Formula of aluminum alloy hub material
A technology for aluminum alloy wheels and materials, which is applied in the field of aluminum alloy wheel material formulations, can solve the problems of increasing the difficulty of mechanical processing of parts, reducing the mechanical properties of alloys, and deteriorating dimensional stability, so as to improve mechanical properties, improve product processing performance, The effect of high tensile strength
Inactive Publication Date: 2014-04-02
SHANDONG HENGYU AUTO PARTS
View PDF4 Cites 9 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Iron is a major harmful impurity in cast aluminum alloys. With the increase of iron content, needles and flaky brittle iron phases with high hardness will be formed in the metallographic structure. Its existence splits the aluminum alloy. The matrix reduces the mechanical properties of the alloy, especially the toughness, and increases the difficulty of machining parts, severe wear of knives and cutting tools, and poor dimensional stability
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0007] Example 1: The formula of this material is (weight percentage): Si6.5%, Cu0.3%, Mg0.4%, Mn0.3%, Ni0.02%,, Ti0.2%, Sr0.02%, Re0.2%, Zr0.01%, the rest is Al.
Embodiment 2
[0008] Example 2: The formula of the material is (weight percent): Si7.5%, Cu0.4%, Mg0.6%, Mn0.4%, Ni0.04%, Ti0.4%, Sr0.04%, Re0 .4%, Zr0.04%, and the rest is Al.
Embodiment 3
[0009] Example 3: The formula of this material is (weight percent): Si7%, Cu0.3%, Mg0.6%, Mn0.3%, Ni0.04%,, Ti0.4%, Sr0.02%, Re0. 3%, Zr0.04%, and the rest is Al.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention provides a formula of an aluminum alloy hub material. The material comprises the following ingredients by weight: 6.5-7.5% of Si, 0.3-0.4% of Cu, 0.4-0.6% of Mg, 0.3-0.4% of Mn, 0.02-0.04% of Ni, 0.2-0.4% of Ti, 0.02-0.04% of Sr, 0.2-0.4% of Re, 0.01-0.04% of Zr and the rest of Al. The novel formula can not only effectively improve the mechanical properties of aluminum alloy, but also greatly improve the processing performance of a product and ensure the mechanical performance of the product.
Description
technical field [0001] The invention relates to a wheel hub material formula, in particular to an aluminum alloy wheel hub material formula. Background technique [0002] At present, the domestic wheel aluminum alloy mainly adopts A356 alloy (domestic brand: ZL101A), and its chemical composition contains: Si7%; Mg0. 35%; Fe < 0. 2%; Cu < 0. 2%; Zn < 0. 1% . Due to the high iron content in low-quality aluminum alloy ingots, and with the reuse of alloy furnace materials and the use of iron crucibles, tools, and roofing parts in production, the iron content of alloys continues to increase. Iron is a major harmful impurity in cast aluminum alloys. With the increase of iron content, needles and flaky brittle iron phases with high hardness will be formed in the metallographic structure. Its existence splits the aluminum alloy. The matrix reduces the mechanical properties of the alloy, especially the toughness, and increases the difficulty of mechanical processing of pa...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More IPC IPC(8): C22C21/02
Inventor 田家礼张光德于海洋
Owner SHANDONG HENGYU AUTO PARTS
PatSnap Eureka turns technology decisions into work you can execute. Powered by our Innovation Knowledge Graph, it runs expert workflows across engineering, life sciences, materials and intellectual property. Get your review-ready output in minutes.