Cold-rolled copper and aluminum composite material production process

A copper-aluminum composite material and production process technology, applied in metal rolling, manufacturing tools, metal rolling, etc., can solve problems such as easy oxidation

Inactive Publication Date: 2013-11-20
SHANDONG LAIWU JINSHI GROUP
View PDF5 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it is also easy to oxidize in an environment higher than room temperature, especially in an environment containing corrosive gases

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cold-rolled copper and aluminum composite material production process
  • Cold-rolled copper and aluminum composite material production process
  • Cold-rolled copper and aluminum composite material production process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The relevant technical contents not mentioned below can adopt or learn from the prior art.

[0023] In order to enable those skilled in the art to better understand the technical solutions in the present application, the technical solutions in the embodiments of the present application will be clearly and completely described below in conjunction with the drawings in the embodiments of the present application. Obviously, the described The embodiments are only some of the embodiments of the present application, but not all of them. Based on the embodiments in this application, all other embodiments obtained by persons of ordinary skill in the art without creative efforts shall fall within the protection scope of this application.

[0024] A production process of cold-rolled copper-aluminum composite material,

[0025] Raw materials: use aluminum strip as the base strip and copper strip as the cladding material; select the thickness and width of the aluminum strip and co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
surface roughnessaaaaaaaaaa
surface roughnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a cold-rolled copper and aluminum composite material production process. The process includes using an aluminum strip as a base strip and a copper strip as a strip covering material, performing surface treatment, performing composite rolling prior to heat treatment at the temperature of 605-610 DEG C, keeping the temperature for 8-10min, and finally forcedly cooling to the normal temperature by water cooling, wherein the thickness of the copper strip is 18-22% of that of the aluminum strip, the surface roughness of the aluminum strip satisfies that Rz=95-115 micrometers, and the surface roughness of the copper strip satisfies that Rz=80-95 micrometers. Optimum matching of deformation, layer thickness ratio and composite strength can be realized, and the process has the advantages of high interface composite strength and good dynamic thermal stability.

Description

technical field [0001] The invention relates to a production process of cold-rolled copper-aluminum composite material. Background technique [0002] At present, the commonly used conductive materials in the electric power industry are copper and aluminum. At the same time, they are also commonly used heat exchange materials in the world. The instantaneous heat absorption capacity of copper is 1.61.6 times faster than that of aluminum, but the heat dissipation speed is relatively slow. The heat dissipation speed of aluminum 2.33 times that of copper block. But it is also easy to oxidize in an environment higher than room temperature, especially in an environment containing corrosive gases. Therefore, under the harsh conditions of industrial and mining, aluminum bars are reused instead of copper bars. If the two metal materials are combined, it will be a perfect conductive and heat exchange material. Therefore, copper-aluminum composite materials are an excellent choice fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B21B1/28B21B47/00
Inventor 石勇石萌陈昊王闯
Owner SHANDONG LAIWU JINSHI GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap