Mud-resistant polycarboxylic acid water reducer and preparation method thereof

A technology of water reducing agent and polycarboxylic acid, applied in the field of concrete water reducing agent, can solve the problems of deactivation, loss of steric hindrance ability, etc., and achieve the effects of low equipment requirements, easy to enlarge and control production, and simple preparation process

Active Publication Date: 2015-05-13
SICHUAN TONGZHOU CHEM TECH
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Scholars and industry experts at home and abroad have done a lot of work on this, and now they have come to a more consistent conclusion that the mud composition structure in fine aggregate is similar to the multi-layer structure of montmorillonite, while polycarboxylic acid has a longer branched chain , the intercalation effect of simultaneous physical and chemical reactions between these branched chains and the layer of soil occurs, thus losing the steric hindrance ability and leading to deactivation
[0005] According to these mechanisms, some experts have carried out some experiments to polymerize carboxylic acid with short-chain branches without hydrophilic ethylene oxide, and investigate the adsorption capacity and intercalation effect of montmorillonite, although it is proved from the data of adsorption curve The correctness of this theory is confirmed, but polycarboxylic acid mainly relies on the steric effect of long-chain branches to disperse cement particles. , the water solubility of polycarboxylate and the adaptability to cement have big problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mud-resistant polycarboxylic acid water reducer and preparation method thereof
  • Mud-resistant polycarboxylic acid water reducer and preparation method thereof
  • Mud-resistant polycarboxylic acid water reducer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A polycarboxylate anti-sludge water-reducing agent is made from the following components, and the weight ratio of each component is:

[0026]

[0027] Described component R is maleic anhydride;

[0028] the R 1 for acrylic;

[0029] the R 2 For hanging white blocks.

[0030] The allyl polyoxyethylene polyoxypropylene ether is allyl polyoxyethylene polyoxypropylene ether; the chain transfer agent is mercaptoacetic acid; the initiator R 3 For ammonium persulfate.

[0031] The molecular weight of the allyl polyoxyethylene polyoxypropylene ether is 1000.

[0032] The preparation method of described a kind of polycarboxylic acid anti-mud-containing water reducing agent, it comprises the following steps:

[0033] S1, take by weighing the raw material according to the above formula;

[0034] S2, put in the weighed allyl polyoxyethylene polyoxypropylene ether and component R in the reaction kettle, add 120 g of water, turn on stirring, slowly heat up to 35~45 ℃, and c...

Embodiment 2

[0039] A polycarboxylate anti-sludge water-reducing agent is made from the following components, and the weight ratio of each component is:

[0040]

[0041] Described component R is 5g sodium methacrylate sulfonate and 11g fumaric acid;

[0042] the R 1 for acrylic;

[0043] the R 2 for ascorbic acid.

[0044] The allyl polyoxyethylene polyoxypropylene ether is methacrylic polyoxyethylene polyoxypropylene ether; the chain transfer agent is mercaptopropionic acid; the initiator R 3 It is 2~5g of 27.5% hydrogen peroxide.

[0045] The molecular weight of the allyl polyoxyethylene polyoxypropylene ether is 2000.

[0046] The preparation method of described a kind of polycarboxylic acid anti-mud-containing water reducing agent, it comprises the following steps:

[0047] S1, take by weighing the raw material according to the above formula;

[0048]S2, put in the weighed allyl polyoxyethylene polyoxypropylene ether and component R in the reactor, add 120 g of water, turn o...

Embodiment 3

[0053] A polycarboxylate anti-sludge water-reducing agent is made from the following components, and the weight ratio of each component is:

[0054]

[0055] Described component R is 12g maleic anhydride and 6g vinyl acetate;

[0056] the R 1 for acrylic;

[0057] the R 2 For hanging white blocks.

[0058] The allyl polyoxyethylene polyoxypropylene ether is methylbutene polyoxyethylene polyoxypropylene ether; the chain transfer agent is a mixture of 0.5g mercaptoacetic acid and 0.5g mercaptopropionic acid; initiator R 3 For 3 ~ 7g content of 27.5% hydrogen peroxide.

[0059] The molecular weight of the allyl polyoxyethylene polyoxypropylene ether is 2400.

[0060] The preparation method of described a kind of polycarboxylic acid anti-mud-containing water reducing agent, it comprises the following steps:

[0061] S1, take by weighing the raw material according to the above formula;

[0062] S2, put in the weighed allyl polyoxyethylene polyoxypropylene ether and compon...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a mud-resistant polycarboxylic acid water reducer which is prepared from the following components: allyl polyoxyethylene polyoxypropylene ether, components R, R1 and R2, a chain transfer agent, an initiating agent R3 and water, wherein the component R is one or more of maleic anhydride, sodium methallyl sulfonate, vinyl acetate, itaconic acid, itaconic anhydride and fumaric acid; R1 is one or a mixture of two of acrylic acid and methylacrylic acid; R2 is one or more of ascorbic acid, sodium formaldehyde sulfoxylate, ferrous sulfate, tin sulfate, sodium hypophosphite, sodium hydrogen sulfite and oxalic acid. The invention further discloses a preparation method for the mud-resistant polycarboxylic acid water reducer. The mud-resistant polycarboxylic acid water reducer has the following benefits: the water solubility and the steric hindrance of polycarboxylic acid are effectively kept; a large amount of non-hydrophilic structures on branch chains can be used for effectively preventing soil interlayer adsorption, so that the adsorption speed and effect are greatly reduced and the mud-resistant purpose is achieved.

Description

technical field [0001] The invention relates to the technical field of concrete water-reducing agents, in particular to a polycarboxylic acid anti-mud-containing water-reducing agent and a preparation method thereof. Background technique [0002] With the rapid development of my country's economic construction, the use of concrete has increased at a rate of more than ten percent per year, and the level of concrete application technology has also continued to develop. The continuous improvement of the use of polycarboxylate water reducer instead. The use of polycarboxylate superplasticizer to configure high performance concrete has become the trend of concrete development. Polycarboxylate superplasticizers are used in high-speed railways, water conservancy and hydropower, drinking Points, highways, harbor terminals and various projects. [0003] Although polycarboxylate superplasticizer has many advantages, it is greatly affected by the fine aggregate in concrete, that is, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08F283/06C04B24/32C04B103/30
Inventor 杨俊舒豆豆何年
Owner SICHUAN TONGZHOU CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap