Fabric for airbag, fully formed airbag and manufacturing method thereof

An airbag, fully formed technology, applied in the direction of vehicle safety arrangements, fabrics, textiles, and papermaking, to achieve good technical effects and reduce costs

Active Publication Date: 2016-03-30
KOLON NANJING SPECIAL TEXTILE
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention solves the problems of dimensional stability, flatness, air tightness, high strength and aging resistance of the current fully formed airbag on the basis of cost reduction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fabric for airbag, fully formed airbag and manufacturing method thereof
  • Fabric for airbag, fully formed airbag and manufacturing method thereof
  • Fabric for airbag, fully formed airbag and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Nylon 66 with a dry heat shrinkage rate of 4.1% and a boiling water shrinkage rate of 4.3% is used as the warp yarn, and a polyester with a dry heat shrinkage rate of 2.2% and a boiling water shrinkage rate of 1.5% is used as the weft yarn. The CEG content in the polyester is 20meq / kg. After the woven fabric is treated with an aqueous solution containing a refining agent at 60°C for 2 minutes, it is dried and shaped in an oven heated by hot air at 150°C for 1 minute, and then coated with 45g / ㎡ of silica gel. In this process, the warp and weft dimensional change rates of the fabric are 3% and 2.5%, respectively, and the strength retention rate of the fabric after heat and humidity aging is above 97%.

[0037] The physical properties of the yarns used in Example 2-Example 4 and Comparative Example 1 and Comparative Example 2 are shown in Table 1, and the physical properties of the fabric obtained using the same method as in Example 1 are shown in Table 2.

[0038] Table ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
shrinkageaaaaaaaaaa
shrinkageaaaaaaaaaa
shrinkageaaaaaaaaaa
Login to View More

Abstract

The invention relates to a fabric for an airbag, the warp and weft yarns of which are composed of polyamide or polyester fibers, characterized in that: the polyamide or polyester fibers have a dry heat shrinkage rate and a wet heat shrinkage rate of less than 5%, and After being treated with hot water and hot air and coated with 35-115g / ㎡ of silicone resin on the surface of the fabric, the change rate of the size of the airbag fabric is less than 3%. The present invention also relates to a fully formed airbag comprising the fabric for an airbag and a manufacturing method thereof. The invention solves the problems of dimensional stability, smoothness, air tightness, high strength, aging resistance and the like of the current fully formed airbag on the basis of cost reduction.

Description

technical field [0001] The invention relates to a fabric for an airbag. The fabric for the airbag uses polyester yarns to partially or completely replace traditional nylon yarns, and all performance indexes of the airbag meet the requirements. The present invention also relates to a fully formed airbag comprising the fabric for an airbag and a manufacturing method thereof. Background technique [0002] In recent years, automobile airbags have provided greater protection to humans during automobile collisions and reduced injuries. People have higher and higher requirements for airbags, such as good dimensional stability, flatness, airtightness, high strength, aging resistance and low cost. Polyamide fibers (such as nylon 66) can meet all indicators, but they are expensive. The price of polyester is relatively cheap, and its various properties can meet the requirements of airbag fabrics, but its performance will decline after aging due to molecular chain breakage in high-tem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/643D03D1/02D03D15/00D03D3/02B60R21/235D06M101/34D06M101/32D03D15/283D03D15/567
Inventor 张克迪庄坤裴仁稷
Owner KOLON NANJING SPECIAL TEXTILE
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com