Chemical fiber quilt stuffing and mixing process thereof

A filling material and chemical fiber technology, applied in the direction of non-woven fabrics, textiles, papermaking, bed sheets, etc., can solve the problems affecting the quality and output of wadding molding, affecting the wearing function, etc., and achieve the effect of reasonable production process and high work efficiency

Active Publication Date: 2015-04-29
NANTONG SIDEFU TEXTILE DECORATION
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The three-dimensional crimped chemical fiber fillings of the known quilt core directly affect its function as a quilt filling material because of its thickness, length, hollowness, and whether it is finished with silicon. , The degree of pulling, not only affects the wearing function of the product, but also affects the quality and output of cotton wool forming in the processing process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0018] A kind of chemical fiber quilt filling material. The chemical fiber quilt filling material is composed of the following components in parts by weight: 30 parts of 10dtex*60mm silicon-finished seven-hole cotton, 6.67dtex*64mm silicon-finished single-hole cotton 20 parts, 6.67dtex *5 parts of 64mm silicon-free finishing single-hole cotton, 0.1 part of antistatic liquid.

[0019] The mixing process of chemical fiber core filling materials includes the following steps:

[0020] (1) Cotton weighing: Weigh the following raw materials in proportion: 10dtex*60mm silicon-finished seven-hole cotton, 6.67dtex*64mm silicon-finished single-hole cotton and 6.67dtex*64mm silicon-free finished single-hole cotton;

[0021] (2) Manual cotton blending: Manually mix the three fillers in step (1) evenly, select the ground of the operating area within the range of 200cm*200cm, sprinkle the corresponding fillers and antistatic liquid in batches in sequence and proportion, and then use iron T...

specific Embodiment 2

[0029] A chemical fiber type quilt filler, said chemical fiber type quilt filler consists of the following components in parts by weight: 60 parts of 8.33dtex*60mm silicon-finished four-hole cotton, 6.67dtex*64mm silicon-finished single-hole cotton 50 parts 25 parts of 6.67dtex*64mm silicon-free finishing single-hole cotton, 1 part of antistatic liquid.

[0030] The mixing process of chemical fiber core filling materials includes the following steps:

[0031] (1) Cotton weighing: Weigh the following raw materials in proportion: 8.33dtex*60mm silicon-finished four-hole cotton, 6.67dtex*64mm silicon-finished single-hole cotton and 6.67dtex*64mm silicon-free finished single-hole cotton;

[0032] (2) Manual cotton blending: Manually mix the three fillers in step (1) evenly, select the ground of the operating area within the range of 200cm*200cm, sprinkle the corresponding fillers and antistatic liquid in batches in sequence and proportion, and then use iron The fork flips in the ...

specific Embodiment 3

[0040] A kind of chemical fiber quilt filling material. The chemical fiber quilt filling material is composed of the following components in parts by weight: 50 parts of 10dtex*60mm silicon-finished seven-hole cotton, 6.67dtex*64mm silicon-finished single-hole cotton 40 parts, 6.67dtex * 10 parts of 64mm silicon-free finishing single-hole cotton, 0.5 parts of antistatic liquid.

[0041] The mixing process of chemical fiber core filling materials includes the following steps:

[0042] (1) Cotton weighing: Weigh the following raw materials in proportion: 10dtex*60mm silicon-finished seven-hole cotton, 6.67dtex*64mm silicon-finished single-hole cotton and 6.67dtex*64mm silicon-free finished single-hole cotton;

[0043] (2) Manual cotton blending: Manually mix the three fillers in step (1) evenly, select the ground of the operating area within the range of 200cm*200cm, sprinkle the corresponding fillers and antistatic liquid in batches in sequence and proportion, and then use iron...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compression ratioaaaaaaaaaa
Login to View More

Abstract

The invention discloses chemical fiber quilt stuffing and a mixing process thereof. The chemical fiber quilt stuffing comprises, by weight, 30-60 parts of silicon finishing thermolite quallo in the specification of 10dtex*60mm or silicon finishing thermolite in the specification of 8.33dtex*60mm, 20-50 parts of silicon finishing invista thermolite in the specification of 6.67dtex*64mm, 5-25 parts of non-silicon finishing invista thermolite in the specification of 6.67dtex*64mm and 0.1-1 part of anti-static liquid. The process includes the steps of cotton weighing, manual cotton mixing, stacking, primary opening, secondary opening, net formation, cotton wadding laying, grinding and cotton wadding forming. The chemical fiber quilt stuffing and the mixing process thereof can be directly used for production of textiles in hotels, production process is reasonable, work efficiency is high, the compression rate of the manufactured quilt stuffing is high and the reversion rate of the manufactured quilt stuffing is good.

Description

technical field [0001] The invention belongs to the field of hotel bedding, and in particular relates to a chemical fiber quilt core filler and a mixing process thereof. Background technique [0002] The three-dimensional crimped chemical fiber fillings of the known quilt core directly affect its function as a quilt filling material because of its thickness, length, hollowness, and whether it is finished with silicon. , The degree of pulling, not only affects the wearing function of the product, but also affects the quality and output of cotton wool forming during processing. Contents of the invention [0003] Purpose of the invention: The present invention provides a chemical fiber core filling material and its mixing process, which can be directly used in the production of hotel textiles. [0004] Technical solution: A chemical fiber quilt filler, the chemical fiber quilt filler is composed of the following components in parts by weight: 10dtex*60mm silicon-finished sev...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A47G9/02D04H1/02
Inventor 张华
Owner NANTONG SIDEFU TEXTILE DECORATION