A kind of production method of large thin-walled full-ring ceramic grinding wheel

A technology of ceramic grinding wheel and production method, which is applied in the direction of abrasive materials, metal processing equipment, grinding devices, etc., and can solve the problems that large thin-walled ceramic grinding wheels cannot be manufactured in a complete ring and the product yield is low.

Active Publication Date: 2016-08-10
HENAN HUAMAO NEW MATERIAL TECH DEV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The invention provides a production method of a large thin-walled ceramic grinding wheel with a whole ring, which solves the problem that the existing large thin-walled ceramic grinding wheel cannot be manufactured in a whole ring or the whole ring is manufactured, and the yield of the product is low.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A method for producing a large thin-walled full-ring ceramic grinding wheel, the diameter of the grinding wheel is 300mm, and the thickness is 1.5mm, comprising the following steps:

[0021] The first step, first mix the vitrified bond, diamond and phenolic resin according to the proportion, the vitrified grinding wheel includes 35% vitrified bond according to the volume ratio, 50% the diamond, and the balance is air holes , the phenolic resin is calculated according to the volume ratio of the vitrified grinding wheel, and the addition of the described phenolic resin is 15% of the total volume of the vitrified grinding wheel;

[0022] The second step is to put the raw materials of the first step into the mold, at a temperature of 100°C and a pressure of 15kg / cm 2 , thermoforming;

[0023] The third step, demoulding;

[0024] The fourth step is firing at high temperature, the temperature is 1200° C., and the time is 1 hour. After the firing is completed and passed the ...

Embodiment 2

[0027] A method for producing a large thin-walled full-ring ceramic grinding wheel, the diameter of the grinding wheel is 500 mm, and the thickness is 1 mm, comprising the following steps:

[0028] The first step, at first mix vitrified bond, CBN and polyimide resin according to the ratio, the vitrified grinding wheel comprises 38% vitrified bond according to the volume ratio, the CBN is 50%, and the rest Amount is air hole, and described polyimide resin is according to the volume ratio of vitrified grinding wheel, and the addition of described polyimide resin is 10% of vitrified grinding wheel total volume;

[0029] The second step is to put the raw materials of the first step into the mold, at a temperature of 150°C and a pressure of 18kg / cm 2 , thermoforming;

[0030] The third step, demoulding;

[0031] The fourth step is firing at high temperature, the temperature is 1200° C., and the time is 1 hour. After the firing is completed and passed the inspection, a large thin-...

Embodiment 3

[0034] A method for producing a large thin-walled full-ring ceramic grinding wheel, the diameter of the grinding wheel is 600mm, and the thickness is 1.5mm, comprising the following steps:

[0035] The first step, first mix vitrified bond, diamond and phenolic resin according to the proportion, the vitrified grinding wheel includes 37% vitrified bond according to volume ratio, 45% described diamond, and the balance is air holes , the phenolic resin is calculated according to the volume ratio of the vitrified grinding wheel, and the addition of the described phenolic resin is 13% of the total volume of the vitrified grinding wheel;

[0036] The second step is to put the raw materials of the first step into the mold, at a temperature of 200°C and a pressure of 12kg / cm 2 , thermoforming;

[0037] The third step, demoulding;

[0038] The fourth step is firing at high temperature, the temperature is 1200° C., and the time is 1 hour. After the firing is completed and passed the in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a production method of a large thin-walled integral ring ceramic grinding wheel. The production method of a large thin-walled integral ring ceramic grinding wheel comprises the following steps: the first step, according to a certain proportion, vitrified bond, abrasive and resin together Mixing; the second step, put the raw materials of the first step into the mold, and hot press; the third step, demoulding; Ring vitrified grinding wheel. The production method of the present invention can directly produce a full-ring thin-walled grinding wheel with a diameter greater than 200mm and a thickness less than 10mm. The yield of the product reaches 99%, and the yield of the product demoulding reaches 100%. The large-diameter full-ring thin-wall ceramic grinding wheel produced by the production method of the present invention has no previous bonding seam, and the surface of the ground product is uniform without ripples.

Description

technical field [0001] The invention relates to a production method of a ceramic grinding wheel, in particular to a production method of a large thin-walled full-ring ceramic grinding wheel. Background technique [0002] The production method of general vitrified grinding wheel is: vitrified bond and abrasive are evenly mixed, cold-pressed, fired at high temperature, and the excess part of the surface is processed to obtain vitrified grinding wheel. After the grinding wheel is cold-pressed and formed in the mold, it needs to be demoulded, the formed grinding wheel is taken out, and fired in a high-temperature firing device. Due to the cold press forming, the combination of the vitrified bond and the abrasive is not very fixed, and it is easy to cause deformation or breakage of the formed grinding wheel during demoulding. Especially for some grinding wheels with a diameter greater than 200mm and a thickness less than 10mm, if the whole ring is used for pressing, it is easy t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B24D3/14B24D3/28B24D18/00
Inventor 秦景厂郭留希袁德禄李晓苹
Owner HENAN HUAMAO NEW MATERIAL TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com