A kind of polyurea coating and preparation method thereof
Active Publication Date: 2016-05-25
JIANGSU XIN AN NEW MATERIALS TECH
View PDF5 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, it also exposed a series of problems in the application process, such as the reaction speed is too fast, the construction requires special high temperature and high pressure impact mixing equipment, pitting, orange peel, etc. are easy to form on the surface of the coating, and the apparent state is poor; The wettability of the material is not good and the adhesion is low; the reaction exotherm is concentrated, the heat shrinkage rate is large, the internal stress is large, and the adhesion is negatively affected; the color retention and UV resistance are poor, etc.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0031] Weigh each component according to the following ratio:
[0032] Component A:
[0033]
[0034] Component B:
[0035] Isocyanate N339020kg
[0036] Accelerator katVP02450.03kg
[0037] Butyl acetate industrial grade 5kg
[0038] For component A, first add polyurea resin, titanium dioxide, 3A activated powder, dispersant, acetic acid, and PMA into the mixing tank by weight and stir for 30 minutes; Foaming agent and leveling agent can adjust viscosity and color. 3A activating powder can improve the water absorption in the system and improve the waterproof function. Component B is weighed in proportion and added to the mixing tank and stirred evenly.
Embodiment 2
[0040] Component A:
[0041]
[0042] All the other contents are the same as those described in Example 1.
[0043] The performance data of the polyurea coating that the present invention obtains:
[0044]
[0045]
[0046] acid resistance
[0047]
[0048] Oil resistance:
[0049] No. 0 diesel oil, crude oil, 30d, no corrosion, no foaming, no shedding
[0050] Gel time comparison data test:
[0051]
Embodiment 3
[0053] A polyurea coating consisting of components A and B,
[0054] The percentage by weight of each composition of described A component is as follows:
[0055]
[0056] The weight percent of each composition of described B component is as follows:
[0057] Isocyanate 70%
[0058] Accelerator katVP02451%
[0059] Butyl acetate 29%
[0060] The sum of the weight percentages of the components of the A component is 100%, and the sum of the weight percentages of the components of the B component is 100%; the mass ratio of the A and B components is A:B=3:1;
[0061] The polyurea resin is polyaspartic acid ester.
[0062] For component A, first add polyurea resin, carbon black, 3A activated powder, dispersant, acetic acid, and PMA into the mixing tank by weight and stir for 30 minutes; Foaming agent and leveling agent can adjust viscosity and color. 3A activating powder can improve the water absorption in the system and improve the waterproof function. Component B is wei...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The present invention discloses a polyurea coating material and a preparation method thereof. The polyurea coating material comprises a component A and a component B, wherein the component A comprises, by weight, 60-80% of a polyurea resin, 10-15% of a pigment, 10-20% of a filler, 0.5-1.5% of 3A activation powder, 1-2% of a dispersing agent, 3-7% of butyl acetate, 2-5% of PMA, 0.2-0.5% of an antifoaming agent, and 0.5-1% of a leveling agent, the component B comprises, by weight, 70-90% of isocyanate, 0.02-1% of an accelerating agent, and 30-10% of butyl acetate, a mass ratio of the component A to the component B is 3:1, and the polyurea resin is polyaspartic ester. During preparation, the raw materials excluding the antifoaming agent and the leveling agent are uniformly stirred and grinded, then the antifoaming agent and the leveling agent are added to adjust the color and the viscosity to obtain the component A, the component B is weighed according to the mass ratio and is added to a stirring tank, and uniform dispersing is performed.
Description
technical field [0001] The invention relates to the field of polyurea coatings, in particular to a two-component polyurea coating. Background technique [0002] Polyurea coatings are widely used in various fields due to their excellent anti-corrosion, waterproof and wear-resistant characteristics. However, it also exposed a series of problems in the application process, such as the reaction speed is too fast, the construction requires special high temperature and high pressure impact mixing equipment, pitting, orange peel, etc. are easy to form on the surface of the coating, and the apparent state is poor; The wettability of the material is not good and the adhesion is low; the reaction exotherm is concentrated, the heat shrinkage rate is large, the internal stress is large, and the adhesion is negatively affected; the color retention and UV resistance are poor. Contents of the invention [0003] Aiming at the problems of low adhesion and uncontrollable reaction speed in ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.