machinery, resistant to various petroleum base oils and various chemical media. [0004] The original rubber sealing products adopt the traditional production process. The rubber material is cut and carved with scissors or blades after being unloaded by the kneading machine, and then overlapped into the mold for vulcanization, thereby making an O-shaped rubber sealing ring. The rubber sealing products have poor oil resistance, liquid resistance, aging resistance, low elongation and low tensile strength, resulting in low pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L9/02C08L45/02C08K13/02C08K3/22C08K5/09C08K3/04C08K3/06C08K5/01
Inventor 岳保平
Owner JIAOZUO WANRUI IND & TRADE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap